Formation of entrance and exit defects in coarse pitch orbital drilling(CPOD)of carbon fiber reinforced plastic(CFRP)plates was investigated.Deep observation on entrance and exit morphology shows tear and burr are typ...Formation of entrance and exit defects in coarse pitch orbital drilling(CPOD)of carbon fiber reinforced plastic(CFRP)plates was investigated.Deep observation on entrance and exit morphology shows tear and burr are typical defects.Meanwhile,tear is more obvious than burr,and more entrance tears emerge than exit tears.As one of the major causes of entrance and exit defects in CPOD,cutting forces were substaintially studied by contrast experiments.Then,the effect of cutting parameters on entrance and exit tear was qualitatively analyzed through a single factor test.Experiment results indicate that the variation of rotation speed has little influence on entrance and exit tear.Increasing tangential feed per tooth can enlarge entrance tear,but bring little effect on exit tear.By increasing axial feed pitch,the hole entrance and exit show severe tear.When revolution radius grows bigger and bigger,entrance and exit tear firstly decreases,and then increases.Finally,the models of tear and delamination during CPOD of CFRP were established,the formation mechanisms of entrance and exit defects were revealed,and the control strategies were accordingly put forward.展开更多
To study the response characteristics of the carbon fiber fabric reinforced composites under impact loading, one dimensional strain impact test, multi gauge technique and Lagrange analysis method are used. The decay...To study the response characteristics of the carbon fiber fabric reinforced composites under impact loading, one dimensional strain impact test, multi gauge technique and Lagrange analysis method are used. The decaying rule of the stress σ , strain ε , strain rate ε · and density ρ with time and space is obtained. By the theory of dynamics, the impact response characteristics of the material is analyzed and discussed.展开更多
Damage caused due to low-velocity impacts in composites leads to substantial deterioration in their residual strength and eventually provokes structural failure.This work presents an experimental investigation on the ...Damage caused due to low-velocity impacts in composites leads to substantial deterioration in their residual strength and eventually provokes structural failure.This work presents an experimental investigation on the effects of different patch and parent laminate stacking sequences on the enhancement of impact strength of Carbon Fiber Reinforced Polymers(CFRP)composites by utilising the adhesively bonded external patch repair technique.Damage evolution study is also performed with the aid of Acoustic Emission(AE).Two different quasi-isotropic configurations were selected for the parent laminate,viz.,[45°/45°/0°/0°]s and[45°/0°/45°/0°]s.Quasi Static Indentation(QSI)test was performed on both the pristine laminates,and damage areas were detected by using the C-scan inspection technique.Damaged laminates were repaired by using a single-sided patch of two different configurations,viz.,[45°/45°/45°/45°]and[45°/0°/0°/45°],and employing a circular plug to fill the damaged hole.Four different combinations of repaired laminates with two configurations of each parent and patch laminate were produced,which were further subjected to the QSI test.The results reveal the effectiveness of the repair method,as all the repaired laminates show higher impact resistance compared to the respective pristine laminates.Patches of[45°/0°/0°/45°]configuration when repaired by taking[45°/45°/0°/0°]s and[45°/0°/45°/0°]s as parents exhibited 68%and 73%higher peak loads,respectively,than the respective pristine laminates.Furthermore,parent and patch of configuration[45°/0°/45°/0°]s and[45°/0°/0°/45°],respectively,attain the highest peak load,whereas[45°/45°/0°/0°]s and[45°/45°/45°/45°]combinations possess the most gradual decrease in the load.展开更多
为了研究20 W纳秒激光对碳纤维复合材料(CFRP)烧蚀的工艺质量,采用单因素实验方法及光切法进行了理论分析和实验验证,得到了扫描速率、峰值功率、离焦量对材料表面加工质量的影响规律,并对0.5 mm CFRP材料板进行了烧蚀实验。结果表明,...为了研究20 W纳秒激光对碳纤维复合材料(CFRP)烧蚀的工艺质量,采用单因素实验方法及光切法进行了理论分析和实验验证,得到了扫描速率、峰值功率、离焦量对材料表面加工质量的影响规律,并对0.5 mm CFRP材料板进行了烧蚀实验。结果表明,调整激光器的离焦量,让激光的焦点与材料平面在同一高度,可使扫描线宽最小,减少了材料烧蚀的热影响区,提高了激光能量利用率;设定激光扫描速率为220 mm/s和峰值功率为10 W,可得到大小为3.50μm的CFRP最小表面粗糙度平均值,其中粗糙度数据稳定性样本方差最佳,约为0.133μm 2,在此条件下可得到良好的加工表现。此研究为脉冲激光加工CFRP材料工艺研究提供一定参考,并为脉冲激光加工复合材料工艺应用打下了一定的实践基础。展开更多
Carbon fiber-reinforced polymer(CFRP)is widely used in aerospace applications.This kind of material may face the threat of high-velocity impact in the process of dedicated service,and the relevant research mainly cons...Carbon fiber-reinforced polymer(CFRP)is widely used in aerospace applications.This kind of material may face the threat of high-velocity impact in the process of dedicated service,and the relevant research mainly considers the impact resistance of the material,and lacks the high-velocity impact damage monitoring research of CFRP.To solve this problem,a real high-velocity impact damage experiment and structural health monitoring(SHM)method of CFRP plate based on piezoelectric guided wave is proposed.The results show that CFRP has obvious perforation damage and fiber breakage when high-velocity impact occurs.It is also proved that guided wave SHM technology can be effectively used in the monitoring of such damage,and the damage can be reflected by quantifying the signal changes and damage index(DI).It provides a reference for further research on guided wave structure monitoring of high/hyper-velocity impact damage of CFRP.展开更多
