The utilization of all-solid-state electrolytes is considered to be an effective way to enhance the safety performance of lithium metal batteries.However,the low ionic conductivity and poor interface compatibility gre...The utilization of all-solid-state electrolytes is considered to be an effective way to enhance the safety performance of lithium metal batteries.However,the low ionic conductivity and poor interface compatibility greatly restrict the development of all-solid-state battery.In this study,a composite electrolyte combining the electrospun polyamide 6(PA6)nanofiber membrane with hierarchical structure and the polyethylene oxide(PEO)polymer is investigated.The introduction of PA6 nanofiber membrane can effectively reduce the crystallinity of the polymer,so that the ionic conductivity of the electrolyte can be enhanced.Moreover,it is found that the presence of finely branched fibers in the hierarchical structure PA6 membrane allows the polar functional groups(C=O and N-H bonds)to be fully exposed,which provides sufficient functional sites for lithium ion transport and helps to regulate the uniform deposition of lithium metal.Moreover,the hierarchical structure can enhance the mechanical strength(9.2 MPa)of the electrolyte,thereby effectively improving the safety and cycle stability of the battery.The prepared Li/Li symmetric battery can be stably cycled for 1500 h under 0.3 mA cm^(-2) and 60℃.This study demonstrates that the prepared electrolyte has excellent application prospects in the next generation all-solid-state lithium metal batteries.展开更多
We report on the synthesis and characterizations of TiO2 nanoparticles embedded in polyamide-6composite nanofibers by using electrospinning technique. The influence of substrate on the electrical characteristics of po...We report on the synthesis and characterizations of TiO2 nanoparticles embedded in polyamide-6composite nanofibers by using electrospinning technique. The influence of substrate on the electrical characteristics of polyamide-6/TiO2 composite nanofibers was investigated. The resultant nanofibers exhibit good incorporation of TiO2 nanoparticles. The doping of TiO2 nanoparticles into the polyamide-6 nanofibers were confirmed by high resolution transmission electron microscopy and energy dispersive X-ray spectroscopy. Photoluminescence（PL） and cathodoluminescence（CL） spectroscopy were also used to characterize the samples.The PL and CL spectra reveal that the as-spun polyamide-6/TiO2 composite nanofibers consisted of overlapping of two broad emission bands due to the contribution of polyamide-6（centered at about 475 nm）, which might originate from organic functional groups of polyamide-6 and TiO2 nanoparticles（centered around 550 nm）. The electrical conductivity of the polyamide-6/TiO2 composite nanofibers on different substrates was carried out.It was found that the electrical conductivity of the polyamide-6/TiO2 composite nanofibers on silicon substrate was in the range of 13 μA, and about 1 to 20 p A for the paper and glass substrates.展开更多
In this study,CuO nanoparticles are pre-modified with styrene-maleic anhydride copolymers(SMAs)of different molecular weights and MAH contents.Then the pre-modified CuO nanoparticles(CuO-SMAs)are added to the PA6/SEBS...In this study,CuO nanoparticles are pre-modified with styrene-maleic anhydride copolymers(SMAs)of different molecular weights and MAH contents.Then the pre-modified CuO nanoparticles(CuO-SMAs)are added to the PA6/SEBS(Styrene Ethylene Butylene Styrene copolymer)(40/60 wt/wt)polymer blends with a co-continuous morphology.When SMA3(MAH=8 wt%,M_(n)=250000 g/mol)is used to modify CuO nanoparticles,and the grafting degree of SMA3 on the surface of CuO reaches 2.74 wt%,90.71%of the added mCuO-SMA3 nanoparticles can be located at the interface of PA6 and SEBS.A porous PA6 membrane with CuO nanoparticles located at the pore walls can be obtained after the SEBS phase is etched with xylene.The catalytic reaction velocity constant(k)for the reduction of p-nitrophenol in NaBH_(4)solutions with the PA6/mCuO-SMA3 porous membrane can reach 1.0040 min^(-1).This work provides a feasible and straightforward method for the preparation of porous polymer membranes with functional nanoparticles located at the wall of the pores.展开更多
