In this paper, turning experiments of machining particle reinforced metal matri x composites(PRMMCs) SiC p/Al with PCD tools have been carried out. The cutting force characteristics in ultrasonic vibration turning com...In this paper, turning experiments of machining particle reinforced metal matri x composites(PRMMCs) SiC p/Al with PCD tools have been carried out. The cutting force characteristics in ultrasonic vibration turning compared with that in com mon turning were studied. Through the single factor experiments and multiple fac tor orthogonal experiments, the influences of three kinds of cutting conditions such as cutting velocity, amount of feed and cutting depth on cutting force were analyzed in detail. Meanwhile, according to the experimental data, the empirica l formula of main cutting force in ultrasonic vibration turning was conclude d. According to the test results, the cutting force is direct proportion to cutt ing depth basically according to the relation between cutting force and other fa ctors, which is similar to that of common cutting, so is the feed rate, but the influence is not so big. The influence of cutting speed is larger than that of f eed rate on cutting force because the efficient cutting time increases in vibrat ion cycle with the increase of cutting speed, which causes cutting force to incr ease. The research results indicate: (1) Ultrasonic vibration turning possesses much lower main cutting force than that in common turning when adopting smaller cutting parameters. If using larger cutting parameters, the difference will inco nspicuous. (2) There are remarkable differences of cutting force-cutting veloci ty characteristics in ultrasonic vibration turning from that in common turning m ainly because built-up edge does not emerge in ultrasonic turning unlike common turning in corresponding velocity range. (3) In ultrasonic vibration cutting, t he influence of cutting velocity on cutting force is most obvious among thre e cutting parameters and the influence of feed is smallest. So adopting lower cu tting velocity and larger cutting depth not only can reduce cutting force effect ively but also can ensure cutting efficiency. (4) The conclusions are useful in precision and super precision manufacturing thin-wall pieces.展开更多
Two-dimensional plain-weave silicon carbide fiber fabric reinforced silicon carbide(2D-SiC/SiC)composites were molded by stacking method and densified through precursor infiltration and pyrolysis(PIP)process.SiC coati...Two-dimensional plain-weave silicon carbide fiber fabric reinforced silicon carbide(2D-SiC/SiC)composites were molded by stacking method and densified through precursor infiltration and pyrolysis(PIP)process.SiC coating was deposited as the fiber/matrix interphase layer by chemical vapor deposition(CVD)technique.Fiber/matrix debonding and relatively long fiber pullouts were observed on the fracture surfaces.Additionally,the flexural strength and elastic modulus of the composites with and without fiber/matrix interphase layer were investigated using three-point bending test and single-edge notched beam test.The results show that the fiber fraction and the porosity of 2D-SiC/SiC composites with and without coating are 27.2%(volume fraction)and 11.1%,and 40.7%(volume fraction)and 7.5%,respectively.And the flexural strength and elastic modulus of 2D-SiC/SiC composites with and without coating are 363.3 MPa and 127.8 GPa,and 180.2 MPa and 97.2 GPa,respectively.With a proper thickness,the coating can effectively adjust the fiber/matrix interface,thus causing a dramatic increase in the mechanical properties of the composites.展开更多
The cutting performance of particulate reinforced me tallic matrix composites(PRMMCs) SiC p/Al in ultrasonic vibration cutting and c ommon cutting with carbide tools and PCD tools was researched in the paper. Mic rost...The cutting performance of particulate reinforced me tallic matrix composites(PRMMCs) SiC p/Al in ultrasonic vibration cutting and c ommon cutting with carbide tools and PCD tools was researched in the paper. Mic rostructure of machined surface was described, the relation between cutting para meters and surface roughness was presented, and characteristic of the surface re mained stress was also presented. Furthermore, wear regularity and abrasion resi stance ability of tools in ultrasonic vibration cutting and common cutting o f PRMMCs were discussed in detail. The test results show: (1) The surface config urations are obviously different when using different tools to machine such PRMM Cs. The surface machined with carbide tools looks luminous and orderly and there are seldom surface defects on it. The reason is that the soft basal body is apt to flow during cutting, therefore a layer of Al matrix film covers machined sur face. On the contrary, the surface machined with PCD tools looks lackluster. But the profile of machined surface is very clear. Superfine grooves, pits and blac k reinforce particulates can be seen easily without obvious Al film. (2) Because of unstable cutting process in common cutting, the surface is easy to produce s ome defects such as burrs, built-up edges and so on so that the quality of surf ace becomes very poor. Vibration cutting can reduce the influence of tearing, pl astic deformation and built-up edge in cutting and can restrain flutter so as t o make cutting process more stable. Therefore, surface roughness of vibration cu tting is better than that of common cutting. (3) There is an optimum value of fe ed rate in vibration cutting of PRMMCs due to the influence of material characte ristics. Whether feed rate is more than or less than this optimum value, surface roughness will increase. (4) According to analyzing the wear rate of tools in v ibration cutting PRMMCs, it can be concluded that abrasion resistance of tools w ill be improved remarkably when vibration cutting composites have a lower pe rcentage of reinforce particulate. If the percentage of reinforce particulate is higher, the influence on abrasion resistance of carbide tool in vibration cut ting will not be obvious. The research result indicates that vibration cutting effect has a close relation with material characteristics.展开更多
