The conversion of waste polylactic acid(PLA)plastics into high-value-added chemicals through electrochemical methods is a promising and sustainable approach.However,developing efficient and highly selective catalysts ...The conversion of waste polylactic acid(PLA)plastics into high-value-added chemicals through electrochemical methods is a promising and sustainable approach.However,developing efficient and highly selective catalysts for lactic acid oxidation reaction(LAOR)and understanding the reaction process are challenging.Here,we report the electrooxidation of waste PLA to acetate at a high current density of 100 mA cm-2 with high Faraday efficiency(~95%)and excellent stability(>100 h)over a nickel selenide nanosheet catalyst.In addition,a total Faraday efficiency of up to 190%was achieved for carboxylic acids,including acetic acid and formic acid,by coupling with the cathodic CO_(2) reduction reaction.In situ experimental results and theoretical simulations revealed that the catalytic activity center of LAOR was dynamically formed NiOOH species,and the surface-adsorbed SeO_(x) species accelerated the formation of Ni~(3+)species,thus promoting catalytic activity.The mechanism of lactic acid electrooxidation was further elucidated.Lactic acid was dehydrogenated to produce pyruvate first and then formed CH_3CO due to preferential C-C bond cleavage,resulting in the presence of acetate.This work demonstrated a sustainable method for recycling waste PLA and CO_(2) into high-value-added products.展开更多
In this paper, poly （acrylamide-co-acrylic acid） （P（AM-co-AA）） hydrogel was pre- pared in an aqueous solution by using glow-discharge electrolysis plasma （GDEP） induced copoly- merization of acrylamide （AM） ...In this paper, poly （acrylamide-co-acrylic acid） （P（AM-co-AA）） hydrogel was pre- pared in an aqueous solution by using glow-discharge electrolysis plasma （GDEP） induced copoly- merization of acrylamide （AM） and acrylic acid （AA）, in which N,N＇-methylenebisacrylamide （MBA） was used as a crosslinker. A mechanism for the synthesis of P（AM-co-AA） hydrogel was proposed. To optimize the synthesis condition, the following parameters were examined in detail： the discharge voltage, discharge time, the content of the crosslinker, and the mass ratio of AM to AA. The results showed that the optimum pH range for cationic dyes removal was found to be 5.0-10.0. The P（AM-co-AA） hydrogel exhibits a very high adsorption potential and the ex- perimental adsorption capacities for Crystal violet （CV） and Methylene blue （MB） were 2974.3 mg/g and 2303.6 mg/g, respectively. The adsorption process follows a pseudo-second-order kinetic model. In addition, the adsorption mechanism of P（AM-co-AA） hydrogel for cationic dyes was also discussed.展开更多
Acidic poly(ionic liquid)s(PILs)with swelling ability were synthesized by free radical copolymerization of N-vinylimidazolium ionic liquids,divinylbenzene(DVB)and sodium acrylate(NaAA),and further acidification by sul...Acidic poly(ionic liquid)s(PILs)with swelling ability were synthesized by free radical copolymerization of N-vinylimidazolium ionic liquids,divinylbenzene(DVB)and sodium acrylate(NaAA),and further acidification by sulfuric acid.The swelling ability of acidic PILs was greatly affected by cross-linker content and chain length of 3-alkyl-substituents on imidazolium.Cross-linked network structures could be observed from the cryogenic scanning electron microscopy(cryo-SEM)images of the swollen acidic PILs in formic acid.Acidic PILs with network structures in swollen state exhibited excellent activities in the esterification of cyclohexene and formic acid,and the catalytic activities were in positive correlation with their swelling abilities.Acidic PIL with 3-octyl-substituent and 2.5 mol%DVB(PIL-C8-2.5DVB-HSO4)had the highest swelling ability in formic acid and exhibited comparable catalytic activities with homogeneous catalysts such as sulfuric acid and p-toluenesulfonic acid.展开更多