基金the National Natural Science Foundation of China(51973157,51673148 and 51678411),Chinathe China Postdoctoral Science Foundation Grant(2019 M651047),Chinathe Science and Technology Plans of Tianjin(No.17PTSYJC00040 and 18PTSYJC00180),China for the financial support。
文摘The utilization of all-solid-state electrolytes is considered to be an effective way to enhance the safety performance of lithium metal batteries.However,the low ionic conductivity and poor interface compatibility greatly restrict the development of all-solid-state battery.In this study,a composite electrolyte combining the electrospun polyamide 6(PA6)nanofiber membrane with hierarchical structure and the polyethylene oxide(PEO)polymer is investigated.The introduction of PA6 nanofiber membrane can effectively reduce the crystallinity of the polymer,so that the ionic conductivity of the electrolyte can be enhanced.Moreover,it is found that the presence of finely branched fibers in the hierarchical structure PA6 membrane allows the polar functional groups(C=O and N-H bonds)to be fully exposed,which provides sufficient functional sites for lithium ion transport and helps to regulate the uniform deposition of lithium metal.Moreover,the hierarchical structure can enhance the mechanical strength(9.2 MPa)of the electrolyte,thereby effectively improving the safety and cycle stability of the battery.The prepared Li/Li symmetric battery can be stably cycled for 1500 h under 0.3 mA cm^(-2) and 60℃.This study demonstrates that the prepared electrolyte has excellent application prospects in the next generation all-solid-state lithium metal batteries.
基金supported by a grant from the Korean Ministry of Education,Science and Technology(The Regional Core Research Program/Center for Healthcare Technology&Development,Chonbuk National University,Jeonju 561-756 Republic of Korea)
文摘We report on the synthesis and characterizations of TiO2 nanoparticles embedded in polyamide-6composite nanofibers by using electrospinning technique. The influence of substrate on the electrical characteristics of polyamide-6/TiO2 composite nanofibers was investigated. The resultant nanofibers exhibit good incorporation of TiO2 nanoparticles. The doping of TiO2 nanoparticles into the polyamide-6 nanofibers were confirmed by high resolution transmission electron microscopy and energy dispersive X-ray spectroscopy. Photoluminescence（PL） and cathodoluminescence（CL） spectroscopy were also used to characterize the samples.The PL and CL spectra reveal that the as-spun polyamide-6/TiO2 composite nanofibers consisted of overlapping of two broad emission bands due to the contribution of polyamide-6（centered at about 475 nm）, which might originate from organic functional groups of polyamide-6 and TiO2 nanoparticles（centered around 550 nm）. The electrical conductivity of the polyamide-6/TiO2 composite nanofibers on different substrates was carried out.It was found that the electrical conductivity of the polyamide-6/TiO2 composite nanofibers on silicon substrate was in the range of 13 μA, and about 1 to 20 p A for the paper and glass substrates.
基金the National Natural Science Foundation of China(Grant Nos.51973052,51473047 and 52003077)Natural Science Foundation of Hubei Province(2019CFB396)for the support of this work.
文摘In this study,CuO nanoparticles are pre-modified with styrene-maleic anhydride copolymers(SMAs)of different molecular weights and MAH contents.Then the pre-modified CuO nanoparticles(CuO-SMAs)are added to the PA6/SEBS(Styrene Ethylene Butylene Styrene copolymer)(40/60 wt/wt)polymer blends with a co-continuous morphology.When SMA3(MAH=8 wt%,M_(n)=250000 g/mol)is used to modify CuO nanoparticles,and the grafting degree of SMA3 on the surface of CuO reaches 2.74 wt%,90.71%of the added mCuO-SMA3 nanoparticles can be located at the interface of PA6 and SEBS.A porous PA6 membrane with CuO nanoparticles located at the pore walls can be obtained after the SEBS phase is etched with xylene.The catalytic reaction velocity constant(k)for the reduction of p-nitrophenol in NaBH_(4)solutions with the PA6/mCuO-SMA3 porous membrane can reach 1.0040 min^(-1).This work provides a feasible and straightforward method for the preparation of porous polymer membranes with functional nanoparticles located at the wall of the pores.