Coal fly ash is a typical secondary aluminum/silicon resource.The preparation of zeolite-type absorbent is a potential way for its value-added utilization,while the purity and adsorption property of zeolite are limite...Coal fly ash is a typical secondary aluminum/silicon resource.The preparation of zeolite-type absorbent is a potential way for its value-added utilization,while the purity and adsorption property of zeolite are limited due to the occurrence of side reactions in the synthesis process.In this study,a designated composite consisted of crystalline zeolites and amorphous calcium silicate hydrate was selected,which was direct synthesized from fly ash under conditions of a Ca/Si molar ratio of 0.8,an initial NaOH concentration of 0.5 mol/L,a hydrothermal temperature of 170℃and a liquid–solid ratio of 15 mL/g.The results indicated that this composite had superior adsorption property for a variety of heavy metals,which was based on the exchange of calcium and sodium ions in zeolites and calcium silicate hydrate.Its adsorption capacities for Pb^(2+),Ni^(2+),Cd^(2+),Zn^(2+),Cu^(2+)and Cr^(3+)attained 409.4,222.4,147.5,93.2,101.1 and 157.0 mg/g,respectively,in single solution with a pH of 4.5.After regulating the synthesis conditions,the transformation of amorphous calcium silicate hydrate into crystallized tobermorite weakened the adsorption capacity of the composite.Besides,due to the competitive adsorption in a multiple ions solution,the adsorption capacities for these heavy metals had a reduction.展开更多
基金This work was supported by the National Natural Science Foun-dation of China(No.52174273)the Basic Science Center Project for National Natural Science Foundation of China(No.72088101)+1 种基金the Postdoctoral Science Foundation of China(No.2021TQ0370)the Science and Technology Innovation Program of Hunan Pro-vince(No.2021RC2003).
文摘Coal fly ash is a typical secondary aluminum/silicon resource.The preparation of zeolite-type absorbent is a potential way for its value-added utilization,while the purity and adsorption property of zeolite are limited due to the occurrence of side reactions in the synthesis process.In this study,a designated composite consisted of crystalline zeolites and amorphous calcium silicate hydrate was selected,which was direct synthesized from fly ash under conditions of a Ca/Si molar ratio of 0.8,an initial NaOH concentration of 0.5 mol/L,a hydrothermal temperature of 170℃and a liquid–solid ratio of 15 mL/g.The results indicated that this composite had superior adsorption property for a variety of heavy metals,which was based on the exchange of calcium and sodium ions in zeolites and calcium silicate hydrate.Its adsorption capacities for Pb^(2+),Ni^(2+),Cd^(2+),Zn^(2+),Cu^(2+)and Cr^(3+)attained 409.4,222.4,147.5,93.2,101.1 and 157.0 mg/g,respectively,in single solution with a pH of 4.5.After regulating the synthesis conditions,the transformation of amorphous calcium silicate hydrate into crystallized tobermorite weakened the adsorption capacity of the composite.Besides,due to the competitive adsorption in a multiple ions solution,the adsorption capacities for these heavy metals had a reduction.