To enhance the overall performance of cyclotrimethylenetrinitramine(RDX),a modification strategy for RDX via in situ coordination with monometallic polydopamine(PDA)coatings(PDA-Fe,PDA-Cu,and PDA-Pb)was developed.The ...To enhance the overall performance of cyclotrimethylenetrinitramine(RDX),a modification strategy for RDX via in situ coordination with monometallic polydopamine(PDA)coatings(PDA-Fe,PDA-Cu,and PDA-Pb)was developed.The thermal properties of pristine RDX and its modified variants(RDX@PDA-Fe,RDX@PDA-Cu,RDX@PDA-Pb)were characterized using differential scanning calorimetry(DSC)and accelerating rate calorimetry(ARC).The impact sensitivity of these materials was evaluated via the characteristic drop-height method.The results demonstrate that PDA-metal metal coatings—formed through coordination between PDA and single metal ions(Fe^(3+),Cu^(2+),or Pb^(2+))—significantly enhance RDX′s thermal stability while attenuating its mechanical sensitivity.These coatings act as energy-absorbing barriers against external stimuli,effectively mitigating RDX′s sensitivity.Furthermore,they elevate RDX′s thermal stability by increasing its decomposition onset temperature and accelerating its decomposition kinetics.The monometallic coatings also catalyze RDX′s thermal decomposition and combustion,with Cu and Pb exhibiting particularly distinct catalytic effects.展开更多
Continuous carbon fiber reinforced silicon carbide(C/SiC)composites are often subjected to low-velocity impacts when utilized as structural materials for thermal protection.However,research on in-plane impact damage a...Continuous carbon fiber reinforced silicon carbide(C/SiC)composites are often subjected to low-velocity impacts when utilized as structural materials for thermal protection.However,research on in-plane impact damage and multiple impact damage of C/SiC composites is limited.To investigate the in-plane impact damage behavior of C/SiC composites,a drop-weight impact test method was developed for strip samples,and these results were subsequently compared with those of C/SiC composite plates.Results show that the in-plane impact behavior of C/SiC strip samples is similar to that of C/SiC composite plates.Variation of the impact load with displacement is characterized by three stages:a nearly linear stage,a severe load drop stage,and a rebound stage where displacement occurs after the impact energy exceeds its peak value.Impact damage behavior under single and multiple impacts on 2D plain and 3D needled C/SiC composites was investigated at different impact energies and durations.Crack propagation in C/SiC composites was studied by computerized tomography(CT)technique.In the 2D plain C/SiC composite,load propagation between layers is hindered during impact,leading to delamination and 90°fiber brittle fracture.The crack length perpendicular to the impact direction increases with impact energy increases,resulting in more serious 0°fiber fracture and a larger area of fiber loss.In the 3D needled C/SiC composite,load propagates between the layers during impact through the connection of needled fibers.The fibers continue to provide substantial structural support,with notable instances of fiber pull-off and debonding.Consequently,the impact resistance is superior to that of 2D plain C/SiC composite.When the 3D needled C/SiC composite undergoes two successive impacts of 1.5 J,the energy absorption efficiency of the second impact is significantly lower,accompanied by a smaller impact displacement.Moreover,the total energy absorption efficiency of these two impacts of 1.5 J is lower than that of a single 3.0 J impact.展开更多
The rising concern over electromagnetic (EM) pollution is re-sponsible for the rapid progress in EM interference (EMI) shielding and EM wave absorption in the last few years, and carbon materials with a large sur-face...The rising concern over electromagnetic (EM) pollution is re-sponsible for the rapid progress in EM interference (EMI) shielding and EM wave absorption in the last few years, and carbon materials with a large sur-face area and high porosity have been investigated. Compared to other car-bon materials, biomass-derived carbon (BC) are considered efficient and eco-friendly materials for this purpose. We summarize the recent advances in BC materials for both EMI shielding and EM wave absorption. After a brief overview of the synthesis strategies of BC materials and a precise out-line of EM wave interference, strategies for improving their EMI shielding and EM wave absorption are discussed. Finally, the existing challenges and the future prospects for such materials are briefly summarized.展开更多
