The co-precipitation derived LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 cathode material was modified by a coating layer of TiP_2O_7 through an ethanol-based process. The TiP_2O_7-coated LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 is charac...The co-precipitation derived LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 cathode material was modified by a coating layer of TiP_2O_7 through an ethanol-based process. The TiP_2O_7-coated LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 is characterized by Xray diffraction analysis, scanning electron microscopy and transmission electron microscopy to investigate the microstructure and morphology. The differential scanning calorimetry was employed to confirm the improved thermal stability. The electrochemical properties were evaluated by the constant-current charge/discharge tests. The TiP_2O_7 coating layer is effectively suppressing the structural degradation and ameliorating the surface status of LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 particles, and the intrinsic rhombohedral layered structure of TiP_2O_7-coated LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 was well maintained during the long-term cycling process, while the surface structure of pristine LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 was degraded from rhombohedral R3 m layered structure to cubic rock-salt structure. The charged state Ni^(4+) ions will easily transform into Ni^(2+) when the electrolytes oxidized at the interface of cathode/electrolytes and formed the cubic rock-salt NiO type structure, and the cubic rock-salt structure without electrochemical activity on the surface of LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 particles will finally accelerate capacity fading. The thermal stability and cyclic performances of the LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 electrode were remarkably improved by TiP_2O_7 coating, the total amount of heat release corresponding to the intensity of thermal runaway were 1075.5 and 964.6 J/g for pristine LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 and TiP_2O_7-coated LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 respectively, the pouch shaped full cells that employed TiP 2 O7-coated LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 as cathode were able to perform more than 2200 cycles at 25 ℃ and more than 1000 cycles at 45 ℃ before the capacity retention fading to 80%.展开更多
基金supported by the National Natural Science Foundation of China (No. 51372178)the Natural Science Foundation for Distinguished Young Scholars of Hubei Province of China (No. 2013CFA021)
文摘The co-precipitation derived LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 cathode material was modified by a coating layer of TiP_2O_7 through an ethanol-based process. The TiP_2O_7-coated LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 is characterized by Xray diffraction analysis, scanning electron microscopy and transmission electron microscopy to investigate the microstructure and morphology. The differential scanning calorimetry was employed to confirm the improved thermal stability. The electrochemical properties were evaluated by the constant-current charge/discharge tests. The TiP_2O_7 coating layer is effectively suppressing the structural degradation and ameliorating the surface status of LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 particles, and the intrinsic rhombohedral layered structure of TiP_2O_7-coated LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 was well maintained during the long-term cycling process, while the surface structure of pristine LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 was degraded from rhombohedral R3 m layered structure to cubic rock-salt structure. The charged state Ni^(4+) ions will easily transform into Ni^(2+) when the electrolytes oxidized at the interface of cathode/electrolytes and formed the cubic rock-salt NiO type structure, and the cubic rock-salt structure without electrochemical activity on the surface of LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 particles will finally accelerate capacity fading. The thermal stability and cyclic performances of the LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 electrode were remarkably improved by TiP_2O_7 coating, the total amount of heat release corresponding to the intensity of thermal runaway were 1075.5 and 964.6 J/g for pristine LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 and TiP_2O_7-coated LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 respectively, the pouch shaped full cells that employed TiP 2 O7-coated LiNi_(0.8)Co_(0.15)Al_(0.05)O_2 as cathode were able to perform more than 2200 cycles at 25 ℃ and more than 1000 cycles at 45 ℃ before the capacity retention fading to 80%.
文摘采用共沉淀-高温固相法在氧气气氛下合成球形Li Ni0.8Co0.15Al0.05O2正极材料。通过XRD、SEM、恒电流充放电测试和交流阻抗测试等手段分析了氧化铝、氢氧化铝和异丙醇铝三种铝源对合成材料的结构、形貌以及电化学性能的影响。结果表明,以三种不同铝源所合成的正极材料均具有良好的层状结构。用异丙醇铝合成的正极材料具有最小的一次颗粒,球型度较好,具有优异的电化学性能,在0.2 C下首次放电比容量为189.22 m Ah/g,50次循环后容量保持率为84.2%。然后,通过EIS测试分析了不同铝源对合成材料性能影响的原因。
