With ongoing global warming and increasing energy demands,the CH_(4)-CO_(2)reforming reaction(dry reforming of methane,DRM)has garnered significant attention as a promising carbon capture and utilization technology.Ni...With ongoing global warming and increasing energy demands,the CH_(4)-CO_(2)reforming reaction(dry reforming of methane,DRM)has garnered significant attention as a promising carbon capture and utilization technology.Nickel-based catalysts are renowned for their outstanding activity and selectivity in this process.The impact of metal-support interaction(MSI),on Ni-based catalyst performance has been extensively researched and debated recently.This paper reviews the recent research progress of MSI on Ni-based catalysts and their characterization and modulation strategies in catalytic reactions.From the perspective of MSI,the effects of different carriers(metal oxides,carbon materials and molecular sieves,etc.)are introduced on the dispersion and surface structure of Ni active metal particles,and the effect of MSI on the activity and stability of DRM reactions on Ni-based catalysts is discussed in detail.Future research should focus on better understanding and controlling MSI to improve the performance and durability of nickel-based catalysts in CH_(4)-CO_(2)reforming,advancing cleaner energy technologies.展开更多
After a standard heat treatment,the microstructural evolution with time during isothermal aging at 850°C and its effect on the creep rupture properties of the Ni-base superalloy M4706 at 870°C and 370 MPa ar...After a standard heat treatment,the microstructural evolution with time during isothermal aging at 850°C and its effect on the creep rupture properties of the Ni-base superalloy M4706 at 870°C and 370 MPa are investigated.It is found that as the aging time increases from 0 to 5000 h,the average diameter of coarseγ′increases from 241 to 484 nm,and the distribution of the carbides at grain boundaries changes from discontinuous to continuous.Moreover,experimental observations on the microstructures of all the crept specimens reveal that dislocation bypassing controls the creep deformation.Thus,it is concluded that the transitions in the microstructures result in the degeneration of the creep rupture properties of the experimental alloy with aging time.展开更多
Ni-based alloy coating on 21-4-N heat-resistant steel was prepared using CO2 laser, and the high-temperature abrasion wear was tested. The microstructure of this cladding layer and its abrasion wear behavior at high t...Ni-based alloy coating on 21-4-N heat-resistant steel was prepared using CO2 laser, and the high-temperature abrasion wear was tested. The microstructure of this cladding layer and its abrasion wear behavior at high temperature by changing compositions and temperatures were investigated by means of optical microscope and scanning electron microscope. Among the three compositions of cladding layer, i.e. Ni21+20%WC+0.5%CeO2, Ni25+20%WC+0.5%CeO2 and Ni60+20%WC+0.5%CeO2, the experimental results show that Ni21+20%WC+ 0.5%CeO2 cladding layer is made up of finer grains, and presents the best abrasion wear behavior at high temperature. The wear pattern of laser cladding layer is mainly grain abrasion at lower temperature, and it would be changed to adhesive abrasion and oxide abrasion at higher temperature.展开更多
Non-metallic inclusions,especially the large ones,within P/M Ni-base superalloy have a major influence on fatigue characteristics,but are not directly measurable by routine inspection.In this paper,a method,automatic ...Non-metallic inclusions,especially the large ones,within P/M Ni-base superalloy have a major influence on fatigue characteristics,but are not directly measurable by routine inspection.In this paper,a method,automatic image analysis,is proposed for estimation of the content,size and amount of non-metallic inclusions in superalloy.The methodology for the practical application of this method is described and the factors affecting the precision of the estimation are discussed.In the experiment,the characteristics of the non-metallic inclusions in Ni-base P/M superalloy are analyzed.展开更多
Recent research progress on the use of Ni-based catalysts supported by various carbon materials,such as carbon nanotubes,graphene,and activated carbon,for the hydrogenation of CO_(2)to CH4 is summarized.The influence ...Recent research progress on the use of Ni-based catalysts supported by various carbon materials,such as carbon nanotubes,graphene,and activated carbon,for the hydrogenation of CO_(2)to CH4 is summarized.The influence of additives and surface modification methods on improving their catalytic performance is discussed as is the reaction mechanism,especially the structurefunction relationship produced by the carbon.The review provides a comprehensive directory for the rational design of carbon-supported Ni-based catalysts for the methanation of CO_(2).展开更多
In this investigation,we examined the high-temperature corrosion behavior of three nickel-based single-crystal superalloys subjected to a mixed molten salt environment of Na_(2)SO_(4)and NaCl at 700℃,leading to a pre...In this investigation,we examined the high-temperature corrosion behavior of three nickel-based single-crystal superalloys subjected to a mixed molten salt environment of Na_(2)SO_(4)and NaCl at 700℃,leading to a preliminary elucidation of their molten salt corrosion mechanisms.By further comparing the corrosion degree of the three nickel-based single-crystal superalloys combined with the Gibbs free energy calculation of the corrosion products,the influence of alloying elements on the corrosion performance of nickel-based single-crystal superalloys was analyzed.It was established that the corrosion mechanism of these nickel-based single-crystal superalloys predominantly involves a cyclic process of oxide layer formation and decomposition,ultimately resulting in the establishment of a protective layer principally composed of NiO,with a constantly regenerating Al2O3 barrier,impeding further alloy degradation.Furthermore,the inclusion of elements such as Cr,Al,Ta,and notably Re has been found to markedly improve the thermal corrosion resistance of the superalloys.These insights not only enhance our comprehension of the corrosion mechanisms pertinent to nickel-based superalloys,but also provide strategic directions for alloy composition refinement aimed at bolstering their corrosion resilience.展开更多
基金supported by the Natural Science Foundation of Shanxi Province(202203021221155)the Foundation of National Key Laboratory of High Efficiency and Low Carbon Utilization of Coal(J23-24-902)。
文摘With ongoing global warming and increasing energy demands,the CH_(4)-CO_(2)reforming reaction(dry reforming of methane,DRM)has garnered significant attention as a promising carbon capture and utilization technology.Nickel-based catalysts are renowned for their outstanding activity and selectivity in this process.The impact of metal-support interaction(MSI),on Ni-based catalyst performance has been extensively researched and debated recently.This paper reviews the recent research progress of MSI on Ni-based catalysts and their characterization and modulation strategies in catalytic reactions.From the perspective of MSI,the effects of different carriers(metal oxides,carbon materials and molecular sieves,etc.)are introduced on the dispersion and surface structure of Ni active metal particles,and the effect of MSI on the activity and stability of DRM reactions on Ni-based catalysts is discussed in detail.Future research should focus on better understanding and controlling MSI to improve the performance and durability of nickel-based catalysts in CH_(4)-CO_(2)reforming,advancing cleaner energy technologies.
