A large amount of acid-leaching residue is produced during the conventional Zn hydrometallurgy process,and this residue has a large concentration of a variety of valuable metals.The purpose of this study was to evalua...A large amount of acid-leaching residue is produced during the conventional Zn hydrometallurgy process,and this residue has a large concentration of a variety of valuable metals.The purpose of this study was to evaluate the ability of a procedure that entails the use of sulfation roasting,water leaching,and chlorination leaching(blowing oxygen technique)to recover Pb and Ag,followed by cooling crystallization and the replacement of Ag with lead sheet,to realize the full recovery of all valuable metals from zinc acid-leaching residue;consequently,good results were achieved.The best results were obtained under the following conditions:a sulfuric acid at 70%of the raw material quality,roasting temperature of 300°C and roasting time of 2 h,followed by the process of leaching the roasted residue for 1 h by applying a water-to-solid ratio of 5꞉1 at room temperature.The recovery rates of Zn and Fe were 98.69%and 92.36%,respectively.The main parameters of the chlorine salt leaching system were as follows:Cl−concentration of 300 g/L,Fe3+concentration of 25 g/L,acid concentration of 2 mol/L,liquid-to-solid ratio of 9 mL:1 g,temperature of 90℃,and leaching time of 0.5 h;this leaching process was followed by filtration separation.These conditions resulted in high extents of leaching for Pb and Ag(i.e.,98.87%and 96.74%,respectively).Finally,the kinetics of the process of Ag leaching using Cl−ions in an oxygen-rich medium was investigated.It was found that the leaching process was controlled by the diffusion of the product layers,and the activation energy was 19.82 kJ/mol.展开更多
Alkali-leaching and acid-leaching were proposed for the dephosphorization of Changde iron ore, which contains an average of 1.12% for phosphorus content. Sodium hydroxide, sulfuriced, hydrochloric and nitric acids wer...Alkali-leaching and acid-leaching were proposed for the dephosphorization of Changde iron ore, which contains an average of 1.12% for phosphorus content. Sodium hydroxide, sulfuriced, hydrochloric and nitric acids were used for the preparation of leach solutions. The results show that phosphorus occurring as apatite phase could be removed by alkali-leaching, but those occurring in the iron phase could not. Sulfuric acid is the most effective among the three kinds of acid. 91.61% phosphorus removal was attained with 1% sulfuric acid after leaching for 20 rain at room temperature. Iron loss during acid-leaching can be negligible, which was less than 0.25%.The pH value of solution after leaching with1% sulfuric acid was about 0.86, which means acid would not be exhausted during the process and it could be recycled, and the recycle of sulfuric acid solution would make the dephosphorization process more economical.展开更多
基金Projects(51804136,52064021,52074136,51564021,52064022)supported by the National Natural Science Foundation of ChinaProjects(2019T120625,2019M652276)supported by the China Postdoctoral Science Foundation+2 种基金Project(20202ACB213002)supported by the Jiangxi Province Science Fund for Distinguished Young Scholars,ChinaProject(2019KY09)supported by the Program for Excellent Young Talents,JXUST Young Jinggang Scholars of Jiangxi Province,Merit-based Postdoctoral Research in Jiangxi Province,ChinaProjects supported by the Distinguished Professor Program of Jinggang Scholars,Chinain Institutions of Higher Learning,Jiangxi Province,China。
文摘A large amount of acid-leaching residue is produced during the conventional Zn hydrometallurgy process,and this residue has a large concentration of a variety of valuable metals.The purpose of this study was to evaluate the ability of a procedure that entails the use of sulfation roasting,water leaching,and chlorination leaching(blowing oxygen technique)to recover Pb and Ag,followed by cooling crystallization and the replacement of Ag with lead sheet,to realize the full recovery of all valuable metals from zinc acid-leaching residue;consequently,good results were achieved.The best results were obtained under the following conditions:a sulfuric acid at 70%of the raw material quality,roasting temperature of 300°C and roasting time of 2 h,followed by the process of leaching the roasted residue for 1 h by applying a water-to-solid ratio of 5꞉1 at room temperature.The recovery rates of Zn and Fe were 98.69%and 92.36%,respectively.The main parameters of the chlorine salt leaching system were as follows:Cl−concentration of 300 g/L,Fe3+concentration of 25 g/L,acid concentration of 2 mol/L,liquid-to-solid ratio of 9 mL:1 g,temperature of 90℃,and leaching time of 0.5 h;this leaching process was followed by filtration separation.These conditions resulted in high extents of leaching for Pb and Ag(i.e.,98.87%and 96.74%,respectively).Finally,the kinetics of the process of Ag leaching using Cl−ions in an oxygen-rich medium was investigated.It was found that the leaching process was controlled by the diffusion of the product layers,and the activation energy was 19.82 kJ/mol.
基金Project (50321402) supported by the National Natural Science Foundation of China project(2004CB619204) supported by Major State Basic Research Development Program of China
文摘Alkali-leaching and acid-leaching were proposed for the dephosphorization of Changde iron ore, which contains an average of 1.12% for phosphorus content. Sodium hydroxide, sulfuriced, hydrochloric and nitric acids were used for the preparation of leach solutions. The results show that phosphorus occurring as apatite phase could be removed by alkali-leaching, but those occurring in the iron phase could not. Sulfuric acid is the most effective among the three kinds of acid. 91.61% phosphorus removal was attained with 1% sulfuric acid after leaching for 20 rain at room temperature. Iron loss during acid-leaching can be negligible, which was less than 0.25%.The pH value of solution after leaching with1% sulfuric acid was about 0.86, which means acid would not be exhausted during the process and it could be recycled, and the recycle of sulfuric acid solution would make the dephosphorization process more economical.