Ni/n-SiO2 composite coating was electrodeposited by brush-plating with pulse-reverse current（RC）. The morphology, hardness, and tribological properties of the coating were investigated and compared with those of Ni ...Ni/n-SiO2 composite coating was electrodeposited by brush-plating with pulse-reverse current（RC）. The morphology, hardness, and tribological properties of the coating were investigated and compared with those of Ni and composite coatings electrodeposited with direct current（DC）. The results indicate that Ni/n-SiO2 composite coating electrodeposited by RC, because of RC and the nano powders, has denser coating, finer crystal grains, higher hardness（HV650.0, nearly 1.5 times higher than that of Ni coating electrodeposited by DC） and lower friction coefficient（nearly 0.62）, as a result, in the wearing experiment, the Ni/n-SiO2 composite coating electrodeposited by RC has the least worn loss. So this kind of coating has better wear resistance. And RC electro brush-plating can be used as a new technology of brush-plating in the area of wear resistance.展开更多
An automatic brush-plating system was developed for component remanufacturing. With this system, Ni/nano-alumina composite coatings from an electrolyte containing 20g/L nano-alumina particles were prepared. Microstr...An automatic brush-plating system was developed for component remanufacturing. With this system, Ni/nano-alumina composite coatings from an electrolyte containing 20g/L nano-alumina particles were prepared. Microstructure, surface morphology, microhardness and wear resistance of automatically plated coatings and manually plated coatings were investigated comparatively. The results show that the automatically plated coatings are relatively dense and uniform and have lower friction coefficient of 0.089 under lubricant condition, when compared with manually plated coatings with friction coefficient of 0.14.展开更多
文摘Ni/n-SiO2 composite coating was electrodeposited by brush-plating with pulse-reverse current（RC）. The morphology, hardness, and tribological properties of the coating were investigated and compared with those of Ni and composite coatings electrodeposited with direct current（DC）. The results indicate that Ni/n-SiO2 composite coating electrodeposited by RC, because of RC and the nano powders, has denser coating, finer crystal grains, higher hardness（HV650.0, nearly 1.5 times higher than that of Ni coating electrodeposited by DC） and lower friction coefficient（nearly 0.62）, as a result, in the wearing experiment, the Ni/n-SiO2 composite coating electrodeposited by RC has the least worn loss. So this kind of coating has better wear resistance. And RC electro brush-plating can be used as a new technology of brush-plating in the area of wear resistance.
文摘An automatic brush-plating system was developed for component remanufacturing. With this system, Ni/nano-alumina composite coatings from an electrolyte containing 20g/L nano-alumina particles were prepared. Microstructure, surface morphology, microhardness and wear resistance of automatically plated coatings and manually plated coatings were investigated comparatively. The results show that the automatically plated coatings are relatively dense and uniform and have lower friction coefficient of 0.089 under lubricant condition, when compared with manually plated coatings with friction coefficient of 0.14.
