N-(4-Hydroxyphenylmethylene)-1-naphthylamine was synthesized by the solid phase reaction of 1-naphthylamine and 4-hydroxybenzaldehyde at room temperature. The reaction was completed in 15 min in yield of 95%. The prod...N-(4-Hydroxyphenylmethylene)-1-naphthylamine was synthesized by the solid phase reaction of 1-naphthylamine and 4-hydroxybenzaldehyde at room temperature. The reaction was completed in 15 min in yield of 95%. The product was characterized by elemental analysis, IR, X-ray powder diffractometry and 1H NMR. The crystal as determined by X-ray single crystal diffractometry belongs to monoclinic system with space group P2 1/c, a=1.004 9(2), b=1.047 3(2), c=1.200 2(2) nm, β=92.60(3)°, V= 1.261 8(4) nm 3, D c=1.302 g/cm 3, Z=4, F(000)=528, μ=0.081 mm -1, R=0.0375, wR=0.106 2, S=1.024.展开更多
N-(4-hydroxy-3-methoxyphenylmethylene)-p-methoxyaniline(C15H15NO3) was synthesized by the one step solid phase reactions of p-methoxyaniline with vanillin at room temperature without solvent.The reaction was completed...N-(4-hydroxy-3-methoxyphenylmethylene)-p-methoxyaniline(C15H15NO3) was synthesized by the one step solid phase reactions of p-methoxyaniline with vanillin at room temperature without solvent.The reaction was completed in 15 min and the yield was 93%.The product was characterized by elemental analysis,X-ray powder diffraction,IR and 1H NMR.展开更多
合成了N-［(2-羟基-5-甲基苯)（苯基）］亚甲基邻苯二胺，晶体属单斜晶系，空 间群P21/c. 晶胞参数 a = 1.034 0(6) nm， b =1.092 0(3) nm， c =1.472 0(4) nm, β = 107.89(3)°, 化学式C20H18N2O, M r =302.36， Z =4, V =1.581 ...合成了N-［(2-羟基-5-甲基苯)（苯基）］亚甲基邻苯二胺，晶体属单斜晶系，空 间群P21/c. 晶胞参数 a = 1.034 0(6) nm， b =1.092 0(3) nm， c =1.472 0(4) nm, β = 107.89(3)°, 化学式C20H18N2O, M r =302.36， Z =4, V =1.581 7(10) nm3 ， D c = 1.268 g/cm3， F （000）= 160，最终偏离因子 R1 = 0.054 1. 结构分析表明，分子间以氢键形成二聚体，二聚体 的分子间互为中心对称. 循环伏安法表明标题化合物的电极反应是一个不可逆的单电子传荷 过程.展开更多
Terpolymers of N-p-tolylmaleimide(NPTMI), methyl methacrylate(MMA) and acrylonitrile(AN) were synthesized by emulsion polymerization. The thermal properties of the terpolymers were investigated by torsional braid anal...Terpolymers of N-p-tolylmaleimide(NPTMI), methyl methacrylate(MMA) and acrylonitrile(AN) were synthesized by emulsion polymerization. The thermal properties of the terpolymers were investigated by torsional braid analysis, differential scanning calorimetry, thermogravimetric analysis and vicat softening point tester. The results showed that the glass transition temperature(T g) and vicat softening point of the terpolymers increased with the increase of NPTMI content but decreased with the increase of AN content. The initial decomposition temperature(T 0) and the half weight-loss temperature(T 50 ) increased both with increasing NPTMI and AN content. The weight and number average molecular weights were also determined by gel permeation chromatography. The results showed that there was a maximum value at mass ratio 10∶85∶5 of NPTMI/MMA/AN.展开更多
N-(p-hydroxyphenyl)methacrylamide was successfully synthesized(yield 86%) by the reaction of methacryloyl chloride with p-aminophenol.The separating and purifying methods of the product was discussed,and the influenci...N-(p-hydroxyphenyl)methacrylamide was successfully synthesized(yield 86%) by the reaction of methacryloyl chloride with p-aminophenol.The separating and purifying methods of the product was discussed,and the influencing factors on the synthesis were simply explored.The aim product was characterized and verified by FT-IR,1H NMR,MS spectra and elemental analysis.展开更多
文摘N-(4-Hydroxyphenylmethylene)-1-naphthylamine was synthesized by the solid phase reaction of 1-naphthylamine and 4-hydroxybenzaldehyde at room temperature. The reaction was completed in 15 min in yield of 95%. The product was characterized by elemental analysis, IR, X-ray powder diffractometry and 1H NMR. The crystal as determined by X-ray single crystal diffractometry belongs to monoclinic system with space group P2 1/c, a=1.004 9(2), b=1.047 3(2), c=1.200 2(2) nm, β=92.60(3)°, V= 1.261 8(4) nm 3, D c=1.302 g/cm 3, Z=4, F(000)=528, μ=0.081 mm -1, R=0.0375, wR=0.106 2, S=1.024.
文摘N-(4-hydroxy-3-methoxyphenylmethylene)-p-methoxyaniline(C15H15NO3) was synthesized by the one step solid phase reactions of p-methoxyaniline with vanillin at room temperature without solvent.The reaction was completed in 15 min and the yield was 93%.The product was characterized by elemental analysis,X-ray powder diffraction,IR and 1H NMR.
文摘合成了N-［(2-羟基-5-甲基苯)（苯基）］亚甲基邻苯二胺，晶体属单斜晶系，空 间群P21/c. 晶胞参数 a = 1.034 0(6) nm， b =1.092 0(3) nm， c =1.472 0(4) nm, β = 107.89(3)°, 化学式C20H18N2O, M r =302.36， Z =4, V =1.581 7(10) nm3 ， D c = 1.268 g/cm3， F （000）= 160，最终偏离因子 R1 = 0.054 1. 结构分析表明，分子间以氢键形成二聚体，二聚体 的分子间互为中心对称. 循环伏安法表明标题化合物的电极反应是一个不可逆的单电子传荷 过程.
文摘Terpolymers of N-p-tolylmaleimide(NPTMI), methyl methacrylate(MMA) and acrylonitrile(AN) were synthesized by emulsion polymerization. The thermal properties of the terpolymers were investigated by torsional braid analysis, differential scanning calorimetry, thermogravimetric analysis and vicat softening point tester. The results showed that the glass transition temperature(T g) and vicat softening point of the terpolymers increased with the increase of NPTMI content but decreased with the increase of AN content. The initial decomposition temperature(T 0) and the half weight-loss temperature(T 50 ) increased both with increasing NPTMI and AN content. The weight and number average molecular weights were also determined by gel permeation chromatography. The results showed that there was a maximum value at mass ratio 10∶85∶5 of NPTMI/MMA/AN.
文摘N-(p-hydroxyphenyl)methacrylamide was successfully synthesized(yield 86%) by the reaction of methacryloyl chloride with p-aminophenol.The separating and purifying methods of the product was discussed,and the influencing factors on the synthesis were simply explored.The aim product was characterized and verified by FT-IR,1H NMR,MS spectra and elemental analysis.