Microarc oxidation is an effective surface treatment for improving certain properties of metals and their alloys.In this paper,TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were prepared on Ti-6Al-4V by microarc...Microarc oxidation is an effective surface treatment for improving certain properties of metals and their alloys.In this paper,TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were prepared on Ti-6Al-4V by microarc oxidation.Thecoatings exhibited good corrosion resistance and antimicrobial properties.X-ray diffraction(XRD),scanning electronmicroscopy(SEM),and 3D laser confocal were used to characterize the coatings.The properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were analyzed,including microstructure,surface roughness,corrosion resistance,andantimicrobial properties.The electrochemical results showed that the coatings prepared by microarc oxidation hadenhanced corrosion resistance compared to the substrate.The antibacterial properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coating against Pseudomonas aeruginosa were evaluated by fluorescence microscopy and plate counting.The antibacterial rate of TiO_(2)/Cu_(2)O@CeO_(2)coating was up to 99.70%.In summary,the TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings prepared by microarc oxidation have a potential application background in the field of marine corrosionprotection and biofouling.展开更多
This experiment obtained different laser energy density(LED) by changing SLM molding process parameters.The surface morphology, surface quality, and microstructure of as-fabricated samples were studied. The effects of...This experiment obtained different laser energy density(LED) by changing SLM molding process parameters.The surface morphology, surface quality, and microstructure of as-fabricated samples were studied. The effects of scanning speed, hatching space, and laser power on surface quality were analyzed, and the optimal LED range for surface quality was determined. The results show that pores and spherical particles appear on the sample’s surface when low LED is applied, while there are lamellar structures on the sides of the samples. Cracks appear on the sample’s surface,and the splash phenomenon increases when a high LED is taken. At the same time, a large amount of unmelted powder adhered to the side of the sample. The surface quality is the best when the LED is 150-170 J/mm^(3). The preferred hatch space is currently 0.05-0.09 mm, the laser power is 200-350 W, and the average surface roughness value is(15.1±3) μm.The average surface hardness reaches HV404±HV3, higher than the forging standard range of HV340-HV395.Increasing the LED within the experiment range can increase the surface hardness, yet an excessively high LED will not further increase the surface hardness. The microstructure is composed of needle-like α’-phases with a length of about 20μm, in a crisscross ‘N’ shape, when the LED is low. The β-phase grain boundary is not obvious, and the secondaryphase volume fraction is high;when the LED is high, the α’-phase of the microstructure is in the form of coarse slats, and the secondary-phase is composed of a small amount of secondary α’-phase, the tertiary α’-phase and the fourth α’-phase disappear, and the volume fraction of the secondary-phase becomes low.展开更多
Ti-6 Al-4 V-Si3 N4 composites were effectively fabricated by spark plasma sintering(SPS) technique. The addition of Si_3 N_4 on Ti-6 AI-4 V was varied from 5% to 15%(wt fraction). The effect of Si_3 N_4 addition on th...Ti-6 Al-4 V-Si3 N4 composites were effectively fabricated by spark plasma sintering(SPS) technique. The addition of Si_3 N_4 on Ti-6 AI-4 V was varied from 5% to 15%(wt fraction). The effect of Si_3 N_4 addition on the densification, microstructure, and microhardness and corrosion behaviour of Ti-6 Al-4 V was investigated.An increase in microhardness value was recorded from 325.46 HV_(0.1) to 585.73 HV_(0.1). X-ray diffraction(XRD) analysis showed that the intensity of diffraction peaks of Si3 N4 phase in the composites increased.The sintered Ti-6 Al-4 V reinforced with Si_3 N_4 compacts revealed the non-existence of intermediate phases, such as TiSi_2(titanium silicide) which was expected. SEM analysis of the spark plasma sintered composites revealed a and β phase microstructures in Ti-6 Al-4 V with uniform distribution of Si3 N4 particulates in the matrix. The corrosion resistance property of the material was improved by the addition of Si_3 N_4 from 0.986629 mm/year to 0.030547 mm/year.展开更多
