Electrospun WO_(3) nanofibers were fabricated by coaxial electrospinning and directly annealing WCl_(6)/polyvinylpyrrolidone(PVP) nanofibers on activated carbon fibres(ACF), and characterized by scanning electron micr...Electrospun WO_(3) nanofibers were fabricated by coaxial electrospinning and directly annealing WCl_(6)/polyvinylpyrrolidone(PVP) nanofibers on activated carbon fibres(ACF), and characterized by scanning electron microscopy(SEM) and X-ray diffractometry(XRD). The most suitable condition for electrospinning is the mass ratio of WCl_(6) to PVP 0.6, appropriate amount DMF and ethanol, a voltage of 28 kV, the reception distance of 15 cm, the humidity range within 10% and 20% and the moving rate of the pump 0.001 mm/s. The photocatalytic activities of WO_(3) nanofibers were evaluated by the photo-degradation of phenol solution under the irradiation of 500 W xenon lamp. The results showed that, the sizes of the fibers are about 100 nm, and after being photodegraded for 210 min, the concentration of phenol decreased from 20.05 mg/L to 8.60 mg/L. Thus, the photo-degradation rate of WO_(3) nanofibers for phenol solution is 2.87 mg/(L·h).展开更多
基金Project(15B003)supported by the Outlayed-up Youth Project of Hunan Provincial Department of Education,ChinaProject(KY201623)supported by the Housing and Urban Construction Department of Hunan Province,China+1 种基金Project(2016CL02)supported by the Hunan Provincial Key Laboratory of Materials Protection for Electric Power and Transportation,ChinaProject(11405013)supported by the National Natural Science Foundation of China
文摘Electrospun WO_(3) nanofibers were fabricated by coaxial electrospinning and directly annealing WCl_(6)/polyvinylpyrrolidone(PVP) nanofibers on activated carbon fibres(ACF), and characterized by scanning electron microscopy(SEM) and X-ray diffractometry(XRD). The most suitable condition for electrospinning is the mass ratio of WCl_(6) to PVP 0.6, appropriate amount DMF and ethanol, a voltage of 28 kV, the reception distance of 15 cm, the humidity range within 10% and 20% and the moving rate of the pump 0.001 mm/s. The photocatalytic activities of WO_(3) nanofibers were evaluated by the photo-degradation of phenol solution under the irradiation of 500 W xenon lamp. The results showed that, the sizes of the fibers are about 100 nm, and after being photodegraded for 210 min, the concentration of phenol decreased from 20.05 mg/L to 8.60 mg/L. Thus, the photo-degradation rate of WO_(3) nanofibers for phenol solution is 2.87 mg/(L·h).