Herein,manganese(Mn)‑doped poly(1,5‑diaminonaphthalene)(PN)electrode material(Mn@PN)was synthesized via chemical oxidative polymerization.The material′s distinctive vesicular architecture enables rapid ion transport ...Herein,manganese(Mn)‑doped poly(1,5‑diaminonaphthalene)(PN)electrode material(Mn@PN)was synthesized via chemical oxidative polymerization.The material′s distinctive vesicular architecture enables rapid ion transport while maintaining the structural stability of the electrode under continuous charge‑discharge cycles.Electrochemical characterization under a three‑electrode system revealed exceptional rate capability:Mn@PN delivered an ultrahigh specific capacitance of 10318 F·g^(-1) at a low current density of 3 A·g^(-1) and retained 9415 F·g^(-1)(91.2%retention compared to the value at 3 A·g^(-1))even at an ultrahigh current density of 50 A·g^(-1).Moreover,the material exhibited 97.4%capacitance retention after 9000 cycles at 30 A·g^(-1),corresponding with a low capacitance decay rate of 0.003‰per cycle,significantly outperforming conventional conductive polymers like polyaniline(PANI).An asymmetric supercapacitor assembled with Mn@PN as the positive electrode(Mn@PN||AC)achieved an energy density of 328 Wh·kg^(-1) at 15 A·g^(-1) and retained 80.7%of its initial specific capacitance after 4000 cycles at 20 A·g^(-1).展开更多
Poly（vinylidene fluoride-co-hexafluoropropylene） （PVDF-HFP） based composite polymer electrolyte （CPE） modified with CeO2, La2O3 and Y2O3 nano-rare earth oxides was prepared by phase inversion technique. Physical...Poly（vinylidene fluoride-co-hexafluoropropylene） （PVDF-HFP） based composite polymer electrolyte （CPE） modified with CeO2, La2O3 and Y2O3 nano-rare earth oxides was prepared by phase inversion technique. Physical and chemical properties of the modified CPEs were studied by SEM, TG-DSC and electrochemical methods. The results show that the CPE modified with 10% La2O3 （mass fraction） has the best practical applicability, which indicates that the thermal and electrochemical stability can reach over 400 ℃ and 4.5 V, respectively, and temperature dependence of ionic conductivity follows Vogel-Tamman-Fulcher （VTF） relationship and ionic conductivity at room temperature is up to 3.3 mS/cm. The interfacial resistance Ri reaches a stable value about 557 Ω after 6 d storage.展开更多
A polymer electrolyte based on poly(vinylidene) fluoride-hexafluoropropylene was prepared by evaporating the solvent of dimethyl formamide, and non-woven fabric was used to reinforce the mechanical strength of polymer...A polymer electrolyte based on poly(vinylidene) fluoride-hexafluoropropylene was prepared by evaporating the solvent of dimethyl formamide, and non-woven fabric was used to reinforce the mechanical strength of polymer electrolyte and maintain a good interfacial property between the polymer electrolyte and electrodes. Polymer lithium batteries were assembled by using LiCoO2 as cathode material and lithium foil as anode material. Scanning electron microscopy, alternating current impedance, linear sweep voltammetry and charge-discharge tests were used to study the properties of polymer membrane and polymer Li-ion batteries. The results show that the technics of preparing polymer electrolyte by directly evaporating solvent is simple. The polymer membrane has rich micro-porous structure on both sides and exhibits 280% uptake of electrolyte solution. The electrochemical stability window of this polymer electrolyte is about 5.5 V, and its ionic conductivity at room temperature reaches 0.151 S/m. The polymer lithium battery displays an initial discharge capacity of 138 mA·h/g and discharge plateau of about 3.9 V at 0.2 current rate. After 30 cycles, its loss of discharge capacity is only 2%. When the battery discharges at 0.5 current rate, the voltage plateau is still 3.7 V. The discharge capacities of 0.5 and 1.0 current rates are 96% and 93% of that of 0.1 current rate, respectively.展开更多
文摘Herein,manganese(Mn)‑doped poly(1,5‑diaminonaphthalene)(PN)electrode material(Mn@PN)was synthesized via chemical oxidative polymerization.The material′s distinctive vesicular architecture enables rapid ion transport while maintaining the structural stability of the electrode under continuous charge‑discharge cycles.Electrochemical characterization under a three‑electrode system revealed exceptional rate capability:Mn@PN delivered an ultrahigh specific capacitance of 10318 F·g^(-1) at a low current density of 3 A·g^(-1) and retained 9415 F·g^(-1)(91.2%retention compared to the value at 3 A·g^(-1))even at an ultrahigh current density of 50 A·g^(-1).Moreover,the material exhibited 97.4%capacitance retention after 9000 cycles at 30 A·g^(-1),corresponding with a low capacitance decay rate of 0.003‰per cycle,significantly outperforming conventional conductive polymers like polyaniline(PANI).An asymmetric supercapacitor assembled with Mn@PN as the positive electrode(Mn@PN||AC)achieved an energy density of 328 Wh·kg^(-1) at 15 A·g^(-1) and retained 80.7%of its initial specific capacitance after 4000 cycles at 20 A·g^(-1).
基金Project(2011FJ1005)supported by the Major Provincial Science and Technology Program of Hunan Province,ChinaProject(2010qzzd0101)supported by the Central College on the 2010 Operational Costs of Basic Research Program,China
文摘Poly（vinylidene fluoride-co-hexafluoropropylene） （PVDF-HFP） based composite polymer electrolyte （CPE） modified with CeO2, La2O3 and Y2O3 nano-rare earth oxides was prepared by phase inversion technique. Physical and chemical properties of the modified CPEs were studied by SEM, TG-DSC and electrochemical methods. The results show that the CPE modified with 10% La2O3 （mass fraction） has the best practical applicability, which indicates that the thermal and electrochemical stability can reach over 400 ℃ and 4.5 V, respectively, and temperature dependence of ionic conductivity follows Vogel-Tamman-Fulcher （VTF） relationship and ionic conductivity at room temperature is up to 3.3 mS/cm. The interfacial resistance Ri reaches a stable value about 557 Ω after 6 d storage.
基金Project (2003AA32X010) supported by the National High Technology Research and Development Program of China
文摘A polymer electrolyte based on poly(vinylidene) fluoride-hexafluoropropylene was prepared by evaporating the solvent of dimethyl formamide, and non-woven fabric was used to reinforce the mechanical strength of polymer electrolyte and maintain a good interfacial property between the polymer electrolyte and electrodes. Polymer lithium batteries were assembled by using LiCoO2 as cathode material and lithium foil as anode material. Scanning electron microscopy, alternating current impedance, linear sweep voltammetry and charge-discharge tests were used to study the properties of polymer membrane and polymer Li-ion batteries. The results show that the technics of preparing polymer electrolyte by directly evaporating solvent is simple. The polymer membrane has rich micro-porous structure on both sides and exhibits 280% uptake of electrolyte solution. The electrochemical stability window of this polymer electrolyte is about 5.5 V, and its ionic conductivity at room temperature reaches 0.151 S/m. The polymer lithium battery displays an initial discharge capacity of 138 mA·h/g and discharge plateau of about 3.9 V at 0.2 current rate. After 30 cycles, its loss of discharge capacity is only 2%. When the battery discharges at 0.5 current rate, the voltage plateau is still 3.7 V. The discharge capacities of 0.5 and 1.0 current rates are 96% and 93% of that of 0.1 current rate, respectively.