基金supported in part by the Major Project of the Ministry of Science and Technology of China(No.2012ZX04003-031)the Innovation Project of Jiangsu Province(No.2016-05)
文摘Formation of entrance and exit defects in coarse pitch orbital drilling(CPOD)of carbon fiber reinforced plastic(CFRP)plates was investigated.Deep observation on entrance and exit morphology shows tear and burr are typical defects.Meanwhile,tear is more obvious than burr,and more entrance tears emerge than exit tears.As one of the major causes of entrance and exit defects in CPOD,cutting forces were substaintially studied by contrast experiments.Then,the effect of cutting parameters on entrance and exit tear was qualitatively analyzed through a single factor test.Experiment results indicate that the variation of rotation speed has little influence on entrance and exit tear.Increasing tangential feed per tooth can enlarge entrance tear,but bring little effect on exit tear.By increasing axial feed pitch,the hole entrance and exit show severe tear.When revolution radius grows bigger and bigger,entrance and exit tear firstly decreases,and then increases.Finally,the models of tear and delamination during CPOD of CFRP were established,the formation mechanisms of entrance and exit defects were revealed,and the control strategies were accordingly put forward.
文摘To study the response characteristics of the carbon fiber fabric reinforced composites under impact loading, one dimensional strain impact test, multi gauge technique and Lagrange analysis method are used. The decaying rule of the stress σ , strain ε , strain rate ε · and density ρ with time and space is obtained. By the theory of dynamics, the impact response characteristics of the material is analyzed and discussed.
基金the financial support by the Council of Scientific&Industrial Research(CSIR)-Research Scheme,India(22/0809/2019-EMR-II)。
文摘Damage caused due to low-velocity impacts in composites leads to substantial deterioration in their residual strength and eventually provokes structural failure.This work presents an experimental investigation on the effects of different patch and parent laminate stacking sequences on the enhancement of impact strength of Carbon Fiber Reinforced Polymers(CFRP)composites by utilising the adhesively bonded external patch repair technique.Damage evolution study is also performed with the aid of Acoustic Emission(AE).Two different quasi-isotropic configurations were selected for the parent laminate,viz.,[45°/45°/0°/0°]s and[45°/0°/45°/0°]s.Quasi Static Indentation(QSI)test was performed on both the pristine laminates,and damage areas were detected by using the C-scan inspection technique.Damaged laminates were repaired by using a single-sided patch of two different configurations,viz.,[45°/45°/45°/45°]and[45°/0°/0°/45°],and employing a circular plug to fill the damaged hole.Four different combinations of repaired laminates with two configurations of each parent and patch laminate were produced,which were further subjected to the QSI test.The results reveal the effectiveness of the repair method,as all the repaired laminates show higher impact resistance compared to the respective pristine laminates.Patches of[45°/0°/0°/45°]configuration when repaired by taking[45°/45°/0°/0°]s and[45°/0°/45°/0°]s as parents exhibited 68%and 73%higher peak loads,respectively,than the respective pristine laminates.Furthermore,parent and patch of configuration[45°/0°/45°/0°]s and[45°/0°/0°/45°],respectively,attain the highest peak load,whereas[45°/45°/0°/0°]s and[45°/45°/45°/45°]combinations possess the most gradual decrease in the load.
基金supported by the National Natural Science Foundation of China(Nos.51921003,52275153)the Fundamental Research Funds for the Central Universities(No.NI2023001)+2 种基金the Research Fund of State Key Laboratory of Mechanics and Control for Aero-space Structures(No.MCAS-I-0423G01)the Fund of Pro-spective Layout of Scientific Research for Nanjing University of Aeronautics and Astronauticsthe Priority Academic Program Development of Jiangsu Higher Education Institu-tions of China.
文摘Carbon fiber-reinforced polymer(CFRP)is widely used in aerospace applications.This kind of material may face the threat of high-velocity impact in the process of dedicated service,and the relevant research mainly considers the impact resistance of the material,and lacks the high-velocity impact damage monitoring research of CFRP.To solve this problem,a real high-velocity impact damage experiment and structural health monitoring(SHM)method of CFRP plate based on piezoelectric guided wave is proposed.The results show that CFRP has obvious perforation damage and fiber breakage when high-velocity impact occurs.It is also proved that guided wave SHM technology can be effectively used in the monitoring of such damage,and the damage can be reflected by quantifying the signal changes and damage index(DI).It provides a reference for further research on guided wave structure monitoring of high/hyper-velocity impact damage of CFRP.