Anatase TiO2 nanosheets（-ns-） with dominant exposed {001} facets were used as support to load copper,and the synthesized Cu/TiO2-ns catalysts were evaluated for CO2 hydrogenation to methanol. Under the reaction cond...Anatase TiO2 nanosheets（-ns-） with dominant exposed {001} facets were used as support to load copper,and the synthesized Cu/TiO2-ns catalysts were evaluated for CO2 hydrogenation to methanol. Under the reaction conditions, P = 3.0 MPa, T = 260 ℃, V（N2）：V（H2）：V（CO2） = 8：69：23 and gas hourly space velocity（GHSV） = 3600 mL g-1h-1, the methanol yield reached an appealing high value, 5.6%. Copper-loading amount, calcination temperature and reduction atmosphere have been investigated in this work, which significantly influence the particle sizes of copper and/or the defect concentration in TiO2, then leading to different catalytic performance. Characterizations of XRD, EPR, CO2-TPD and FTIR demonstrate that higher specific surface area of Cu is good for the hydrogenation of CO2 and adequate amount of Ti3＋ plays important roles in CO2 activation. Both of them facilitate high turnover frequency（TOF） of methanol formation.展开更多
A type of TiO/bamboo charcoal composite made by a dip-dry method was loaded onto wood veneer with a vacuum- pressure method in order to prepare modified poplar veneer. The pore structure parameters and surface morphol...A type of TiO/bamboo charcoal composite made by a dip-dry method was loaded onto wood veneer with a vacuum- pressure method in order to prepare modified poplar veneer. The pore structure parameters and surface morphology of the TiO2/ bamboo charcoal composite were determined and analyzed by means of a porosimetry analyzer and SEM. The results show that the surface morphology of the composite does not change after being loaded with nano TiO2. However, its specific surface area （359.814 m^2·g^-1）, pore volume （0.317 cm^3.g^-1） and average pore diameter （3.526 nm） increased; particularly the cumulative volume of pores was increased by 65.83%. In addition, the distribution range of the pores was wider than that of the bamboo charcoal. Combining the SEM of unmodified and modified poplar veneer, the results of X-ray photoelectron spectroscopy revealed that actually some TiOz compounds, i.e., 4.08%, are imbedded in the modified poplar veneer.展开更多
基金financially supported by the National Natural Science Foundation of China (no. 91645119, 21207039, B5151050)the Fundamental Research Funds for the Central Universities (No.2017ZD076)+2 种基金Guangzhou science and technology plan (201607010095)the Natural Science Foundation of Guangdong Province, China (Grant no. S2011010000737)State Key Laboratory of Physical Chemistry of Solid Surfaces, Xiamen University, P.R. China (No. 201602)
文摘Anatase TiO2 nanosheets（-ns-） with dominant exposed {001} facets were used as support to load copper,and the synthesized Cu/TiO2-ns catalysts were evaluated for CO2 hydrogenation to methanol. Under the reaction conditions, P = 3.0 MPa, T = 260 ℃, V（N2）：V（H2）：V（CO2） = 8：69：23 and gas hourly space velocity（GHSV） = 3600 mL g-1h-1, the methanol yield reached an appealing high value, 5.6%. Copper-loading amount, calcination temperature and reduction atmosphere have been investigated in this work, which significantly influence the particle sizes of copper and/or the defect concentration in TiO2, then leading to different catalytic performance. Characterizations of XRD, EPR, CO2-TPD and FTIR demonstrate that higher specific surface area of Cu is good for the hydrogenation of CO2 and adequate amount of Ti3＋ plays important roles in CO2 activation. Both of them facilitate high turnover frequency（TOF） of methanol formation.
基金A Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions for financial support to conduct this research
文摘A type of TiO/bamboo charcoal composite made by a dip-dry method was loaded onto wood veneer with a vacuum- pressure method in order to prepare modified poplar veneer. The pore structure parameters and surface morphology of the TiO2/ bamboo charcoal composite were determined and analyzed by means of a porosimetry analyzer and SEM. The results show that the surface morphology of the composite does not change after being loaded with nano TiO2. However, its specific surface area （359.814 m^2·g^-1）, pore volume （0.317 cm^3.g^-1） and average pore diameter （3.526 nm） increased; particularly the cumulative volume of pores was increased by 65.83%. In addition, the distribution range of the pores was wider than that of the bamboo charcoal. Combining the SEM of unmodified and modified poplar veneer, the results of X-ray photoelectron spectroscopy revealed that actually some TiOz compounds, i.e., 4.08%, are imbedded in the modified poplar veneer.