Effect of electromagnetic stirring on microstructure of AZ91-0.8%Ce magnesium alloy was investigated. The results show that electromagnetic stirring causes a change of morphology of α-Mg phase from coarse dendrites t...Effect of electromagnetic stirring on microstructure of AZ91-0.8%Ce magnesium alloy was investigated. The results show that electromagnetic stirring causes a change of morphology of α-Mg phase from coarse dendrites to fine rosette-like or spherical shape. Grain size is significantly refined within the range of input voltage 75?125 V, moreover, the optimum input voltage corresponded to the minimum value (64 μm) of grain size is 125 V. Compared to the non-stirred condition, the amount of β-Mg17Al12 precipitate under the stirred condition obviously increases. The grain refinement of AZ91-0.8%Ce alloy is mainly attributed to multiplication of existing grains in the melt caused by forced fluid flow under electromagnetic stirring condition. Addition of 0.8% Ce results in the formation of ‘necking’ at secondary dendrite arm roots of α-Mg crystals, and consequently, it is helpful to increase the number of heterogeneous nucleation.展开更多
Fine-grained 01420 Al-Li alloy sheets were produced by thermo-mechanical processing based on the mechanism of particle stimulated nucleation of recrystallization.The thermo-mechanically processed sheets were observed ...Fine-grained 01420 Al-Li alloy sheets were produced by thermo-mechanical processing based on the mechanism of particle stimulated nucleation of recrystallization.The thermo-mechanically processed sheets were observed to contain layers of different microstructures along the thickness.The precipitate behavior of the second phase particles and their effects on the distribution of dislocations and layered recrystallized grain structure were analyzed by optical microscopy(OM),scanning electron microscopy(SEM),transmission electron microscopy(TEM) and X-ray diffractometry(XRD).The formation mechanism of the gradient particles was discussed.The results show that after aging,a gradient distribution of large particles along the thickness is observed,the particles in the surface layer(SL) are distributed homogeneously,whereas those in the center layer(CL) are mainly distributed parallel to the rolling direction,and the volume fraction of the particles in the SL is higher than that in the CL.Subsequent rolling in the presence of layer-distributed particles results in a corresponding homogeneous distribution of highly strained regions in the SL and a banded distribution of them in CL,which is the main reason for the formation of layered grain structure along the thickness in the sheets.展开更多
通过SEM、EDS和XRD,研究了稀土La添加量(0.1wt%、0.2wt%、0.4wt%、0.8wt%)对6082铝合金铸态组织和力学性能的影响。结果表明:稀土La可以明显细化合金晶粒、有效调控第二相并提高合金的力学性能。随着合金中稀土La含量的增加,合金晶粒尺...通过SEM、EDS和XRD,研究了稀土La添加量(0.1wt%、0.2wt%、0.4wt%、0.8wt%)对6082铝合金铸态组织和力学性能的影响。结果表明:稀土La可以明显细化合金晶粒、有效调控第二相并提高合金的力学性能。随着合金中稀土La含量的增加,合金晶粒尺寸先减小后增加,当稀土La含量为0.2wt%时合金的晶粒细化效果最好,此时合金的抗拉强度、屈服强度和伸长率均达到最高,分别为181 MPa、167 MPa和5.43%,明显优于未添加稀土La的合金抗拉强度、屈服强度和伸长率(128 MPa、87 MPa和4.68%)。稀土La的添加能将细长条状的β-Al Fe Si相调控成π状α-Al Si Fe相,大大降低了应力集中,从而有效提高合金的力学性能。展开更多
In order to prolong the service life of aircraft skin made from AA2524, the effects of laser shock peening(LSP) on fatigue crack growth(FCG) rate and fracture toughness(K_(c)) of AA2524 were investigated. Multiple LSP...In order to prolong the service life of aircraft skin made from AA2524, the effects of laser shock peening(LSP) on fatigue crack growth(FCG) rate and fracture toughness(K_(c)) of AA2524 were investigated. Multiple LSP treatment was performed on compact tension(CT) specimen from single side and double sides. The surface integrity was measured with Vickers hardness tester, X-ray diffractometer and confocal laser scanning microscope, respectively. FCG rate test and fracture toughness test under plane stress were carried out after LSP treatment. The microstructure features of cross-sections were observed with scanning electron microscope. The results showed that the micro-hardness and residual stress of CT specimens were increased dramatically after LSP treatment. Compared to the base metal(BM), the fatigue life was prolonged by 2.4 times and fracture toughness was increased by 22% after multiple LSP.展开更多
An Al-3Ti-0.2C-1RE grain refiner was prepared by in-situ reaction method.The microstructure was investigated by optical microscopy(OM),scanning electron microscopy(SEM) equipped with energy-dispersive spectrometry(EDS...An Al-3Ti-0.2C-1RE grain refiner was prepared by in-situ reaction method.The microstructure was investigated by optical microscopy(OM),scanning electron microscopy(SEM) equipped with energy-dispersive spectrometry(EDS) and X-ray diffraction(XRD).The results show that the Al-3Ti-0.2C-1RE grain refiner is composed of α-Al,TiAl3,TiC and Ti2 Al20 Ce phases.Compared with Al-3Ti-0.2C refiner,the morphology of TiAl3 phase is changed and Ti2 Al20 Ce phases form with the addition of RE.Accordingly,the refining performance is improved.The phase forming process of the refiner is as follows: Blocky Ti2 Al20 Ce and fine blocky TiAl3 form in the melt at the initial stage of reaction,then the fine blocky TiAl3 gradually disappears,and the blocky Ti2 Al20 Ce grows bigger with the increase of holding time.The predominant mechanism to synthesize TiC particles is the reaction between high concentration of solute Ti atoms and graphite particles.展开更多
基金Project(2004ABA110) supported by the Natural Science Foundation of Hubei Province project(471-38300843) supported by the Research Foundation for the Doctoral Program of Wuhan University of Technology
文摘Effect of electromagnetic stirring on microstructure of AZ91-0.8%Ce magnesium alloy was investigated. The results show that electromagnetic stirring causes a change of morphology of α-Mg phase from coarse dendrites to fine rosette-like or spherical shape. Grain size is significantly refined within the range of input voltage 75?125 V, moreover, the optimum input voltage corresponded to the minimum value (64 μm) of grain size is 125 V. Compared to the non-stirred condition, the amount of β-Mg17Al12 precipitate under the stirred condition obviously increases. The grain refinement of AZ91-0.8%Ce alloy is mainly attributed to multiplication of existing grains in the melt caused by forced fluid flow under electromagnetic stirring condition. Addition of 0.8% Ce results in the formation of ‘necking’ at secondary dendrite arm roots of α-Mg crystals, and consequently, it is helpful to increase the number of heterogeneous nucleation.
