A new inorganic-organic hybrid framework microporous material Cd 3(BDC) 0.5(BTC) 2·(DMF)(H 2O)·3DMF·H 3O·H 2O, in which two kinds of carboxylate ligands coordinate with cadmium ions synchronously, ...A new inorganic-organic hybrid framework microporous material Cd 3(BDC) 0.5(BTC) 2·(DMF)(H 2O)·3DMF·H 3O·H 2O, in which two kinds of carboxylate ligands coordinate with cadmium ions synchronously, was obtained under a mild synthesis condition. The titled compound is crystallized in a monoclinic system, space group P2(1)/c with a=1.584 7(7) nm, b=1.426 7(6) nm, c=1.936 3(6) nm, β=113.186(7)°, V=4.024 6(3) nm 3, Z=4, D X=1.947 mg/m 3, M r=1 179.92, μ=1.662 mm -1, F(000)=2 344, R=0.074 8, wR=0.215 1. Three cadmium centers link with each other through BDC or BTC ligand to form a 3-D open framework.展开更多
Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part i...Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.展开更多
文摘A new inorganic-organic hybrid framework microporous material Cd 3(BDC) 0.5(BTC) 2·(DMF)(H 2O)·3DMF·H 3O·H 2O, in which two kinds of carboxylate ligands coordinate with cadmium ions synchronously, was obtained under a mild synthesis condition. The titled compound is crystallized in a monoclinic system, space group P2(1)/c with a=1.584 7(7) nm, b=1.426 7(6) nm, c=1.936 3(6) nm, β=113.186(7)°, V=4.024 6(3) nm 3, Z=4, D X=1.947 mg/m 3, M r=1 179.92, μ=1.662 mm -1, F(000)=2 344, R=0.074 8, wR=0.215 1. Three cadmium centers link with each other through BDC or BTC ligand to form a 3-D open framework.
文摘Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.