In this paper, optical spectra of LiYF4 single crystals doped with Tm3＋ ions of various concentrations are reported. The emission intensity at 1.8 ktm first increases with increasing Tm3＋ concentration, and reaches ...In this paper, optical spectra of LiYF4 single crystals doped with Tm3＋ ions of various concentrations are reported. The emission intensity at 1.8 ktm first increases with increasing Tm3＋ concentration, and reaches a maximum value when the concentration of Tm3＋ is about 1.28 mol%, then it decreases rapidly as the concentration of Tm3＋ further increases to 3.49 mol%. The emission lifetime at 1.8 p.m also shows a similar tendency to the emission intensity. The maximum lifetime of 1.8 μm is measured to be 17.68 ms for the sample doped with Tm3＋ of 1.28 mol%. The emission cross section of 3F4 level is calculated. The maximum reaches 3.76 × 10 -21 cm2 at 1909 nm. The cross relaxation （3H6, 3H4 →3 F4, 3F4） between Tm3＋ ions and the concentration quenching effect are mainly attributed to the change of emission with Tm3＋ concentration. The largest quantum efficiency between Tm3＋ ions is estimated to be ,-147% from the measured lifetime and calculated radiative lifetime. All the results suggest that the Tm3＋/LiYF4 single crystal may have potential applications in 2 μm mid-infrared lasers.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant Nos.51472125 and 51272109)the Natural Science Foundation of Ningbo City,China(Grant No.201401A6105016)K.C.Wong Magna Fund in Ningbo University,China(Grant No.NBUWC001)
文摘In this paper, optical spectra of LiYF4 single crystals doped with Tm3＋ ions of various concentrations are reported. The emission intensity at 1.8 ktm first increases with increasing Tm3＋ concentration, and reaches a maximum value when the concentration of Tm3＋ is about 1.28 mol%, then it decreases rapidly as the concentration of Tm3＋ further increases to 3.49 mol%. The emission lifetime at 1.8 p.m also shows a similar tendency to the emission intensity. The maximum lifetime of 1.8 μm is measured to be 17.68 ms for the sample doped with Tm3＋ of 1.28 mol%. The emission cross section of 3F4 level is calculated. The maximum reaches 3.76 × 10 -21 cm2 at 1909 nm. The cross relaxation （3H6, 3H4 →3 F4, 3F4） between Tm3＋ ions and the concentration quenching effect are mainly attributed to the change of emission with Tm3＋ concentration. The largest quantum efficiency between Tm3＋ ions is estimated to be ,-147% from the measured lifetime and calculated radiative lifetime. All the results suggest that the Tm3＋/LiYF4 single crystal may have potential applications in 2 μm mid-infrared lasers.