基金Project(2006DFA53250) supported by the International Science and Technology Cooperation Program of ChinaProject(2005CB623706) supported by the Major State Basic Research Development Program of China
文摘Fine-grained 01420 Al-Li alloy sheets were produced by thermo-mechanical processing based on the mechanism of particle stimulated nucleation of recrystallization.The thermo-mechanically processed sheets were observed to contain layers of different microstructures along the thickness.The precipitate behavior of the second phase particles and their effects on the distribution of dislocations and layered recrystallized grain structure were analyzed by optical microscopy(OM),scanning electron microscopy(SEM),transmission electron microscopy(TEM) and X-ray diffractometry(XRD).The formation mechanism of the gradient particles was discussed.The results show that after aging,a gradient distribution of large particles along the thickness is observed,the particles in the surface layer(SL) are distributed homogeneously,whereas those in the center layer(CL) are mainly distributed parallel to the rolling direction,and the volume fraction of the particles in the SL is higher than that in the CL.Subsequent rolling in the presence of layer-distributed particles results in a corresponding homogeneous distribution of highly strained regions in the SL and a banded distribution of them in CL,which is the main reason for the formation of layered grain structure along the thickness in the sheets.
文摘通过SEM、EDS和XRD,研究了稀土La添加量(0.1wt%、0.2wt%、0.4wt%、0.8wt%)对6082铝合金铸态组织和力学性能的影响。结果表明:稀土La可以明显细化合金晶粒、有效调控第二相并提高合金的力学性能。随着合金中稀土La含量的增加,合金晶粒尺寸先减小后增加,当稀土La含量为0.2wt%时合金的晶粒细化效果最好,此时合金的抗拉强度、屈服强度和伸长率均达到最高,分别为181 MPa、167 MPa和5.43%,明显优于未添加稀土La的合金抗拉强度、屈服强度和伸长率(128 MPa、87 MPa和4.68%)。稀土La的添加能将细长条状的β-Al Fe Si相调控成π状α-Al Si Fe相,大大降低了应力集中,从而有效提高合金的力学性能。
基金Project(52075552) supported by the National Natural Science Foundation of ChinaProject(kq2007085) supported by Changsha Municipal Natural Science Foundation,China。
文摘In order to prolong the service life of aircraft skin made from AA2524, the effects of laser shock peening(LSP) on fatigue crack growth(FCG) rate and fracture toughness(K_(c)) of AA2524 were investigated. Multiple LSP treatment was performed on compact tension(CT) specimen from single side and double sides. The surface integrity was measured with Vickers hardness tester, X-ray diffractometer and confocal laser scanning microscope, respectively. FCG rate test and fracture toughness test under plane stress were carried out after LSP treatment. The microstructure features of cross-sections were observed with scanning electron microscope. The results showed that the micro-hardness and residual stress of CT specimens were increased dramatically after LSP treatment. Compared to the base metal(BM), the fatigue life was prolonged by 2.4 times and fracture toughness was increased by 22% after multiple LSP.
基金Project(51174177)supported by the National Natural Science Foundation of China
文摘An Al-3Ti-0.2C-1RE grain refiner was prepared by in-situ reaction method.The microstructure was investigated by optical microscopy(OM),scanning electron microscopy(SEM) equipped with energy-dispersive spectrometry(EDS) and X-ray diffraction(XRD).The results show that the Al-3Ti-0.2C-1RE grain refiner is composed of α-Al,TiAl3,TiC and Ti2 Al20 Ce phases.Compared with Al-3Ti-0.2C refiner,the morphology of TiAl3 phase is changed and Ti2 Al20 Ce phases form with the addition of RE.Accordingly,the refining performance is improved.The phase forming process of the refiner is as follows: Blocky Ti2 Al20 Ce and fine blocky TiAl3 form in the melt at the initial stage of reaction,then the fine blocky TiAl3 gradually disappears,and the blocky Ti2 Al20 Ce grows bigger with the increase of holding time.The predominant mechanism to synthesize TiC particles is the reaction between high concentration of solute Ti atoms and graphite particles.