A nanosolid heteropoly acid of H 3PW 12 O 40 /SiO 2 was prepared with the sol-gel method and used to catalyze sythesis of methyl 5-amino-1,2,4,-trazolylformate sulfate.The structure of the nanosolid heteropoly acid H ...A nanosolid heteropoly acid of H 3PW 12 O 40 /SiO 2 was prepared with the sol-gel method and used to catalyze sythesis of methyl 5-amino-1,2,4,-trazolylformate sulfate.The structure of the nanosolid heteropoly acid H 3PW 12 O 40 /SiO 2 was characterized by IR,XRD and TEM.The following optimum condition were that the mole ratio of alcohol to carboxylic acid is 27∶1,the temperature is 75℃,the reaction time is 5 hours,and the catalyst is 2 5% of feedstock.Under the optimum conditions,the yield of esters was above 94%.展开更多
The title compound H2SiW12O40·(CH3)2NH was synthesized in mixed solvent of aqueous and acetonitrile, and its crystal structure had been determined using single crystal X ray diffraction. The crystal belongs to mo...The title compound H2SiW12O40·(CH3)2NH was synthesized in mixed solvent of aqueous and acetonitrile, and its crystal structure had been determined using single crystal X ray diffraction. The crystal belongs to monoclinic, space group C2/m, a=2.0654(4)nm, b=1.3306(3)nm, c=1.3194(3)nm, β=119.59(3)°, V=3.1531(11)nm3, Dc=3.606Mg·m-3, Z=2, R=0.0462, Rw=0.0836. The title compound comprises of a 2+ unit, a polyanion and a free (CH3)2NH molecule. The ESR spectrum of the title compound shows that charge transfer between organic groups and polyanion takes place under irradiation of the sunlight in solid state. The TG study of the title compound shows that it had four stages of the weight loss, and the increase of the decomposition temperature for the polyanion shows that the stability of the polyanion was enhanced due to the influence of Zn2+ ion. CCDC:175866.展开更多
Using a reversed-phase microemulsion polymerization method, polyoxometalates(POMs) CoW 11Ti loaded starch nanoparticles were prepared and structurally characterized by elemental analyses, IR, UV-Vis and ESR spectrosco...Using a reversed-phase microemulsion polymerization method, polyoxometalates(POMs) CoW 11Ti loaded starch nanoparticles were prepared and structurally characterized by elemental analyses, IR, UV-Vis and ESR spectroscopy. The particle size of CoW 11Ti/starch was estimated by transmission electron microscope(TEM) and the size ranges by a 1000HSA MALVIRN Zetasizer instrument. The result shows that the polyoxometalate retained the parent structure after encapsulated by starch microspheres, which are able to enhance the stability and antitumoral activity of POMs and decrease the toxicity of POMs as well.展开更多
基金supported by the National Key Basic Research Program of China(973)(2010CB226903)National Natural Science Foundation of China(21073147,21303140)Program for Changjiang Scholars and Innovative Research Team in University,China(IRT1036)~~
文摘A nanosolid heteropoly acid of H 3PW 12 O 40 /SiO 2 was prepared with the sol-gel method and used to catalyze sythesis of methyl 5-amino-1,2,4,-trazolylformate sulfate.The structure of the nanosolid heteropoly acid H 3PW 12 O 40 /SiO 2 was characterized by IR,XRD and TEM.The following optimum condition were that the mole ratio of alcohol to carboxylic acid is 27∶1,the temperature is 75℃,the reaction time is 5 hours,and the catalyst is 2 5% of feedstock.Under the optimum conditions,the yield of esters was above 94%.
文摘The title compound H2SiW12O40·(CH3)2NH was synthesized in mixed solvent of aqueous and acetonitrile, and its crystal structure had been determined using single crystal X ray diffraction. The crystal belongs to monoclinic, space group C2/m, a=2.0654(4)nm, b=1.3306(3)nm, c=1.3194(3)nm, β=119.59(3)°, V=3.1531(11)nm3, Dc=3.606Mg·m-3, Z=2, R=0.0462, Rw=0.0836. The title compound comprises of a 2+ unit, a polyanion and a free (CH3)2NH molecule. The ESR spectrum of the title compound shows that charge transfer between organic groups and polyanion takes place under irradiation of the sunlight in solid state. The TG study of the title compound shows that it had four stages of the weight loss, and the increase of the decomposition temperature for the polyanion shows that the stability of the polyanion was enhanced due to the influence of Zn2+ ion. CCDC:175866.
文摘Using a reversed-phase microemulsion polymerization method, polyoxometalates(POMs) CoW 11Ti loaded starch nanoparticles were prepared and structurally characterized by elemental analyses, IR, UV-Vis and ESR spectroscopy. The particle size of CoW 11Ti/starch was estimated by transmission electron microscope(TEM) and the size ranges by a 1000HSA MALVIRN Zetasizer instrument. The result shows that the polyoxometalate retained the parent structure after encapsulated by starch microspheres, which are able to enhance the stability and antitumoral activity of POMs and decrease the toxicity of POMs as well.