The novel polymer metal chelate electrolytes(polychelates)were prepared by incorporation of cobalt sulfate(Co)into poly(acrylic acid)(PAA)host matrix.Quasi-solid state supercapacitor devices were fabricated using poly...The novel polymer metal chelate electrolytes(polychelates)were prepared by incorporation of cobalt sulfate(Co)into poly(acrylic acid)(PAA)host matrix.Quasi-solid state supercapacitor devices were fabricated using polychelates,PAA-Co X(X:3,5,7,and 10)where X represents the doping fraction(w/w)of Co in PAA.All polymer metal electrolytes were showed excellent bending-stretching properties,thermal stability and electrochemical durability with an optimum ionic conductivity of 3.15×10^(-4) S cm^(-1).Hierarchically porous activated carbon and nano-sized conductive carbon were used to form carbon composite symmetrical device electrodes.The electric double-layer capacitor(EDLC)and redox reactions of Co-incorporated polychelates at the interfaces of porous activated carbon provided an optimum specific capacitance of 341.33 F g^(-1) with a device of PAA-Co7,which is at least 15 times enhancement compared to the device of pristine PAA.The PAA-Co7 device also provided energy density of 21.25 Wh kg^(-1) at a power density of 117.69 W kg^(-1).A prolonged cyclic stability of the device exhibited superior capacitive performance after 10,000 charge-discharge cycles and the maintained 90%of its initial performance.In addition,the supercapacitor with a dimension of 1.5 cm×3 cm containing PAA-Co7 successfully operated the red-blue-green(RGB)LED light.展开更多
Acid loss and plasticization of phosphoric acid(PA)-doped high-temperature polymer electrolyte membranes(HT-PEMs)are critical limitations to their practical application in fuel cells.To overcome these barriers,poly(te...Acid loss and plasticization of phosphoric acid(PA)-doped high-temperature polymer electrolyte membranes(HT-PEMs)are critical limitations to their practical application in fuel cells.To overcome these barriers,poly(terphenyl piperidinium)s constructed from the m-and p-isomers of terphenyl were synthesized to regulate the microstructure of the membrane.Highly rigid p-terphenyl units prompt the formation of moderate PA aggregates,where the ion-pair interaction between piperidinium and biphosphate is reinforced,leading to a reduction in the plasticizing effect.As a result,there are trade-offs between the proton conductivity,mechanical strength,and PA retention of the membranes with varied m/p-isomer ratios.The designed PA-doped PTP-20m membrane exhibits superior ionic conductivity,good mechanical strength,and excellent PA retention over a wide range of temperature(80–160°C)as well as satisfactory resistance to harsh accelerated aging tests.As a result,the membrane presents a desirable combination of performance(1.462 W cm^(-2) under the H_(2)/O_(2)condition,which is 1.5 times higher than that of PBI-based membrane)and durability(300 h at 160°C and 0.2 A cm^(-2))in the fuel cell.The results of this study provide new insights that will guide molecular design from the perspective of microstructure to improve the performance and robustness of HT-PEMs.展开更多
A novel cyclodextrin-containing polymer was prepared by graftingβ-cyclodextrin onto the backbone of poly(D,L-lactic acid)(PLA).First,mono(6-(2-aminoethyl)amino-6-deoxy)-β-cyclodextrin(β-CD-6-en)was prepared by sulf...A novel cyclodextrin-containing polymer was prepared by graftingβ-cyclodextrin onto the backbone of poly(D,L-lactic acid)(PLA).First,mono(6-(2-aminoethyl)amino-6-deoxy)-β-cyclodextrin(β-CD-6-en)was prepared by sulfonylation and amination ofβ-cyclodextrin and modified poly(D,L-lactic acid)(MPLA)was prepared by free radical polymerization of maleic anhydride and PLA.Then,grafting ofβ-cyclodextrin derivative to MPLA backbone was carried out by N-acylation reaction of MPLA andβ-CD-6-en in dimethyl formamide.The...展开更多
基金financially supported by the National Key R&D Program of China (2021YFA1501700)the National Science Foundation of China (22272114)+4 种基金the Fundamental Research Funds from Sichuan University (2022SCUNL103)the Funding for Hundred Talent Program of Sichuan University (20822041E4079)the NSFC (22102018 and 52171201)the Huzhou Science and Technology Bureau (2022GZ45)the Hefei National Research Center for Physical Sciences at the Microscale (KF2021005)。
