采用熔盐顶部籽晶法从K 2 Mo 3 O 10-B 2 O 3助熔剂中生长出尺寸为20 mm的优质GdAl 3(BO 3)4(简称GAB)和Nd^3+激活的自变频激光晶体。确定了GAB晶体的透光波长范围、折射率和倍频系数随波长的变化,结果表明其在整个透光范围内均可实现...采用熔盐顶部籽晶法从K 2 Mo 3 O 10-B 2 O 3助熔剂中生长出尺寸为20 mm的优质GdAl 3(BO 3)4(简称GAB)和Nd^3+激活的自变频激光晶体。确定了GAB晶体的透光波长范围、折射率和倍频系数随波长的变化,结果表明其在整个透光范围内均可实现相位匹配。测定了Nd^3+∶GAB晶体在室温下的偏振吸收、荧光光谱和荧光寿命,进行了光谱计算,测试了晶体的自变频激光性能,实现了紫外-可见光-红外-中红外多波段激光输出。展开更多
Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re...Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.展开更多
文摘采用熔盐顶部籽晶法从K 2 Mo 3 O 10-B 2 O 3助熔剂中生长出尺寸为20 mm的优质GdAl 3(BO 3)4(简称GAB)和Nd^3+激活的自变频激光晶体。确定了GAB晶体的透光波长范围、折射率和倍频系数随波长的变化,结果表明其在整个透光范围内均可实现相位匹配。测定了Nd^3+∶GAB晶体在室温下的偏振吸收、荧光光谱和荧光寿命,进行了光谱计算,测试了晶体的自变频激光性能,实现了紫外-可见光-红外-中红外多波段激光输出。
基金Shanghai Commission of Sciences and Technology(08520513100)Shanghai Municipal Education Commission(J51504,09ZZ196)SIT Research Project on Optical Functional Crystals(TDP2009-03)
文摘Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.