Effects of Zn/P ratio on the structures and properties of glasses with the general composition of （80-x）ZnO-20Fe2O3-xP2O5 （x=40, 45, 50, 55, 60） （molar fraction, %） were investigated. Glass structure was measure...Effects of Zn/P ratio on the structures and properties of glasses with the general composition of （80-x）ZnO-20Fe2O3-xP2O5 （x=40, 45, 50, 55, 60） （molar fraction, %） were investigated. Glass structure was measured by infrared absorption spectrum. Glass density （/9） was measured by the Archimedes method. Coefficients of thermal expansion （a） and characterization temperature were obtained by a dilatometer. Water durability of each glass was estimated from the dissolution rate （DR）in water at 90 ℃ for 24 h. With increasing Zn/P ratio, water durability of zinc-iron phosphate glasses increases dramatically without large increase in the characterization temperature. （80-x）ZnO-20Fe2O3-xP2O5 glasses with 0.3≤Zn/P≤0.5 are suit for low-to-mid temperature sealing application for substrates with a〈8.0× 10^-6℃^-1.展开更多
基金Project(7602110340) supported by the Postdoctoral Science Foundation of Central South University, ChinaProject(721500277)supported by the Fundamental Research Funds for the Central Universities of China
文摘Effects of Zn/P ratio on the structures and properties of glasses with the general composition of （80-x）ZnO-20Fe2O3-xP2O5 （x=40, 45, 50, 55, 60） （molar fraction, %） were investigated. Glass structure was measured by infrared absorption spectrum. Glass density （/9） was measured by the Archimedes method. Coefficients of thermal expansion （a） and characterization temperature were obtained by a dilatometer. Water durability of each glass was estimated from the dissolution rate （DR）in water at 90 ℃ for 24 h. With increasing Zn/P ratio, water durability of zinc-iron phosphate glasses increases dramatically without large increase in the characterization temperature. （80-x）ZnO-20Fe2O3-xP2O5 glasses with 0.3≤Zn/P≤0.5 are suit for low-to-mid temperature sealing application for substrates with a〈8.0× 10^-6℃^-1.