Plant roots are widely known to provide mechanical reinforcement to soils against shearing and further increase slope stability.However,whether roots provide reinforcement to loess cyclic re-sistance and how various f...Plant roots are widely known to provide mechanical reinforcement to soils against shearing and further increase slope stability.However,whether roots provide reinforcement to loess cyclic re-sistance and how various factors affect roots reinforcement during seismic loading have rarely been studied.The objective is to conduct a series of cyclic direct simple shear tests and DEM numerical simulation to investigate the cyclic behaviour of rooted loess.The effects of initial static shear stress and loading frequency on the cyclic resistance of root-soil composites were first investigated.After that,cyclic direct simple shear simulations at constant volume were carried out based on the discrete element method(PFC^(3D))to investigate the effects of root geome-try,mechanical traits and root-soil bond strength on the cyclic strength of rooted loess.It was discovered that the roots could effectively improve the cyclic resistance of loess.The cyclic resistance of the root-soil composite decreases with the increase of the initial shear stress,then increases,and improves with the increase of the frequency.The simulation result show that increases in root elastic modulus and root-soil interfacial bond strength can all enhance the cyclic resistance of root-soil composites,and the maximum cyclic resistance of the root-soil composite was obtained when the initial inclination angle of the root system was 90°.展开更多
In a high heat flux ablative environment,the surface temperature of aircraft rises rapidly,leading to traditional high thermal conductivity materials being ineffective at protecting internal metal components.In this s...In a high heat flux ablative environment,the surface temperature of aircraft rises rapidly,leading to traditional high thermal conductivity materials being ineffective at protecting internal metal components.In this study,continuous carbon fiber reinforced Li_(2)O-Al_(2)O_(3)-SiO_(2)(C_(f)/LAS)glass ceramic composites doped with SiC particles(SiC_(p))were prepared by slurry immersion winding and hot pressing sintering.Effect of matrix crystallinity on ablative properties of the composites under ultra-high heat flux was investigated.By utilizing heat absorption and low thermal conductivity characteristics associated with SiO_(2)gasification within composite materials,both surface and internal temperatures of these materials are effectively reduced,thereby ensuring the safe operation of aircraft and electronic devices.Results indicate that the average linear ablation rate of composites doped with 10%(in mass)of SiC_(p)significantly decreases at a heat flux of 20 MW/m^(2).Transmission electron microscope observation reveals that the doped glass matrix exhibits increased crystallinity,reduced internal stress,and minimized lattice distortion,thereby enhancing the composites’high-temperature performance.However,excessive SiC_(p)doping leads to reduced crystallinity and deteriorated ablation performance.Ultimately,the average linear ablation rate of C_(f)/LAS composites with 10%(in mass)SiC_(p)at 20 MW/m^(2)heat flux is comparable to that of commercial carbon/carbon composites,accompanied by providing lower thermal conductivity and higher bending strength.This novel high-performance C_(f)/LAS composite is cost-effective,short-cycled,and suitable for mass production,offering promising potential for widespread application in ablation-resistant components of hypersonic vehicles.展开更多
Basalt fibers/7075 aluminum matrix composites were studied to meet the demand of aluminum alloy drill pipes for material wear resistance.The composites with different basalt fiber additions were prepared by hot presse...Basalt fibers/7075 aluminum matrix composites were studied to meet the demand of aluminum alloy drill pipes for material wear resistance.The composites with different basalt fiber additions were prepared by hot pressed sintering and hot extrusion.The mechanical properties as well as friction and wear properties of the composites were studied by microstructure analysis,tensile experiments,friction and wear experiments.The results showed that basalt fibers were oriented and uniformly distributed and led to local grain refinement in the alloy matrix.The hardness and elongation of the composites were improved.The friction coefficient of the composites increased and then decreased,and the maximum wear depth and wear amount decreased,then increased,then decreased again with the growth of basalt fiber addition.Meanwhile,the inclusion of basalt fibers mitigated the uneven wear of the extruded 7075 aluminum alloy.The value of wear depth difference of 7075-0.2BF was the smallest,and that of 7075-2.0BF was close to it.The maximum wear depth and wear volume the 7075-0.2BF and 7075-2.0BF were also the smallest.The inhibition of uneven wear by basalt fibers enhanced of wear resistance for 7075 aluminum alloy,which has reference significance for improving the performance of aluminum alloy drill pipes.展开更多
