A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acid...A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.展开更多
通过水热改性氢氧化锆制备了SO42-/ZrO2固体酸催化剂。以冰乙酸和正丁醇的酯化反应为探针反应,确定了固体超强酸的最佳制备条件。分别考察了浸渍硫酸浓度、硫酸浸渍时间和焙烧温度等对催化活性的影响。并以水热改性和未经水热改性氢氧...通过水热改性氢氧化锆制备了SO42-/ZrO2固体酸催化剂。以冰乙酸和正丁醇的酯化反应为探针反应,确定了固体超强酸的最佳制备条件。分别考察了浸渍硫酸浓度、硫酸浸渍时间和焙烧温度等对催化活性的影响。并以水热改性和未经水热改性氢氧化锆制备SO42-/ZrO2固体超强酸做了对比实验,采用XRD、BET对催化剂进行了表征。实验结果表明:水热改性氢氧化锆制备SO42-/ZrO2固体酸催化剂的最佳条件是:浸渍硫酸浓度为0.5mol/L,浸渍时间是120 m in,焙烧温度500℃。乙酸正丁酯较佳的合成工艺条件是:反应温度105~110℃,反应时间2 h,n(正丁醇)∶n(冰乙酸)=2∶1,催化剂用量占反应投料总质量的0.27%,冰乙酸的酯化率达99.1%。催化剂重复使用4次后催化活性降低5%。展开更多
文摘A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.
文摘通过水热改性氢氧化锆制备了SO42-/ZrO2固体酸催化剂。以冰乙酸和正丁醇的酯化反应为探针反应,确定了固体超强酸的最佳制备条件。分别考察了浸渍硫酸浓度、硫酸浸渍时间和焙烧温度等对催化活性的影响。并以水热改性和未经水热改性氢氧化锆制备SO42-/ZrO2固体超强酸做了对比实验,采用XRD、BET对催化剂进行了表征。实验结果表明:水热改性氢氧化锆制备SO42-/ZrO2固体酸催化剂的最佳条件是:浸渍硫酸浓度为0.5mol/L,浸渍时间是120 m in,焙烧温度500℃。乙酸正丁酯较佳的合成工艺条件是:反应温度105~110℃,反应时间2 h,n(正丁醇)∶n(冰乙酸)=2∶1,催化剂用量占反应投料总质量的0.27%,冰乙酸的酯化率达99.1%。催化剂重复使用4次后催化活性降低5%。