The effects of forming damage are analyzed,which occur during hot stamping process,on the load-carrying capacity and failure mode of hot stamped beams.A damage-coupled pre-forming constitutive model was proposed,in wh...The effects of forming damage are analyzed,which occur during hot stamping process,on the load-carrying capacity and failure mode of hot stamped beams.A damage-coupled pre-forming constitutive model was proposed,in which the damage during hot stamping process was introduced into the service response.The constitutive model was applied into the three-point bending simulation of a hot stamped beam,and then the influences of forming damage on the load-carrying capacity and cracks propagation were investigated.The results show that the forming damage reduces the maximum load capacity of the hot stamped beam by 7.5%.It also causes the crack to occur earlier and promotes crack to propagate along the radial direction of the punch.展开更多
基金Supported by the National Natural Science Foundation of China(5137520151775227)。
文摘The effects of forming damage are analyzed,which occur during hot stamping process,on the load-carrying capacity and failure mode of hot stamped beams.A damage-coupled pre-forming constitutive model was proposed,in which the damage during hot stamping process was introduced into the service response.The constitutive model was applied into the three-point bending simulation of a hot stamped beam,and then the influences of forming damage on the load-carrying capacity and cracks propagation were investigated.The results show that the forming damage reduces the maximum load capacity of the hot stamped beam by 7.5%.It also causes the crack to occur earlier and promotes crack to propagate along the radial direction of the punch.