文摘In this paper, turning experiments of machining particle reinforced metal matri x composites(PRMMCs) SiC p/Al with PCD tools have been carried out. The cutting force characteristics in ultrasonic vibration turning compared with that in com mon turning were studied. Through the single factor experiments and multiple fac tor orthogonal experiments, the influences of three kinds of cutting conditions such as cutting velocity, amount of feed and cutting depth on cutting force were analyzed in detail. Meanwhile, according to the experimental data, the empirica l formula of main cutting force in ultrasonic vibration turning was conclude d. According to the test results, the cutting force is direct proportion to cutt ing depth basically according to the relation between cutting force and other fa ctors, which is similar to that of common cutting, so is the feed rate, but the influence is not so big. The influence of cutting speed is larger than that of f eed rate on cutting force because the efficient cutting time increases in vibrat ion cycle with the increase of cutting speed, which causes cutting force to incr ease. The research results indicate: (1) Ultrasonic vibration turning possesses much lower main cutting force than that in common turning when adopting smaller cutting parameters. If using larger cutting parameters, the difference will inco nspicuous. (2) There are remarkable differences of cutting force-cutting veloci ty characteristics in ultrasonic vibration turning from that in common turning m ainly because built-up edge does not emerge in ultrasonic turning unlike common turning in corresponding velocity range. (3) In ultrasonic vibration cutting, t he influence of cutting velocity on cutting force is most obvious among thre e cutting parameters and the influence of feed is smallest. So adopting lower cu tting velocity and larger cutting depth not only can reduce cutting force effect ively but also can ensure cutting efficiency. (4) The conclusions are useful in precision and super precision manufacturing thin-wall pieces.
基金Project(NCET-07-0228)support by the New Century Excellent Talents in University
文摘Two-dimensional plain-weave silicon carbide fiber fabric reinforced silicon carbide(2D-SiC/SiC)composites were molded by stacking method and densified through precursor infiltration and pyrolysis(PIP)process.SiC coating was deposited as the fiber/matrix interphase layer by chemical vapor deposition(CVD)technique.Fiber/matrix debonding and relatively long fiber pullouts were observed on the fracture surfaces.Additionally,the flexural strength and elastic modulus of the composites with and without fiber/matrix interphase layer were investigated using three-point bending test and single-edge notched beam test.The results show that the fiber fraction and the porosity of 2D-SiC/SiC composites with and without coating are 27.2%(volume fraction)and 11.1%,and 40.7%(volume fraction)and 7.5%,respectively.And the flexural strength and elastic modulus of 2D-SiC/SiC composites with and without coating are 363.3 MPa and 127.8 GPa,and 180.2 MPa and 97.2 GPa,respectively.With a proper thickness,the coating can effectively adjust the fiber/matrix interface,thus causing a dramatic increase in the mechanical properties of the composites.
文摘The cutting performance of particulate reinforced me tallic matrix composites(PRMMCs) SiC p/Al in ultrasonic vibration cutting and c ommon cutting with carbide tools and PCD tools was researched in the paper. Mic rostructure of machined surface was described, the relation between cutting para meters and surface roughness was presented, and characteristic of the surface re mained stress was also presented. Furthermore, wear regularity and abrasion resi stance ability of tools in ultrasonic vibration cutting and common cutting o f PRMMCs were discussed in detail. The test results show: (1) The surface config urations are obviously different when using different tools to machine such PRMM Cs. The surface machined with carbide tools looks luminous and orderly and there are seldom surface defects on it. The reason is that the soft basal body is apt to flow during cutting, therefore a layer of Al matrix film covers machined sur face. On the contrary, the surface machined with PCD tools looks lackluster. But the profile of machined surface is very clear. Superfine grooves, pits and blac k reinforce particulates can be seen easily without obvious Al film. (2) Because of unstable cutting process in common cutting, the surface is easy to produce s ome defects such as burrs, built-up edges and so on so that the quality of surf ace becomes very poor. Vibration cutting can reduce the influence of tearing, pl astic deformation and built-up edge in cutting and can restrain flutter so as t o make cutting process more stable. Therefore, surface roughness of vibration cu tting is better than that of common cutting. (3) There is an optimum value of fe ed rate in vibration cutting of PRMMCs due to the influence of material characte ristics. Whether feed rate is more than or less than this optimum value, surface roughness will increase. (4) According to analyzing the wear rate of tools in v ibration cutting PRMMCs, it can be concluded that abrasion resistance of tools w ill be improved remarkably when vibration cutting composites have a lower pe rcentage of reinforce particulate. If the percentage of reinforce particulate is higher, the influence on abrasion resistance of carbide tool in vibration cut ting will not be obvious. The research result indicates that vibration cutting effect has a close relation with material characteristics.