Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part i...Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.展开更多
Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nano...Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nanocrystalline is in the range of 10\20 nm, the mean size is 16 nm.展开更多
Magnesium oxysulfate （MgSO4·5Mg（OH）2·2H2O） flake powders with an average diameter of 2 ~tm and a thickness of 0.052 μm were prepared using magnesium sulfate and sodium hydroxide as raw materials by hydr...Magnesium oxysulfate （MgSO4·5Mg（OH）2·2H2O） flake powders with an average diameter of 2 ~tm and a thickness of 0.052 μm were prepared using magnesium sulfate and sodium hydroxide as raw materials by hydrothermal synthesis process. The composition, morphology and structural features of the hydrothermal products were examined with X-ray powder diffraction （XRD）, scanning electron microscopy （SEM） and Fourier transform infrared spectroscopy （FTIR）. The experimental results indicate that in the conditions of n（NaOH）/n（MgSO4） of 1.25, the dosage of w（Na3PO4） crystal additives of 1.0% w（MgSO4）, stirring for 5 h at 180 ℃, the morphology of MgSO4·5Mg（OH）2·2H2O products is flaky and laminar, which is a kind of complex magnesium singlecrystal. The recycling of MgSO4 mother liquor was also investigated to make a full use of the materials and reduce disposal. The results prove that there is no adverse effect on the yield and purity of the products.展开更多
文摘Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.
文摘Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nanocrystalline is in the range of 10\20 nm, the mean size is 16 nm.
基金Project(50704036) supported by the National Natural Science Foundation of ChinaProject(08JJ3027) supported by the Natural Science Foundation of Hunan Province, China
文摘Magnesium oxysulfate （MgSO4·5Mg（OH）2·2H2O） flake powders with an average diameter of 2 ~tm and a thickness of 0.052 μm were prepared using magnesium sulfate and sodium hydroxide as raw materials by hydrothermal synthesis process. The composition, morphology and structural features of the hydrothermal products were examined with X-ray powder diffraction （XRD）, scanning electron microscopy （SEM） and Fourier transform infrared spectroscopy （FTIR）. The experimental results indicate that in the conditions of n（NaOH）/n（MgSO4） of 1.25, the dosage of w（Na3PO4） crystal additives of 1.0% w（MgSO4）, stirring for 5 h at 180 ℃, the morphology of MgSO4·5Mg（OH）2·2H2O products is flaky and laminar, which is a kind of complex magnesium singlecrystal. The recycling of MgSO4 mother liquor was also investigated to make a full use of the materials and reduce disposal. The results prove that there is no adverse effect on the yield and purity of the products.