This study represents an important step forward in the domain of additive manufacturing of energetic materials.It presents the successful formulation and fabrication by 3D printing of gun propellants using Fused Depos...This study represents an important step forward in the domain of additive manufacturing of energetic materials.It presents the successful formulation and fabrication by 3D printing of gun propellants using Fused Deposition Modeling(FDM)technology,highlighting the immense potential of this innovative approach.The use of FDM additive manufacturing technology to print gun propellants is a significant advancement due to its novel application in this field,which has not been previously reported.Through this study,the potential of FDM 3D-printing in the production of high-performance energetic composites is demonstrated,and also a new standard for manufacturability in this field can be established.The thermoplastic composites developed in this study are characterized by a notably high energetic solids content,comprising 70%hexogen(RDX)and 10%nitrocellulose(NC),which surpasses the conventional limit of 60%energetic solids typically achieved in stereolithography and light-curing 3D printing methods.The primary objective of the study was to optimize the formulation,enhance performance,and establish an equilibrium between printability and propellant efficacy.Among the three energetic for-mulations developed for 3D printing feedstock,only two were suitable for printing via the FDM tech-nique.Notably,the formulation consisting of 70%RDX,10%NC,and 20%polycaprolactone(PCL)emerged as the most advantageous option for gun propellants,owing to its exceptional processability,ease of printability,and high energetic performance.展开更多
In order to obtain high-density dual-scale ceramic particles(8.5 wt.%SiC+1.5 wt.%TiC)reinforced Al-Mg Sc-Zr composites with uniform microstructure,50 nm TiC and 7μm SiC particles were pre-dispersed into 15−53μm alum...In order to obtain high-density dual-scale ceramic particles(8.5 wt.%SiC+1.5 wt.%TiC)reinforced Al-Mg Sc-Zr composites with uniform microstructure,50 nm TiC and 7μm SiC particles were pre-dispersed into 15−53μm aluminum alloy powders by low-speed ball milling and mechanical mixing technology,respectively.Then,the effects of laser energy density,power and scanning rate on the density of the composites were investigated based on selective laser melting(SLM)technology.The effect of micron-sized SiC and nano-sized TiC particles on solidification structure,mechanical properties and fracture behaviors of the composites was revealed and analyzed in detail.Interfacial reaction and phase variations in the composites with varying reinforced particles were emphatically considered.Results showed that SiC-TiC particles could significantly improve forming quality and density of the SLMed composites,and the optimal relative density was up to 100%.In the process of laser melting,a strong chemical reaction occurs between SiC and aluminum matrix,and micron-scale acicular Al_(4)SiC_(4) bands were formed in situ.There was no interfacial reaction between TiC particles and aluminum matrix.TiC/Al semi-coherent interface had good bonding strength.Pinning effect of TiC particles in grain boundaries could prevent the equiaxial crystals from growing and transforming into columnar crystals,resulting in grain refinement.The optimal ultimate tensile strength(UTS),yield strength(YS),elongation(EL)and elastic modulus of the SiC-TiC/Al-Mg-Sc-Zr composite were~394 MPa,~262 MPa,~8.2%and~86 GPa,respectively.The fracture behavior of the composites included ductile fracture of Al matrix and brittle cleavage fracture of Al_(4)SiC_(4) phases.A large number of cross-distributed acicular Al_(4)SiC_(4) bands were the main factors leading to premature failure and fracture of SiC-TiC/Al-Mg-Sc-Zr composites.展开更多
In the present study,two-layered stainless steel-copper composites with a thickness of 50μm were initially subjected to annealing at 800,900 and 1000℃for 5 min,respectively,to achieve diverse microstructural feature...In the present study,two-layered stainless steel-copper composites with a thickness of 50μm were initially subjected to annealing at 800,900 and 1000℃for 5 min,respectively,to achieve diverse microstructural features.Then the influence of annealing temperature on the formability of stainless steel-copper composites and the quality of micro composite cups manufactured by micro deep drawing(MDD)were investigated,and the underlying mechanism was analyzed.Three finite element(FE)models,including basic FE model,Voronoi FE model and surface morphological FE model,were developed to analyze the forming performance of stainless steel-copper composites during MDD.The results show that the stainless steel-copper composites annealed at 900℃possess the best plasticity owing to the homogeneous and refined microstructure in both stainless steel and copper matrixes,and the micro composite cup with specimen annealed at 900℃exhibits a uniform wall thickness as well as high surface quality with the fewest wrinkles.The results obtained from the surface morphological FE model considering material inhomogeneity and surface morphology of the composites are the closest to the experimental results compared to the basic and Voronoi FE model.During MDD process,the drawing forces decrease with increasing annealing temperature as a consequence of the strength reduction.展开更多
