Ca2-xSrxZn4Ti15O36∶Pr red long decay phosphor was synthesized by high temperature solid state reaction. Photoluminescence property and crystalline and unit cell parameters of the orthorhombic were investigated by flu...Ca2-xSrxZn4Ti15O36∶Pr red long decay phosphor was synthesized by high temperature solid state reaction. Photoluminescence property and crystalline and unit cell parameters of the orthorhombic were investigated by fluorescence spectrophotometer and by powder X-ray diffraction, respectively. The emission intensity at 618 nm changes sharply when the concentration of Sr2+ （x） is less than 0.1 and the emission intensity reaches the maximum when x is equal to 0.007. There is an obviously broad excitation band at 270 nm when x is equal to 0.003 and it disappears gradually when x is over 0.01. The unit cell a parameter of Ca2-xSrxZn4Ti15O36∶Pr decreases while c parameter increases with the increases of the concentration of the doped Sr2+. When x is over 0.1 the value of the unit cell parameters a and c become stable. TL peaks of Ca2Zn4Ti15O36∶Pr, Ca1.993Sr0.007Zn4Ti15O36∶0.002Pr3+, 0.002Na+, are located at 62 ℃, 88 ℃, respectively, which indicates that there are deeper traps in Ca1.993Sr0.007Zn4 Ti15O36∶0.002Pr3+, 0.002Na+.展开更多
The vacuum ultraviolet (VUV) spectroscopic properties of praseodymium (Pr3+, 1at%) doped LaF3 nanocrystals/glass at room temperature and 20 K are reported. Two types of Pr3+ ions, those in LaF3 nanocrystals and those ...The vacuum ultraviolet (VUV) spectroscopic properties of praseodymium (Pr3+, 1at%) doped LaF3 nanocrystals/glass at room temperature and 20 K are reported. Two types of Pr3+ ions, those in LaF3 nanocrystals and those in the glass host, were excited to 4f 5d band by VUV using synchrotron radiation as an excitation source, and emissions of 1S0 → 1D2 (336 nm), 1S0 → 1I6 (397 nm ) of Pr3+ in the nanocrystals and emissions of 4f 5d → 3HJ, 3FJ of Pr3+ in the glass appeared at the same time. But unlike in the bulk sample crystals, emission of 3P0 → 3HJ, 3FJ as the second step of the quantum splitting (QS) of Pr3+ in the LaF3 nanocrystals was not observed at room temperature, which could be explained that Pr3+ ions in the glass absorbed the energy of 3P0 → 3H4 of Pr3+ in the nanocrystals. Two types of excitation spectra monitoring different emissions were also measured, so it could be observed that the lowest energy of 4f 5d band of Pr3+ in the nanocrystals was about 53 500 cm-1 (186 nm) and in the glass about 33 800 cm-1(295 nm), respectively. These emission and excitation spectra were contrasted to those of bulk sample crystals LaF3∶Pr3+.展开更多
The single crystal of GdP 5O 14 :Sm 3+ ,Pr 3+ (GdPP:Sm,Pr) was grown by the hydrothermal method. The crystal belongs to the monoclinic space group P2 1/ C by X ray powder diffraction results. The dependence of Pr 3+ i...The single crystal of GdP 5O 14 :Sm 3+ ,Pr 3+ (GdPP:Sm,Pr) was grown by the hydrothermal method. The crystal belongs to the monoclinic space group P2 1/ C by X ray powder diffraction results. The dependence of Pr 3+ ion concentration in GdPP:Sm,Pr crystals on the emission intensity of 4 G 5/2 → 6 H 7/2 transitions of Sm 3+ ion and the energy transfer between Sm 3+ and Pr 3+ ions have been investigated and discussed.展开更多
文摘Ca2-xSrxZn4Ti15O36∶Pr red long decay phosphor was synthesized by high temperature solid state reaction. Photoluminescence property and crystalline and unit cell parameters of the orthorhombic were investigated by fluorescence spectrophotometer and by powder X-ray diffraction, respectively. The emission intensity at 618 nm changes sharply when the concentration of Sr2+ （x） is less than 0.1 and the emission intensity reaches the maximum when x is equal to 0.007. There is an obviously broad excitation band at 270 nm when x is equal to 0.003 and it disappears gradually when x is over 0.01. The unit cell a parameter of Ca2-xSrxZn4Ti15O36∶Pr decreases while c parameter increases with the increases of the concentration of the doped Sr2+. When x is over 0.1 the value of the unit cell parameters a and c become stable. TL peaks of Ca2Zn4Ti15O36∶Pr, Ca1.993Sr0.007Zn4Ti15O36∶0.002Pr3+, 0.002Na+, are located at 62 ℃, 88 ℃, respectively, which indicates that there are deeper traps in Ca1.993Sr0.007Zn4 Ti15O36∶0.002Pr3+, 0.002Na+.
文摘The vacuum ultraviolet (VUV) spectroscopic properties of praseodymium (Pr3+, 1at%) doped LaF3 nanocrystals/glass at room temperature and 20 K are reported. Two types of Pr3+ ions, those in LaF3 nanocrystals and those in the glass host, were excited to 4f 5d band by VUV using synchrotron radiation as an excitation source, and emissions of 1S0 → 1D2 (336 nm), 1S0 → 1I6 (397 nm ) of Pr3+ in the nanocrystals and emissions of 4f 5d → 3HJ, 3FJ of Pr3+ in the glass appeared at the same time. But unlike in the bulk sample crystals, emission of 3P0 → 3HJ, 3FJ as the second step of the quantum splitting (QS) of Pr3+ in the LaF3 nanocrystals was not observed at room temperature, which could be explained that Pr3+ ions in the glass absorbed the energy of 3P0 → 3H4 of Pr3+ in the nanocrystals. Two types of excitation spectra monitoring different emissions were also measured, so it could be observed that the lowest energy of 4f 5d band of Pr3+ in the nanocrystals was about 53 500 cm-1 (186 nm) and in the glass about 33 800 cm-1(295 nm), respectively. These emission and excitation spectra were contrasted to those of bulk sample crystals LaF3∶Pr3+.
文摘The single crystal of GdP 5O 14 :Sm 3+ ,Pr 3+ (GdPP:Sm,Pr) was grown by the hydrothermal method. The crystal belongs to the monoclinic space group P2 1/ C by X ray powder diffraction results. The dependence of Pr 3+ ion concentration in GdPP:Sm,Pr crystals on the emission intensity of 4 G 5/2 → 6 H 7/2 transitions of Sm 3+ ion and the energy transfer between Sm 3+ and Pr 3+ ions have been investigated and discussed.