The effects of H3PO4 and Ca（H2PO4）2 on compressive strength, water resistance, hydration process of thermally decomposed magnesium oxychloride cement （TDMOC） pastes were studied. The mineral composition, hydration...The effects of H3PO4 and Ca（H2PO4）2 on compressive strength, water resistance, hydration process of thermally decomposed magnesium oxychloride cement （TDMOC） pastes were studied. The mineral composition, hydration products and hydration heat release were analyzed by XRD, FT-IR, SEM and TAM air isothermal calorimeter, etc. After being modified by H3PO4 and Ca（HzPO4）2, the properties of the TDMOC are improved obviously. The compressive strength increases from 14.8 MPa to 48.1 MPa and 37.1 MPa, respectively. The strength retention coefficient （Kn） increases from 0.38 to 0.99 and 0.94, respectively. The 24 h hydration heat release decreases by 10% and 4% and the time of hydration peak appearing is delayed from 1 h to about 10 h. The XRD, FT-IR and SEM results show that the main composition is 5Mg（OH）z＇MgCIz＇8H20 in the modified TDMOC pastes. The possible mechanism for the strength enhancement was discussed. The purposes are to extend the potential applications of the salt lake magnesium resources and to improve the mechanical properties of TDMOC.展开更多
NiFe2O4-based cermet inert anodes with metallic phase compositions of Cu, Ni and 85Cu15Ni were prepared by cold pressing-sintering. Their corrosion resistance was also investigated in Na3 AIF6-Al2O3 melts. The resuits...NiFe2O4-based cermet inert anodes with metallic phase compositions of Cu, Ni and 85Cu15Ni were prepared by cold pressing-sintering. Their corrosion resistance was also investigated in Na3 AIF6-Al2O3 melts. The resuits show that the metallic phase species in cermets have no effect on the concentration of impurities in bath during electrolysis, the total steady-state concentration of impurities is almost the same, i.e. between 4.12 × 10^-4- 4.80 × 10^-4. There exists metal preferential corrosion for the cermet inert anode with metal Ni as metallic phase. For NiFe2 O4-based cermets, the cermet with metal Cu as metallic phase exhibits better corrosion resistance than the others.展开更多
BNp/Al2O3-SiO2 system ceramic matrix composites with different volume fractions （10%-60%） of hexagonal BN particulates （BNp） were prepared by hot-press sintering technique. Phase components, microstructure, mechan...BNp/Al2O3-SiO2 system ceramic matrix composites with different volume fractions （10%-60%） of hexagonal BN particulates （BNp） were prepared by hot-press sintering technique. Phase components, microstructure, mechanical properties and plasma erosion resistance were also investigated. With the increase of h-BNp content, relative density and Vickers＇ hardness of the composite ceramics decrease, while the flexural strength, elastic modulus and fracture toughness increase and then decrease. The plasma erosion resistance linearly deteriorated with the increase of BNp content which is mainly determined by the density, crystal structure and atomic number of the elements.展开更多
The CaO doped 10NiO-NiFe2O4 composite ceramics were prepared by the cold isostatic pressing-sintering process, and the effects of CaO content on the phase composition, mechanical property and thermal shock resistance ...The CaO doped 10NiO-NiFe2O4 composite ceramics were prepared by the cold isostatic pressing-sintering process, and the effects of CaO content on the phase composition, mechanical property and thermal shock resistance of 10NiO-NiFe2O4 composite ceramics were studied. The results show that the samples mainly consist of NiO and NiFe2O4 when content of CaO is less than 4%(mass fraction), bending strength increases obviously by CaO doping. Bending strength of the samples doped with 2% CaO is above 185 MPa, but that of the samples without CaO is only 60 MPa. Fracture toughness is improved obviously by CaO doping, the samples doped with 2% CaO have the maximum fracture toughness of 2.12 MPa ·m1/2 , which is about two times of that of the undoped ceramics. CaO doping is bad to thermal shock resistance of 10NiO-NiFe2O4 composite ceramics.展开更多
基金Project(B0210)supported by One Hundred Talent Project of Chinese Academy of SciencesProject(2008-G-158)supported by Science and Technology Tackling Key Program of Qinghai Province,China
文摘The effects of H3PO4 and Ca（H2PO4）2 on compressive strength, water resistance, hydration process of thermally decomposed magnesium oxychloride cement （TDMOC） pastes were studied. The mineral composition, hydration products and hydration heat release were analyzed by XRD, FT-IR, SEM and TAM air isothermal calorimeter, etc. After being modified by H3PO4 and Ca（HzPO4）2, the properties of the TDMOC are improved obviously. The compressive strength increases from 14.8 MPa to 48.1 MPa and 37.1 MPa, respectively. The strength retention coefficient （Kn） increases from 0.38 to 0.99 and 0.94, respectively. The 24 h hydration heat release decreases by 10% and 4% and the time of hydration peak appearing is delayed from 1 h to about 10 h. The XRD, FT-IR and SEM results show that the main composition is 5Mg（OH）z＇MgCIz＇8H20 in the modified TDMOC pastes. The possible mechanism for the strength enhancement was discussed. The purposes are to extend the potential applications of the salt lake magnesium resources and to improve the mechanical properties of TDMOC.
基金Project(2005CB623703) supported by the National Basic Research Programof China project(03JJY3080) supported bythe Hunan Provincial Natural Science Foundation
文摘NiFe2O4-based cermet inert anodes with metallic phase compositions of Cu, Ni and 85Cu15Ni were prepared by cold pressing-sintering. Their corrosion resistance was also investigated in Na3 AIF6-Al2O3 melts. The resuits show that the metallic phase species in cermets have no effect on the concentration of impurities in bath during electrolysis, the total steady-state concentration of impurities is almost the same, i.e. between 4.12 × 10^-4- 4.80 × 10^-4. There exists metal preferential corrosion for the cermet inert anode with metal Ni as metallic phase. For NiFe2 O4-based cermets, the cermet with metal Cu as metallic phase exhibits better corrosion resistance than the others.
基金Project(HIT.NSRIF.2010112)supported by the Fundamental Research Fund for the Central Universities,ChinaProjects(50902030,51021002)supported by the National Natural Science Foundation of China
文摘BNp/Al2O3-SiO2 system ceramic matrix composites with different volume fractions （10%-60%） of hexagonal BN particulates （BNp） were prepared by hot-press sintering technique. Phase components, microstructure, mechanical properties and plasma erosion resistance were also investigated. With the increase of h-BNp content, relative density and Vickers＇ hardness of the composite ceramics decrease, while the flexural strength, elastic modulus and fracture toughness increase and then decrease. The plasma erosion resistance linearly deteriorated with the increase of BNp content which is mainly determined by the density, crystal structure and atomic number of the elements.
基金Project(2005CB623703) supported by the National Basic Research Program of China
文摘The CaO doped 10NiO-NiFe2O4 composite ceramics were prepared by the cold isostatic pressing-sintering process, and the effects of CaO content on the phase composition, mechanical property and thermal shock resistance of 10NiO-NiFe2O4 composite ceramics were studied. The results show that the samples mainly consist of NiO and NiFe2O4 when content of CaO is less than 4%(mass fraction), bending strength increases obviously by CaO doping. Bending strength of the samples doped with 2% CaO is above 185 MPa, but that of the samples without CaO is only 60 MPa. Fracture toughness is improved obviously by CaO doping, the samples doped with 2% CaO have the maximum fracture toughness of 2.12 MPa ·m1/2 , which is about two times of that of the undoped ceramics. CaO doping is bad to thermal shock resistance of 10NiO-NiFe2O4 composite ceramics.