Zinc oxide （ZnO） is one of the most promising and frequently used semiconductor materials. In-doped nanos- tructure ZnO thin films are grown on p-type gallium nitride substrates by employing the simultaneous rf and ...Zinc oxide （ZnO） is one of the most promising and frequently used semiconductor materials. In-doped nanos- tructure ZnO thin films are grown on p-type gallium nitride substrates by employing the simultaneous rf and dc magnetron co-sputtering technique. The effect of In-doping on structural, morphological and electrical properties is studied. The different dopant concentrations are accomplished by varying the direct current power of the In target while keeping the fixed radio frequency power of the ZnO target through the co-sputtering deposition technique by using argon as the sputtering gas at ambient temperature. The structural analysis confirms that all the grown thin films preferentially orientate along the c-axis with the wurtzite hexagonal crystal structure without having any kind of In oxide phases. The presenting Zn, 0 and In elements＇ chemical compositions are identified with EDX mapping analysis of the deposited thin films and the calculated M ratio has been found to decrease with the increasing In power. The surface topographies of the grown thin films are examined with the atomic force microscope technique. The obtained results reveal that the grown film roughness increases with the In power. The Hall measurements ascertain that all the grown films have n-type conductivity and also the other electrical parameters such as resistivity,mobility and carrier concentration are analyzed.展开更多
Copper （Cu）-doped ZrO2 （CZO） films with different Cu content （0 at.%- 8.07 at.%） are successfully deposited on Si （100） substrates by direct current （DC） and radio frequency （RF） magnetron co-sputtering. T...Copper （Cu）-doped ZrO2 （CZO） films with different Cu content （0 at.%- 8.07 at.%） are successfully deposited on Si （100） substrates by direct current （DC） and radio frequency （RF） magnetron co-sputtering. The influences of Cu content on structural, morphological, optical and electrical properties of CZO films are discussed in detail. The CZO films exhibit ZrO2 monocline （1^-11） preferred orientation, which indicates that Cu atoms are doped in ZrO2 host lattice. The crystallite size estimated form x-ray diffraction （XRD） increases by Cu doping, which accords with the result observed from the scanning electron microscope （SEM）. The electrical resistivity decreases from 2.63 Ω·cm to 1.48 Ω·cm with Cu doping content increasing, which indicates that the conductivity of CZO film is improved. However, the visible light transmittances decrease slightly by Cu doping and the optical band gap values decrease from 4.64 eV to 4.48 eV for CZO fihns.展开更多
基金Supported by the RU Top-Down under Grant No 1001/CSS/870019
文摘Zinc oxide （ZnO） is one of the most promising and frequently used semiconductor materials. In-doped nanos- tructure ZnO thin films are grown on p-type gallium nitride substrates by employing the simultaneous rf and dc magnetron co-sputtering technique. The effect of In-doping on structural, morphological and electrical properties is studied. The different dopant concentrations are accomplished by varying the direct current power of the In target while keeping the fixed radio frequency power of the ZnO target through the co-sputtering deposition technique by using argon as the sputtering gas at ambient temperature. The structural analysis confirms that all the grown thin films preferentially orientate along the c-axis with the wurtzite hexagonal crystal structure without having any kind of In oxide phases. The presenting Zn, 0 and In elements＇ chemical compositions are identified with EDX mapping analysis of the deposited thin films and the calculated M ratio has been found to decrease with the increasing In power. The surface topographies of the grown thin films are examined with the atomic force microscope technique. The obtained results reveal that the grown film roughness increases with the In power. The Hall measurements ascertain that all the grown films have n-type conductivity and also the other electrical parameters such as resistivity,mobility and carrier concentration are analyzed.
基金supported by the National Natural Science Foundation of China(Grant Nos.51272224 and 11164031)
文摘Copper （Cu）-doped ZrO2 （CZO） films with different Cu content （0 at.%- 8.07 at.%） are successfully deposited on Si （100） substrates by direct current （DC） and radio frequency （RF） magnetron co-sputtering. The influences of Cu content on structural, morphological, optical and electrical properties of CZO films are discussed in detail. The CZO films exhibit ZrO2 monocline （1^-11） preferred orientation, which indicates that Cu atoms are doped in ZrO2 host lattice. The crystallite size estimated form x-ray diffraction （XRD） increases by Cu doping, which accords with the result observed from the scanning electron microscope （SEM）. The electrical resistivity decreases from 2.63 Ω·cm to 1.48 Ω·cm with Cu doping content increasing, which indicates that the conductivity of CZO film is improved. However, the visible light transmittances decrease slightly by Cu doping and the optical band gap values decrease from 4.64 eV to 4.48 eV for CZO fihns.