文摘The conversion of waste polylactic acid(PLA)plastics into high-value-added chemicals through electrochemical methods is a promising and sustainable approach.However,developing efficient and highly selective catalysts for lactic acid oxidation reaction(LAOR)and understanding the reaction process are challenging.Here,we report the electrooxidation of waste PLA to acetate at a high current density of 100 mA cm-2 with high Faraday efficiency(~95%)and excellent stability(>100 h)over a nickel selenide nanosheet catalyst.In addition,a total Faraday efficiency of up to 190%was achieved for carboxylic acids,including acetic acid and formic acid,by coupling with the cathodic CO_(2) reduction reaction.In situ experimental results and theoretical simulations revealed that the catalytic activity center of LAOR was dynamically formed NiOOH species,and the surface-adsorbed SeO_(x) species accelerated the formation of Ni~(3+)species,thus promoting catalytic activity.The mechanism of lactic acid electrooxidation was further elucidated.Lactic acid was dehydrogenated to produce pyruvate first and then formed CH_3CO due to preferential C-C bond cleavage,resulting in the presence of acetate.This work demonstrated a sustainable method for recycling waste PLA and CO_(2) into high-value-added products.
基金supported by National Natural Science Foundation of China(No.21367023)Natural Science Foundation of Gansu Province,China(No.1208RJZA161)Key Project of Young Teachers’ Scientific Research Promotion of Northwest Normal University of China(Nos.NWNU-LKQN-10-16 and NWNU-LKQN-12-9)
文摘In this paper, poly （acrylamide-co-acrylic acid） （P（AM-co-AA）） hydrogel was pre- pared in an aqueous solution by using glow-discharge electrolysis plasma （GDEP） induced copoly- merization of acrylamide （AM） and acrylic acid （AA）, in which N,N＇-methylenebisacrylamide （MBA） was used as a crosslinker. A mechanism for the synthesis of P（AM-co-AA） hydrogel was proposed. To optimize the synthesis condition, the following parameters were examined in detail： the discharge voltage, discharge time, the content of the crosslinker, and the mass ratio of AM to AA. The results showed that the optimum pH range for cationic dyes removal was found to be 5.0-10.0. The P（AM-co-AA） hydrogel exhibits a very high adsorption potential and the ex- perimental adsorption capacities for Crystal violet （CV） and Methylene blue （MB） were 2974.3 mg/g and 2303.6 mg/g, respectively. The adsorption process follows a pseudo-second-order kinetic model. In addition, the adsorption mechanism of P（AM-co-AA） hydrogel for cationic dyes was also discussed.
基金This work was supported by the National Natural Science Foundation of China(21773068,21811530273,21573072)the National Key Research and Development Program of China(2017YFA0403102)Shanghai Leading Academic Discipline Project(B409).
文摘Acidic poly(ionic liquid)s(PILs)with swelling ability were synthesized by free radical copolymerization of N-vinylimidazolium ionic liquids,divinylbenzene(DVB)and sodium acrylate(NaAA),and further acidification by sulfuric acid.The swelling ability of acidic PILs was greatly affected by cross-linker content and chain length of 3-alkyl-substituents on imidazolium.Cross-linked network structures could be observed from the cryogenic scanning electron microscopy(cryo-SEM)images of the swollen acidic PILs in formic acid.Acidic PILs with network structures in swollen state exhibited excellent activities in the esterification of cyclohexene and formic acid,and the catalytic activities were in positive correlation with their swelling abilities.Acidic PIL with 3-octyl-substituent and 2.5 mol%DVB(PIL-C8-2.5DVB-HSO4)had the highest swelling ability in formic acid and exhibited comparable catalytic activities with homogeneous catalysts such as sulfuric acid and p-toluenesulfonic acid.