基金Project(2018BSHQYXMZZ32)supported by the Postdoctoral Science Foundation of Shaanxi Province of ChinaProject(20192109)supported by the State Key Laboratory for Mechanical Behavior of Materials,ChinaProjects(2017M623213,2018M633487)supported by the Postdoctoral Science Foundation of China
文摘After a standard heat treatment,the microstructural evolution with time during isothermal aging at 850°C and its effect on the creep rupture properties of the Ni-base superalloy M4706 at 870°C and 370 MPa are investigated.It is found that as the aging time increases from 0 to 5000 h,the average diameter of coarseγ′increases from 241 to 484 nm,and the distribution of the carbides at grain boundaries changes from discontinuous to continuous.Moreover,experimental observations on the microstructures of all the crept specimens reveal that dislocation bypassing controls the creep deformation.Thus,it is concluded that the transitions in the microstructures result in the degeneration of the creep rupture properties of the experimental alloy with aging time.
文摘Ni-based alloy coating on 21-4-N heat-resistant steel was prepared using CO2 laser, and the high-temperature abrasion wear was tested. The microstructure of this cladding layer and its abrasion wear behavior at high temperature by changing compositions and temperatures were investigated by means of optical microscope and scanning electron microscope. Among the three compositions of cladding layer, i.e. Ni21+20%WC+0.5%CeO2, Ni25+20%WC+0.5%CeO2 and Ni60+20%WC+0.5%CeO2, the experimental results show that Ni21+20%WC+ 0.5%CeO2 cladding layer is made up of finer grains, and presents the best abrasion wear behavior at high temperature. The wear pattern of laser cladding layer is mainly grain abrasion at lower temperature, and it would be changed to adhesive abrasion and oxide abrasion at higher temperature.
文摘Non-metallic inclusions,especially the large ones,within P/M Ni-base superalloy have a major influence on fatigue characteristics,but are not directly measurable by routine inspection.In this paper,a method,automatic image analysis,is proposed for estimation of the content,size and amount of non-metallic inclusions in superalloy.The methodology for the practical application of this method is described and the factors affecting the precision of the estimation are discussed.In the experiment,the characteristics of the non-metallic inclusions in Ni-base P/M superalloy are analyzed.
文摘Recent research progress on the use of Ni-based catalysts supported by various carbon materials,such as carbon nanotubes,graphene,and activated carbon,for the hydrogenation of CO_(2)to CH4 is summarized.The influence of additives and surface modification methods on improving their catalytic performance is discussed as is the reaction mechanism,especially the structurefunction relationship produced by the carbon.The review provides a comprehensive directory for the rational design of carbon-supported Ni-based catalysts for the methanation of CO_(2).
基金Project(2022QNRC001) supported by the Young Elite Scientists Sponsorship Program by China Association for Science and TechnologyProject supported by the State Key Laboratory of Powder Metallurgy,China。
文摘In this investigation,we examined the high-temperature corrosion behavior of three nickel-based single-crystal superalloys subjected to a mixed molten salt environment of Na_(2)SO_(4)and NaCl at 700℃,leading to a preliminary elucidation of their molten salt corrosion mechanisms.By further comparing the corrosion degree of the three nickel-based single-crystal superalloys combined with the Gibbs free energy calculation of the corrosion products,the influence of alloying elements on the corrosion performance of nickel-based single-crystal superalloys was analyzed.It was established that the corrosion mechanism of these nickel-based single-crystal superalloys predominantly involves a cyclic process of oxide layer formation and decomposition,ultimately resulting in the establishment of a protective layer principally composed of NiO,with a constantly regenerating Al2O3 barrier,impeding further alloy degradation.Furthermore,the inclusion of elements such as Cr,Al,Ta,and notably Re has been found to markedly improve the thermal corrosion resistance of the superalloys.These insights not only enhance our comprehension of the corrosion mechanisms pertinent to nickel-based superalloys,but also provide strategic directions for alloy composition refinement aimed at bolstering their corrosion resilience.