Eu^(2+) and Mn^(2+) co-activated CaAlSiN_(3) red phosphors were produced using the solid-state reaction tech⁃nique in a N2 environment.Excitation spectra,emission spectra,and diffuse reflection spectra were used to st...Eu^(2+) and Mn^(2+) co-activated CaAlSiN_(3) red phosphors were produced using the solid-state reaction tech⁃nique in a N2 environment.Excitation spectra,emission spectra,and diffuse reflection spectra were used to study the luminescence characteristics,energy gap,and thermal stability in detail.CaAlSiN_(3)∶Eu^(2+) exhibits an extended emission band when stimulated with 450 nm blue light,which is caused by the 4f65d to 4f7 transition of Eu^(2+).Similar⁃ly,CaAlSiN_(3)∶Mn^(2+) displays a wide emission band centered at 628 nm,which results from Mn^(2+)’s transition from 4T1(4G) to 6A1(6S).When the ions of Mn^(2+)were combined into CaAlSiN_(3)∶Eu^(2+),the photoluminescence intensity of Eu^(2+ )was greatly boosted because there was energy transfer and co-emission between Mn^(2+) and Eu^(2+).Beyond that,CaAlSiN_(3)∶Eu^(2+),Mn^(2+) emerges with splendid thermostability and high quantum efficiency,the quenching temperature surpasses 300℃,and the internal quantum efficiency is determined to be around 84.9%.The white LED was pack⁃aged with a combination of CaAlSiN_(3)∶Eu^(2+),Mn^(2+),LuAG∶Ce3+ and a blue chip.At a warm white-light corresponding color temperature(3009 K) with CIE coordinates(0.4223,0.3748),the color rendering index Ra has reached 93.2.CaAlSiN_(3)∶Eu^(2+),Mn^(2+) would have great application potential as a red-emitting phosphor for white LEDs.展开更多
By using an improved Bridgman method,0.3 mol%Tm^(3+)/0.6 mol%Tb^(3+)/y mol%Eu^(3+)(y=0,0.4,0.6,0.8)doped Na_(5)Y_(9)F_(32)single crystals were prepared.The x-ray diffraction,excitation spectra,emission spectra and flu...By using an improved Bridgman method,0.3 mol%Tm^(3+)/0.6 mol%Tb^(3+)/y mol%Eu^(3+)(y=0,0.4,0.6,0.8)doped Na_(5)Y_(9)F_(32)single crystals were prepared.The x-ray diffraction,excitation spectra,emission spectra and fluorescence decay curves were used to explore the crystal structure and optical performance of the obtained samples.When excited by 362 nm light,the cool white emission was realized by Na_(5)Y_(9)F_(32)single crystal triply-doped with 0.3 mol%Tm^(3+)/0.6 mol%Tb^(3+)/0.8 mol%Eu^(3+),in which the Commission Internationale de l’Eclairage(CIE)chromaticity coordinate was(0.2995,0.3298)and the correlated color temperature(CCT)was 6586 K.The integrated normalized emission intensity of the tridoped single crystal at 448 K could keep 62%of that at 298 K.The internal quantum yield(QY)was calculated to be~15.16%by integrating spheres.These results suggested that the single crystals tri-doped with Tm^(3+),Tb^(3+)and Eu^(3+)ions have a promising potential application for white light-emitting diodes(w-LEDs).展开更多
文摘Eu^(2+) and Mn^(2+) co-activated CaAlSiN_(3) red phosphors were produced using the solid-state reaction tech⁃nique in a N2 environment.Excitation spectra,emission spectra,and diffuse reflection spectra were used to study the luminescence characteristics,energy gap,and thermal stability in detail.CaAlSiN_(3)∶Eu^(2+) exhibits an extended emission band when stimulated with 450 nm blue light,which is caused by the 4f65d to 4f7 transition of Eu^(2+).Similar⁃ly,CaAlSiN_(3)∶Mn^(2+) displays a wide emission band centered at 628 nm,which results from Mn^(2+)’s transition from 4T1(4G) to 6A1(6S).When the ions of Mn^(2+)were combined into CaAlSiN_(3)∶Eu^(2+),the photoluminescence intensity of Eu^(2+ )was greatly boosted because there was energy transfer and co-emission between Mn^(2+) and Eu^(2+).Beyond that,CaAlSiN_(3)∶Eu^(2+),Mn^(2+) emerges with splendid thermostability and high quantum efficiency,the quenching temperature surpasses 300℃,and the internal quantum efficiency is determined to be around 84.9%.The white LED was pack⁃aged with a combination of CaAlSiN_(3)∶Eu^(2+),Mn^(2+),LuAG∶Ce3+ and a blue chip.At a warm white-light corresponding color temperature(3009 K) with CIE coordinates(0.4223,0.3748),the color rendering index Ra has reached 93.2.CaAlSiN_(3)∶Eu^(2+),Mn^(2+) would have great application potential as a red-emitting phosphor for white LEDs.
基金Project supported by the National Natural Science Foundation of China(Grant No.62275133)the Natural Science Foundation of Zhejiang Province of China(Grant No.LY22E020002)+1 种基金the Natural Science Foundation of Ningbo(Grant Nos.2021J077 and 202003N4099)K.C.Wong Magna Fund in Ningbo University
文摘By using an improved Bridgman method,0.3 mol%Tm^(3+)/0.6 mol%Tb^(3+)/y mol%Eu^(3+)(y=0,0.4,0.6,0.8)doped Na_(5)Y_(9)F_(32)single crystals were prepared.The x-ray diffraction,excitation spectra,emission spectra and fluorescence decay curves were used to explore the crystal structure and optical performance of the obtained samples.When excited by 362 nm light,the cool white emission was realized by Na_(5)Y_(9)F_(32)single crystal triply-doped with 0.3 mol%Tm^(3+)/0.6 mol%Tb^(3+)/0.8 mol%Eu^(3+),in which the Commission Internationale de l’Eclairage(CIE)chromaticity coordinate was(0.2995,0.3298)and the correlated color temperature(CCT)was 6586 K.The integrated normalized emission intensity of the tridoped single crystal at 448 K could keep 62%of that at 298 K.The internal quantum yield(QY)was calculated to be~15.16%by integrating spheres.These results suggested that the single crystals tri-doped with Tm^(3+),Tb^(3+)and Eu^(3+)ions have a promising potential application for white light-emitting diodes(w-LEDs).