The synthesis of high purity intermetallic FeAI nanoparticles using the flow-levitation （FL） method was reported. Iron and aluminium droplets were levitated stably at about 2 230℃. The morphology, clystal structure...The synthesis of high purity intermetallic FeAI nanoparticles using the flow-levitation （FL） method was reported. Iron and aluminium droplets were levitated stably at about 2 230℃. The morphology, clystal structure and chemical composition of FeAI nanoparticles were investigated by transmission electron microscopy （TEM）, high-resolution TEM, X-ray diffraction and energy dispersive spectrometry. The results show that the average particle size of these nanoparticles is about 34.5 nm. Measurements of the d-spacing from X-ray diffraction and electron diffraction studies confirm that the intermetallic nanoparticles have the same crystal structure （B2） as the bulk FeA1. A thin oxidation coating is formed around the particles when being exposed to air. Based on the XPS measurements, the surface coating of the FeAI nanoparticles is composed of Fe2O3 and FeAl2O4. Besides, hysteresis curve reveals that saturation magnetization （Ms） of FeA1 is 1.66 A/m2, and the coercivity is about 1.214×10^3 A/re.展开更多
基金Project(10804101) supported by the National Natural Science Foundation of China
文摘The synthesis of high purity intermetallic FeAI nanoparticles using the flow-levitation （FL） method was reported. Iron and aluminium droplets were levitated stably at about 2 230℃. The morphology, clystal structure and chemical composition of FeAI nanoparticles were investigated by transmission electron microscopy （TEM）, high-resolution TEM, X-ray diffraction and energy dispersive spectrometry. The results show that the average particle size of these nanoparticles is about 34.5 nm. Measurements of the d-spacing from X-ray diffraction and electron diffraction studies confirm that the intermetallic nanoparticles have the same crystal structure （B2） as the bulk FeA1. A thin oxidation coating is formed around the particles when being exposed to air. Based on the XPS measurements, the surface coating of the FeAI nanoparticles is composed of Fe2O3 and FeAl2O4. Besides, hysteresis curve reveals that saturation magnetization （Ms） of FeA1 is 1.66 A/m2, and the coercivity is about 1.214×10^3 A/re.