基金Projects(41827805,41976044)supported by the National Natural Science Foundation of ChinaProject(ZDYF2021GXJS210)supported by the Hainan Provincial Science and Technology Special Fund,China+2 种基金Project(2021CXLH0005)supported by the Hainan Provincial Joint Project of Sanya Yazhou Bay Science and Technology City,ChinaProject(2021WHZZB2301)supported by the Wenhai Program of the S&T Fund of Shandong Province for Pilot National Laboratory for Marine Science and Technology,ChinaProject(121311KYSB20210005)supported by the Overseas Science and Education Centers of Bureau of International Cooperation Chinese Academy of Sciences。
文摘Microarc oxidation is an effective surface treatment for improving certain properties of metals and their alloys.In this paper,TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were prepared on Ti-6Al-4V by microarc oxidation.Thecoatings exhibited good corrosion resistance and antimicrobial properties.X-ray diffraction(XRD),scanning electronmicroscopy(SEM),and 3D laser confocal were used to characterize the coatings.The properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were analyzed,including microstructure,surface roughness,corrosion resistance,andantimicrobial properties.The electrochemical results showed that the coatings prepared by microarc oxidation hadenhanced corrosion resistance compared to the substrate.The antibacterial properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coating against Pseudomonas aeruginosa were evaluated by fluorescence microscopy and plate counting.The antibacterial rate of TiO_(2)/Cu_(2)O@CeO_(2)coating was up to 99.70%.In summary,the TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings prepared by microarc oxidation have a potential application background in the field of marine corrosionprotection and biofouling.
基金Projects(51975006, 51505006) supported by the National Natural Science Foundation of China。
文摘This experiment obtained different laser energy density(LED) by changing SLM molding process parameters.The surface morphology, surface quality, and microstructure of as-fabricated samples were studied. The effects of scanning speed, hatching space, and laser power on surface quality were analyzed, and the optimal LED range for surface quality was determined. The results show that pores and spherical particles appear on the sample’s surface when low LED is applied, while there are lamellar structures on the sides of the samples. Cracks appear on the sample’s surface,and the splash phenomenon increases when a high LED is taken. At the same time, a large amount of unmelted powder adhered to the side of the sample. The surface quality is the best when the LED is 150-170 J/mm^(3). The preferred hatch space is currently 0.05-0.09 mm, the laser power is 200-350 W, and the average surface roughness value is(15.1±3) μm.The average surface hardness reaches HV404±HV3, higher than the forging standard range of HV340-HV395.Increasing the LED within the experiment range can increase the surface hardness, yet an excessively high LED will not further increase the surface hardness. The microstructure is composed of needle-like α’-phases with a length of about 20μm, in a crisscross ‘N’ shape, when the LED is low. The β-phase grain boundary is not obvious, and the secondaryphase volume fraction is high;when the LED is high, the α’-phase of the microstructure is in the form of coarse slats, and the secondary-phase is composed of a small amount of secondary α’-phase, the tertiary α’-phase and the fourth α’-phase disappear, and the volume fraction of the secondary-phase becomes low.
基金financial support from National Research Foundation(NRF), Pretoria, South Africa
文摘Ti-6 Al-4 V-Si3 N4 composites were effectively fabricated by spark plasma sintering(SPS) technique. The addition of Si_3 N_4 on Ti-6 AI-4 V was varied from 5% to 15%(wt fraction). The effect of Si_3 N_4 addition on the densification, microstructure, and microhardness and corrosion behaviour of Ti-6 Al-4 V was investigated.An increase in microhardness value was recorded from 325.46 HV_(0.1) to 585.73 HV_(0.1). X-ray diffraction(XRD) analysis showed that the intensity of diffraction peaks of Si3 N4 phase in the composites increased.The sintered Ti-6 Al-4 V reinforced with Si_3 N_4 compacts revealed the non-existence of intermediate phases, such as TiSi_2(titanium silicide) which was expected. SEM analysis of the spark plasma sintered composites revealed a and β phase microstructures in Ti-6 Al-4 V with uniform distribution of Si3 N4 particulates in the matrix. The corrosion resistance property of the material was improved by the addition of Si_3 N_4 from 0.986629 mm/year to 0.030547 mm/year.