In the present study,the mechanical properties of polyvinyl alcohol(PVA)-basalt hybrid fiber reinforced engineered cementitious composites(ECC)after exposure to elevated temperatures were experimentally investigated.F...In the present study,the mechanical properties of polyvinyl alcohol(PVA)-basalt hybrid fiber reinforced engineered cementitious composites(ECC)after exposure to elevated temperatures were experimentally investigated.Five temperatures of 20,50,100,200 and 400℃ were set to evaluate the residual compressive,tensile and flexural behaviors of hybrid and mono fiber ECC.It was shown that partial replacement of PVA fibers with basalt fibers endowed ECC with improved residual compressive toughness,compared to brittle failure of mono fiber ECC heated to 400℃.The tension tests indicated that the presence of basalt fibers benefited the tensile strength up to 200℃,and delayed the sharp reduction of strength to 400℃.Under flexural load,the peak deflections corresponding to flexural strengths of hybrid fiber ECC were found to be less vulnerable ranging from 20 to 100℃.Further,the scanning electron microscopy(SEM)results uncovered that the rupture of basalt fiber at moderate temperature and its pullout mechanism at high temperature was responsible for the mechanical evolution of hybrid fiber ECC.This work develops a better understanding of elevated temperature and basalt fiber impact on the residual mechanical properties and further provides guideline for tailoring ECC for improved fire resistance.展开更多
A novel engineered cementitious composite(ECC) was prepared with the complex binder of Portland cement and asphalt emulsion.By adjusting the amount of asphalt emulsion,different mixture proportions were adopted in exp...A novel engineered cementitious composite(ECC) was prepared with the complex binder of Portland cement and asphalt emulsion.By adjusting the amount of asphalt emulsion,different mixture proportions were adopted in experiments,including four-point bending test,compressive test,and scanning electric microscopy(SEM).The SEM observation was conducted to evaluate the contribution of polyvinyl alcohol(PVA) fiber and asphalt emulsion to the composite toughening mechanism.The tests results show that the most remarkable deflection-hardening behavior and saturated multiple cracking are achieved when the content of asphalt emulsion is 10%.However,excessive content of asphalt emulsion causes severe damages on the deformation behavior as well as loss in compressive strength of the mixture.SEM observation indicates that the influence of asphalt emulsion on the fiber/matrix interfacial property changes the dominant fiber failure type from rupture into pull-out mode,and thus causes beneficial effects for strain-hardening behavior.展开更多
基金Project(51808545)supported by the National Natural Science Foundation of ChinaProject(8184083)supported by the Beijing Natural Science Foundation,ChinaProject(2021YQLJ05)supported by the Fundamental Research Funds for the Central Universities,China。
文摘In the present study,the mechanical properties of polyvinyl alcohol(PVA)-basalt hybrid fiber reinforced engineered cementitious composites(ECC)after exposure to elevated temperatures were experimentally investigated.Five temperatures of 20,50,100,200 and 400℃ were set to evaluate the residual compressive,tensile and flexural behaviors of hybrid and mono fiber ECC.It was shown that partial replacement of PVA fibers with basalt fibers endowed ECC with improved residual compressive toughness,compared to brittle failure of mono fiber ECC heated to 400℃.The tension tests indicated that the presence of basalt fibers benefited the tensile strength up to 200℃,and delayed the sharp reduction of strength to 400℃.Under flexural load,the peak deflections corresponding to flexural strengths of hybrid fiber ECC were found to be less vulnerable ranging from 20 to 100℃.Further,the scanning electron microscopy(SEM)results uncovered that the rupture of basalt fiber at moderate temperature and its pullout mechanism at high temperature was responsible for the mechanical evolution of hybrid fiber ECC.This work develops a better understanding of elevated temperature and basalt fiber impact on the residual mechanical properties and further provides guideline for tailoring ECC for improved fire resistance.
基金Project(2011BAE27B04)supported by the National Key Technology R&D Program of ChinaProjects(CHD2011TD003,CHD2011ZD017)supported by the Special Fund for Basic Scientific Research of Central Colleges in Chang’an University,China
文摘A novel engineered cementitious composite(ECC) was prepared with the complex binder of Portland cement and asphalt emulsion.By adjusting the amount of asphalt emulsion,different mixture proportions were adopted in experiments,including four-point bending test,compressive test,and scanning electric microscopy(SEM).The SEM observation was conducted to evaluate the contribution of polyvinyl alcohol(PVA) fiber and asphalt emulsion to the composite toughening mechanism.The tests results show that the most remarkable deflection-hardening behavior and saturated multiple cracking are achieved when the content of asphalt emulsion is 10%.However,excessive content of asphalt emulsion causes severe damages on the deformation behavior as well as loss in compressive strength of the mixture.SEM observation indicates that the influence of asphalt emulsion on the fiber/matrix interfacial property changes the dominant fiber failure type from rupture into pull-out mode,and thus causes beneficial effects for strain-hardening behavior.