The compound reacts with 2-(Methylthio)thiophene (C5H6S2) while refluxing in xylene to afford a methylthio-tetramanganese product 4, in which C5H6S2 is cleaved with loss of thiophene. The crystal structure of 4 has be...The compound reacts with 2-(Methylthio)thiophene (C5H6S2) while refluxing in xylene to afford a methylthio-tetramanganese product 4, in which C5H6S2 is cleaved with loss of thiophene. The crystal structure of 4 has been studied by direct method. Based on the 21 685 unique reflections collected using MoKα of X-ray radiation and a CCD-based detector, it is refined to an agreement index (R1) of 0.079 0. The cell is triclinic with dimensions: a=1.719 49 nm, b=1.959 2 nm, c=2.632 6 nm and α=79.733°, β=71.407°, γ=89.387°. There are 12 unit cells of 4 in the cell, with space group P1.展开更多
为提高锂硫电池的循环性能,采用水热法制备负载有硫化锰（MnS）的竹炭（BC）复合材料MnS@BC,通过热复合获得负载S的BC复合材料S-BC和负载S、MnS的BC复合材料S-MnS@BC。SEM和XRD分析表明：MnS@BC中MnS可填充BC表面的孔洞,并呈不均匀分布...为提高锂硫电池的循环性能,采用水热法制备负载有硫化锰（MnS）的竹炭（BC）复合材料MnS@BC,通过热复合获得负载S的BC复合材料S-BC和负载S、MnS的BC复合材料S-MnS@BC。SEM和XRD分析表明：MnS@BC中MnS可填充BC表面的孔洞,并呈不均匀分布;没有出现MnS的衍射峰。电化学性能测试结果表明：负载于BC上的MnS本身没有电化学活性,但对多硫离子的氧化还原过程有催化作用,可提高电极的可逆性。S-MnS@BC复合材料电极以100 m A/g的电流在1.5~3.0 V充放电,首次放电比容量为1 346.1 m Ah/g,第50次循环的放电比容量保持在504.0 m Ah/g,在同等条件下的性能好于S-BC复合材料,表现出较轻的“飞梭效应”和较好的循环性能。展开更多
采用MIG焊焊接超高强钢35Cr Mn Si A,对热处理前后焊接接头组织进行分析,并对热处理后焊接接头进行了硬度测试、拉伸试验、冲击试验及断口分析,从而研究分析了35Cr Mn Si A的焊接性。结果表明:焊态下,焊缝区组织为针状马氏体和少量残余...采用MIG焊焊接超高强钢35Cr Mn Si A,对热处理前后焊接接头组织进行分析,并对热处理后焊接接头进行了硬度测试、拉伸试验、冲击试验及断口分析,从而研究分析了35Cr Mn Si A的焊接性。结果表明:焊态下,焊缝区组织为针状马氏体和少量残余奥氏体,热影响区组织为板条状马氏体、贝氏体和残余奥氏体;热处理后,焊缝组织为回火马氏体和残余奥氏体,热影响区组织为回火马氏体、少量贝氏体和残余奥氏体;焊接接头焊缝区的硬度高于热影响区和母材;焊接接头抗拉强度为1640.8 MPa,伸长率为9.2%,焊缝区冲击功为37.6 J,焊缝区的冲击断口为混合断口。展开更多
基于有限元分析软件ABAQUS开展了30Cr Mn Si A合金钢正交切削有限元仿真研究,分析了该材料切削过程中塑性变形区分布及内应力分布。通过调整刀具前角及主轴转速分别研究了刀具前角和主轴转速对切削力的影响规律,得到刀具最佳前角为13...基于有限元分析软件ABAQUS开展了30Cr Mn Si A合金钢正交切削有限元仿真研究,分析了该材料切削过程中塑性变形区分布及内应力分布。通过调整刀具前角及主轴转速分别研究了刀具前角和主轴转速对切削力的影响规律,得到刀具最佳前角为13°,临界主轴转速为2000r/min。展开更多
文摘The compound reacts with 2-(Methylthio)thiophene (C5H6S2) while refluxing in xylene to afford a methylthio-tetramanganese product 4, in which C5H6S2 is cleaved with loss of thiophene. The crystal structure of 4 has been studied by direct method. Based on the 21 685 unique reflections collected using MoKα of X-ray radiation and a CCD-based detector, it is refined to an agreement index (R1) of 0.079 0. The cell is triclinic with dimensions: a=1.719 49 nm, b=1.959 2 nm, c=2.632 6 nm and α=79.733°, β=71.407°, γ=89.387°. There are 12 unit cells of 4 in the cell, with space group P1.
文摘为提高锂硫电池的循环性能,采用水热法制备负载有硫化锰（MnS）的竹炭（BC）复合材料MnS@BC,通过热复合获得负载S的BC复合材料S-BC和负载S、MnS的BC复合材料S-MnS@BC。SEM和XRD分析表明：MnS@BC中MnS可填充BC表面的孔洞,并呈不均匀分布;没有出现MnS的衍射峰。电化学性能测试结果表明：负载于BC上的MnS本身没有电化学活性,但对多硫离子的氧化还原过程有催化作用,可提高电极的可逆性。S-MnS@BC复合材料电极以100 m A/g的电流在1.5~3.0 V充放电,首次放电比容量为1 346.1 m Ah/g,第50次循环的放电比容量保持在504.0 m Ah/g,在同等条件下的性能好于S-BC复合材料,表现出较轻的“飞梭效应”和较好的循环性能。
文摘采用MIG焊焊接超高强钢35Cr Mn Si A,对热处理前后焊接接头组织进行分析,并对热处理后焊接接头进行了硬度测试、拉伸试验、冲击试验及断口分析,从而研究分析了35Cr Mn Si A的焊接性。结果表明:焊态下,焊缝区组织为针状马氏体和少量残余奥氏体,热影响区组织为板条状马氏体、贝氏体和残余奥氏体;热处理后,焊缝组织为回火马氏体和残余奥氏体,热影响区组织为回火马氏体、少量贝氏体和残余奥氏体;焊接接头焊缝区的硬度高于热影响区和母材;焊接接头抗拉强度为1640.8 MPa,伸长率为9.2%,焊缝区冲击功为37.6 J,焊缝区的冲击断口为混合断口。