Piezoelectric ceramics (Na0.5Bi0.5) （0.92）Ba0.08TiO3 +x%MnCO3（BNBT-Mn, x=0CD*21.6, mass fraction） were synthesized by conventional solid state reaction. The results show that when the addition of MnCO3 is 0CD*2 1....Piezoelectric ceramics (Na0.5Bi0.5) （0.92）Ba0.08TiO3 +x%MnCO3（BNBT-Mn, x=0CD*21.6, mass fraction） were synthesized by conventional solid state reaction. The results show that when the addition of MnCO3 is 0CD*2 1.4%, BNBT-Mn ceramics exhibit a single-phase perovskite structure. With the increase of content of MnCO3, piezoelectric constant and electromechanical coupling factor increase rapidly when x is lower than 0.3. Then they both decrease when x is in the range of 0.3 and 1.6. When x=0.3, piezoelectric constant and electromechanical coupling factor reach the maximum value of 160pC/N and 58.5% respectively, which can improve the temperature stability of BNBT-Mn.展开更多
以固态氧化物为原料,采用固态合成工艺制备Pb(Zn1/3Nb2/3)O3-Pb(Ni1/3Nb2/3)O3-Pb(ZrTi)O3(PZN-PNN-PZT)压电陶瓷,并研究了锆钛比(r(Zr)/r(Ti))、Ba2+的A位取代及Ba2+、La3+的A位复合取代对压电陶瓷电性能的影响。结果表明,PZN-PNN-PZT...以固态氧化物为原料,采用固态合成工艺制备Pb(Zn1/3Nb2/3)O3-Pb(Ni1/3Nb2/3)O3-Pb(ZrTi)O3(PZN-PNN-PZT)压电陶瓷,并研究了锆钛比(r(Zr)/r(Ti))、Ba2+的A位取代及Ba2+、La3+的A位复合取代对压电陶瓷电性能的影响。结果表明,PZN-PNN-PZT压电陶瓷在r(Zr)/r(Ti)=1.03下,进行Ba2+,La3+的A位复合取代后,即式子在Pb0.92Ba0.04La0.04(Ni1/3Nb2/3)y(Zn1/3Nb2/3)z Zrm Tin O3时压电性能最佳,其介电常数εT33/ε0=5 657,压电常数d33=709pC/N,机电耦合系数kp=0.69,品质因数Qm=45,居里温度TC=180.9℃。展开更多
文摘Piezoelectric ceramics (Na0.5Bi0.5) （0.92）Ba0.08TiO3 +x%MnCO3（BNBT-Mn, x=0CD*21.6, mass fraction） were synthesized by conventional solid state reaction. The results show that when the addition of MnCO3 is 0CD*2 1.4%, BNBT-Mn ceramics exhibit a single-phase perovskite structure. With the increase of content of MnCO3, piezoelectric constant and electromechanical coupling factor increase rapidly when x is lower than 0.3. Then they both decrease when x is in the range of 0.3 and 1.6. When x=0.3, piezoelectric constant and electromechanical coupling factor reach the maximum value of 160pC/N and 58.5% respectively, which can improve the temperature stability of BNBT-Mn.
文摘以固态氧化物为原料,采用固态合成工艺制备Pb(Zn1/3Nb2/3)O3-Pb(Ni1/3Nb2/3)O3-Pb(ZrTi)O3(PZN-PNN-PZT)压电陶瓷,并研究了锆钛比(r(Zr)/r(Ti))、Ba2+的A位取代及Ba2+、La3+的A位复合取代对压电陶瓷电性能的影响。结果表明,PZN-PNN-PZT压电陶瓷在r(Zr)/r(Ti)=1.03下,进行Ba2+,La3+的A位复合取代后,即式子在Pb0.92Ba0.04La0.04(Ni1/3Nb2/3)y(Zn1/3Nb2/3)z Zrm Tin O3时压电性能最佳,其介电常数εT33/ε0=5 657,压电常数d33=709pC/N,机电耦合系数kp=0.69,品质因数Qm=45,居里温度TC=180.9℃。