基金Deputyship for Research&Innovation,Ministry of Education in Saudi Arabia for funding this research work。
文摘The novel polymer metal chelate electrolytes(polychelates)were prepared by incorporation of cobalt sulfate(Co)into poly(acrylic acid)(PAA)host matrix.Quasi-solid state supercapacitor devices were fabricated using polychelates,PAA-Co X(X:3,5,7,and 10)where X represents the doping fraction(w/w)of Co in PAA.All polymer metal electrolytes were showed excellent bending-stretching properties,thermal stability and electrochemical durability with an optimum ionic conductivity of 3.15×10^(-4) S cm^(-1).Hierarchically porous activated carbon and nano-sized conductive carbon were used to form carbon composite symmetrical device electrodes.The electric double-layer capacitor(EDLC)and redox reactions of Co-incorporated polychelates at the interfaces of porous activated carbon provided an optimum specific capacitance of 341.33 F g^(-1) with a device of PAA-Co7,which is at least 15 times enhancement compared to the device of pristine PAA.The PAA-Co7 device also provided energy density of 21.25 Wh kg^(-1) at a power density of 117.69 W kg^(-1).A prolonged cyclic stability of the device exhibited superior capacitive performance after 10,000 charge-discharge cycles and the maintained 90%of its initial performance.In addition,the supercapacitor with a dimension of 1.5 cm×3 cm containing PAA-Co7 successfully operated the red-blue-green(RGB)LED light.
基金supported by The National Key Research and Development Program of China(2021YFB4001204)National Natural Science Foundation of China(22379143)。
文摘Acid loss and plasticization of phosphoric acid(PA)-doped high-temperature polymer electrolyte membranes(HT-PEMs)are critical limitations to their practical application in fuel cells.To overcome these barriers,poly(terphenyl piperidinium)s constructed from the m-and p-isomers of terphenyl were synthesized to regulate the microstructure of the membrane.Highly rigid p-terphenyl units prompt the formation of moderate PA aggregates,where the ion-pair interaction between piperidinium and biphosphate is reinforced,leading to a reduction in the plasticizing effect.As a result,there are trade-offs between the proton conductivity,mechanical strength,and PA retention of the membranes with varied m/p-isomer ratios.The designed PA-doped PTP-20m membrane exhibits superior ionic conductivity,good mechanical strength,and excellent PA retention over a wide range of temperature(80–160°C)as well as satisfactory resistance to harsh accelerated aging tests.As a result,the membrane presents a desirable combination of performance(1.462 W cm^(-2) under the H_(2)/O_(2)condition,which is 1.5 times higher than that of PBI-based membrane)and durability(300 h at 160°C and 0.2 A cm^(-2))in the fuel cell.The results of this study provide new insights that will guide molecular design from the perspective of microstructure to improve the performance and robustness of HT-PEMs.
基金Funded by the Natural Science Foundation of China(No.50603032)Education Commission of Chongqing(No.KJ090617)the Science and Technology Plan Project of Jiulongpo District,Chongqing,China(No.2008Q95)
文摘A novel cyclodextrin-containing polymer was prepared by graftingβ-cyclodextrin onto the backbone of poly(D,L-lactic acid)(PLA).First,mono(6-(2-aminoethyl)amino-6-deoxy)-β-cyclodextrin(β-CD-6-en)was prepared by sulfonylation and amination ofβ-cyclodextrin and modified poly(D,L-lactic acid)(MPLA)was prepared by free radical polymerization of maleic anhydride and PLA.Then,grafting ofβ-cyclodextrin derivative to MPLA backbone was carried out by N-acylation reaction of MPLA andβ-CD-6-en in dimethyl formamide.The...