将纤维素溶解在ZnCl_2溶液中,以SnCl_4为催化剂,微波下使纤维素降解成5-羟甲基糠醛(5-HMF)。实验考察了微波功率、纤维素的质量、ZnCl_2溶液浓度、反应时间及催化剂与纤维素物质的量比等对5-HMF产率的影响。结果表明,以SnCl_4为催化剂,...将纤维素溶解在ZnCl_2溶液中,以SnCl_4为催化剂,微波下使纤维素降解成5-羟甲基糠醛(5-HMF)。实验考察了微波功率、纤维素的质量、ZnCl_2溶液浓度、反应时间及催化剂与纤维素物质的量比等对5-HMF产率的影响。结果表明,以SnCl_4为催化剂,在优化条件:1.0 g纤维素溶解在100 m L 70%ZnCl_2溶液中,微波功率为420 W,降解反应9 min,SnCl_4与纤维素物质的量比2∶1下,5-HMF的产率达到39.4%。展开更多
This work presents a method to solve the weak solubility of zinc chloride(ZnCl_2) in the ethanol by adding some reasonable water into an ethanol electrolyte containing ZnCl_2 and myristic acid(CH_3(CH_2)_(12)COOH).A r...This work presents a method to solve the weak solubility of zinc chloride(ZnCl_2) in the ethanol by adding some reasonable water into an ethanol electrolyte containing ZnCl_2 and myristic acid(CH_3(CH_2)_(12)COOH).A rapid one-step electrodeposition process was developed to fabricate anodic(2.5 min) and cathodic(40 s) superhydrophobic surfaces of copper substrate(contact angle more than 150°) in an aqueous ethanol electrolyte.Morphology,composition,chemical structure and superhydrophobicity of these superhydrophobic surfaces were investigated by SEM,FTIR,XRD,and contact angle measurement,respectively.The results indicate that water ratio of the electrolyte can reduce the required deposition time,superhydrophobic surface needs over 30 min with anhydrous electrolyte,while it needs only 2.5 min with electrolyte including 10 mL water,and the maximum contact angle of anodic surface is 166° and that of the cathodic surface is 168°.Two copper electrode surfaces have different reactions in the process of electrodeposition time,and the anodic copper surface covers copper myristate(Cu[CH_3(CH_2)_(12)COO]_2) and cupric chloride(CuCl);while,zinc myristate(Zn[CH_3(CH_2)_(12)COO]_2) and pure zinc(Zn) appear on the cathodic surface.展开更多
文摘将纤维素溶解在ZnCl_2溶液中,以SnCl_4为催化剂,微波下使纤维素降解成5-羟甲基糠醛(5-HMF)。实验考察了微波功率、纤维素的质量、ZnCl_2溶液浓度、反应时间及催化剂与纤维素物质的量比等对5-HMF产率的影响。结果表明,以SnCl_4为催化剂,在优化条件:1.0 g纤维素溶解在100 m L 70%ZnCl_2溶液中,微波功率为420 W,降解反应9 min,SnCl_4与纤维素物质的量比2∶1下,5-HMF的产率达到39.4%。
基金Projects(11304243,11102164)supported by the National Natural Science Foundation of ChinaProject(2014JQ1039)supported by the Natural Science Foundation of Shannxi Province,China+3 种基金Project(12JK0966)supported by the Shaanxi Provincial Education Department,ChinaProject(2013QDJ037)supported by the Xi’an University of Science and Technology Dr Scientific Research Fund,ChinaProject(3102016ZY027)supported by the Fundamental Research Funds for the Central Universities of ChinaProject(13GH014602)supported by the Program of New Staff and Research Area Project of NPU,China
文摘This work presents a method to solve the weak solubility of zinc chloride(ZnCl_2) in the ethanol by adding some reasonable water into an ethanol electrolyte containing ZnCl_2 and myristic acid(CH_3(CH_2)_(12)COOH).A rapid one-step electrodeposition process was developed to fabricate anodic(2.5 min) and cathodic(40 s) superhydrophobic surfaces of copper substrate(contact angle more than 150°) in an aqueous ethanol electrolyte.Morphology,composition,chemical structure and superhydrophobicity of these superhydrophobic surfaces were investigated by SEM,FTIR,XRD,and contact angle measurement,respectively.The results indicate that water ratio of the electrolyte can reduce the required deposition time,superhydrophobic surface needs over 30 min with anhydrous electrolyte,while it needs only 2.5 min with electrolyte including 10 mL water,and the maximum contact angle of anodic surface is 166° and that of the cathodic surface is 168°.Two copper electrode surfaces have different reactions in the process of electrodeposition time,and the anodic copper surface covers copper myristate(Cu[CH_3(CH_2)_(12)COO]_2) and cupric chloride(CuCl);while,zinc myristate(Zn[CH_3(CH_2)_(12)COO]_2) and pure zinc(Zn) appear on the cathodic surface.