Wood nondestructive testing （NDT） is one of the high efficient methods in utilizing wood. This paper explained the principle of log defect testing by using stress wave, and analyzed the effects of sensor quantity on...Wood nondestructive testing （NDT） is one of the high efficient methods in utilizing wood. This paper explained the principle of log defect testing by using stress wave, and analyzed the effects of sensor quantity on defect testing results by using stress wave in terms of image fitting degree and error rate. The results showed that for logs with diameter ranging from 20 to 40 cm, at least 12 sensors were needed to meet the requirement which ensure a high testing accuracy of roughly 90% of fitness with 0.1 of error rate. And 10 sensors were recommended to judge the possible locations of defects and 6 sensors were sufficient to decide whether there were defects or not.展开更多
A differential excitation probe based on eddy current testing technology was designed. Sheet specimens of Q 235 steel with prefabricated micro-cracks of different widths and of aluminum with prefabricated micro-cracks...A differential excitation probe based on eddy current testing technology was designed. Sheet specimens of Q 235 steel with prefabricated micro-cracks of different widths and of aluminum with prefabricated micro-cracks of different depths were detected through the designed detection system. The characteristics of micro-cracks can be clearly showed after signals processing through the short-time Fourier transform（ STFT）. By changing the parameter and its value in detecting process,the factors including the excitation frequency and amplitude,the lift-off effect and the scanning direction were discussed,respectively. The results showed that the differential excitation probe was insensitive to dimension and surface state of the tested specimen,while it had a high degree of recognition for micro-crack detection. Therefore,when the differential excitation detection technology was used for inspecting micro-crack of turbine blade in aero-engine,and smoothed pseudo Wigner-Ville distribution was used for signal processing,micro-cracks of 0. 3 mm depth and 0. 1 mm width could be identified. The experimental results might be useful for further research on engineering test of turbine blades of aero-engine.展开更多
基金This paper was supported by the project "Devel-opment of Portable NDT Instrument (2002(39-1))" sponsored by Na-tional Forestry Administrative Bureau of China
文摘Wood nondestructive testing （NDT） is one of the high efficient methods in utilizing wood. This paper explained the principle of log defect testing by using stress wave, and analyzed the effects of sensor quantity on defect testing results by using stress wave in terms of image fitting degree and error rate. The results showed that for logs with diameter ranging from 20 to 40 cm, at least 12 sensors were needed to meet the requirement which ensure a high testing accuracy of roughly 90% of fitness with 0.1 of error rate. And 10 sensors were recommended to judge the possible locations of defects and 6 sensors were sufficient to decide whether there were defects or not.
基金Supported by the Ministerial Level Advanced Research Foundation(051317030586)Ph.D.Programs Foundation of the Ministry of Education of China(20121101110018)
文摘A differential excitation probe based on eddy current testing technology was designed. Sheet specimens of Q 235 steel with prefabricated micro-cracks of different widths and of aluminum with prefabricated micro-cracks of different depths were detected through the designed detection system. The characteristics of micro-cracks can be clearly showed after signals processing through the short-time Fourier transform（ STFT）. By changing the parameter and its value in detecting process,the factors including the excitation frequency and amplitude,the lift-off effect and the scanning direction were discussed,respectively. The results showed that the differential excitation probe was insensitive to dimension and surface state of the tested specimen,while it had a high degree of recognition for micro-crack detection. Therefore,when the differential excitation detection technology was used for inspecting micro-crack of turbine blade in aero-engine,and smoothed pseudo Wigner-Ville distribution was used for signal processing,micro-cracks of 0. 3 mm depth and 0. 1 mm width could be identified. The experimental results might be useful for further research on engineering test of turbine blades of aero-engine.