Pt and Ir coatings were produced by double glow plasma technology on the surface of Ti alloy substrates. The chemical compositions of the coatings were determined by X-ray diffraction and X-ray photoelectron spectrosc...Pt and Ir coatings were produced by double glow plasma technology on the surface of Ti alloy substrates. The chemical compositions of the coatings were determined by X-ray diffraction and X-ray photoelectron spectroscopy. The microstructure and morphology of the coatings were observed by scanning electron microscopy. The hardness and elastic modulus of the coatings were estimated by nanoindentation. The measurements of adhesive forces of the coatings were performed with scratch tester. The results indicated that the Pt and Ir coatings displayed the preferred (220) orientation due to the initial nuclei with preferred growth on the surface of the substrates. The interface between the Pt coating and substrate exhibited no evidence of delamination. The Ir coating was composed of irregular columnar grains with many nanovoids at the interface between the coating and substrate. The mean values of hardness for Pt and Ir coatings were 0.9 GPa and 9 GPa, respectively. The elastic modulus of Pt and Ir coatings were 178 GPa and 339 GPa, respectively. The adhesive forces of the Pt and Ir coatings were about 66.4 N and 55 N, respectively. The Pt and Ir coatings adhered well to the Ti alloy substrates.展开更多
The cooperative effect of laser surface texturing(LST) and double glow plasma surface alloying on tribological performance of lubricated sliding contacts was investigated.A Nd:YAG laser was used to generate microdimpl...The cooperative effect of laser surface texturing(LST) and double glow plasma surface alloying on tribological performance of lubricated sliding contacts was investigated.A Nd:YAG laser was used to generate microdimples on steel surfaces. Dimples with the diameter of 150μm and the depth of 30-35μm distributed circumferentially on the disc surface.The alloying element Cr was sputtered to the laser texturing steel surface by double glow plasma technique.A deep diffusion layer with a thickness of 30μm and a high hardness of HV900 was formed in this alloy.Tribological experiments of three types of samples(smooth,texturing and texturing+alloying) were conducted with a ring-on-disc tribometer to simulate the face seal.It is found that,in comparison with smooth steel surfaces,the laser texturing samples significantly reduce the friction coefficient.Moreover,the lower wear rate of the sample treated with the two surface techniques is observed.展开更多
基金supported by the National Natural Science Foundation of China(50872055/E020703)Funding for Outstanding Doctoral Dissertation in NUAA(BCXJ1109)the Funding of Jiangsu Innovation Program for Graduate Education(CXLX11_0207)
文摘Pt and Ir coatings were produced by double glow plasma technology on the surface of Ti alloy substrates. The chemical compositions of the coatings were determined by X-ray diffraction and X-ray photoelectron spectroscopy. The microstructure and morphology of the coatings were observed by scanning electron microscopy. The hardness and elastic modulus of the coatings were estimated by nanoindentation. The measurements of adhesive forces of the coatings were performed with scratch tester. The results indicated that the Pt and Ir coatings displayed the preferred (220) orientation due to the initial nuclei with preferred growth on the surface of the substrates. The interface between the Pt coating and substrate exhibited no evidence of delamination. The Ir coating was composed of irregular columnar grains with many nanovoids at the interface between the coating and substrate. The mean values of hardness for Pt and Ir coatings were 0.9 GPa and 9 GPa, respectively. The elastic modulus of Pt and Ir coatings were 178 GPa and 339 GPa, respectively. The adhesive forces of the Pt and Ir coatings were about 66.4 N and 55 N, respectively. The Pt and Ir coatings adhered well to the Ti alloy substrates.
基金Project(2007046) supported by High Technology Research Project of Jiangsu Province,China
文摘The cooperative effect of laser surface texturing(LST) and double glow plasma surface alloying on tribological performance of lubricated sliding contacts was investigated.A Nd:YAG laser was used to generate microdimples on steel surfaces. Dimples with the diameter of 150μm and the depth of 30-35μm distributed circumferentially on the disc surface.The alloying element Cr was sputtered to the laser texturing steel surface by double glow plasma technique.A deep diffusion layer with a thickness of 30μm and a high hardness of HV900 was formed in this alloy.Tribological experiments of three types of samples(smooth,texturing and texturing+alloying) were conducted with a ring-on-disc tribometer to simulate the face seal.It is found that,in comparison with smooth steel surfaces,the laser texturing samples significantly reduce the friction coefficient.Moreover,the lower wear rate of the sample treated with the two surface techniques is observed.