A composite explosive based on 1,3,5-trinitro-1,3,5-triazinane(RDX)was prepared by electrostaticspray method with dioctyl sebacate(DOS)as desensitizer.After preparation,the particle size and crystal structure were cha...A composite explosive based on 1,3,5-trinitro-1,3,5-triazinane(RDX)was prepared by electrostaticspray method with dioctyl sebacate(DOS)as desensitizer.After preparation,the particle size and crystal structure were characterized and chemical features,such as chemical bonds,functional groups,thermal decomposition parameters and mechanical sensitivity were investigated as well.In terms of the morphologies of the composites,the particle sizes were in the range of 1e3 mm.Compared with RDX,the crystal types,chemical bonds and functional groups of the RDX/DOS composites were unchanged.The activation energy of the composites was lower than that of raw RDX,and the 3wt%DOS composites had the lowest activation energy.The impact sensitivity and friction sensitivity of the RDX/DOS composites were lower than those of raw RDX,and the 10wt%DOS composites had the highest H50(125.9 cm)and the lowest friction sensitivity(8%).展开更多
Green composites made from bamboo fibers and biodegradable resins were fabricated with press molding.On the basis of the Weibull distribution and the weakest-link theory,the statistical strength and distribution of ba...Green composites made from bamboo fibers and biodegradable resins were fabricated with press molding.On the basis of the Weibull distribution and the weakest-link theory,the statistical strength and distribution of bamboo fiber were analyzed,and the tensile strength of green composites was also investigated.The result confirms that the tensile statistical strength of fiber fits well with two-parameter Weibull distribution.In addition,the tensile strength of bamboo fiber reinforced composites is about 330 MPa with the fiber volume fraction of 70%.This value is close to or higher than that of other natural fiber reinforced green composites.展开更多
In the present work, the surface characteristics of Electrical Discharge Machined (EDM) Al (6351)eSiC and Al (6351)eSiCeB4C composites are investigated. The composites are prepared by employing the conventional stir c...In the present work, the surface characteristics of Electrical Discharge Machined (EDM) Al (6351)eSiC and Al (6351)eSiCeB4C composites are investigated. The composites are prepared by employing the conventional stir casting technique, as it can produce better particle dispersion in the matrix. The detailed experimental study is performed on the composites by varying current (I), duty factor (t), pulse on time (Ton), and the gap voltage (V) in order to analyze the Heat Affected Zone (HAZ) formed in the sub surface and the average crater diameter formed on the machined surface of the composites as an output function. The formation of recast layers, presence of bubbles and the surface texture of the composites at various machining conditions are observed. The results show that the increased Metal Removal Rate (MRR) increases the depth of HAZ and the average crater diameter on the machined area. Further, the addition of B4C particles to the composite produces more surface defect than the AleSiC composite.展开更多
Effects of sintering temperature in hot pressing, t yp es, states and amounts of rare earth as well as TiH 2 on the transverse rupture strength (TRS) of Fe-based composites are studied by means of orthogonal test and ...Effects of sintering temperature in hot pressing, t yp es, states and amounts of rare earth as well as TiH 2 on the transverse rupture strength (TRS) of Fe-based composites are studied by means of orthogonal test and variance analysis in this paper. It is found that sintering temperature has a significant effect on the TRS of Fe-based diamond composites. The optimal sin tering temperature is 780～860 ℃. On the contrary, the effects of RE additi v es on values of TRS of the diamond composites have on distinct difference no mat ter the RE is in the state of mixture or compound or oxidization. Experimental r esults demonstrate that Fe-based diamond composites with RE additives exhibit h igher TRS, which results in an increase in diamond retention capacity. The degre e of increment of TRS is different at different sintering temperatures. The opti mal amount of rare earth was found to be about 1% in weight. The effect of RE is more significant at lower sintering temperature. The experimental results also reveal that TiH 2 additive has a negative effect on the TRS of Fe-based compos ites. Microscope observations demonstrate that specimen without TiH 2 additives , shows fewer pores and denser structures in the base metal. It can also be seen from the SEM observation of the resulting fracturing surface of bending test sp ecimens that the bonding of the diamond-matrix interface is better in the speci men without TiH 2 than in the specimen with TiH 2. Also the fracture surface o f the specimen without TiH 2 reveals ductile cup and cone behavior.展开更多
Polymer matrix composites(PMC)are extensively been used in many engineering applications.Various natural fibers have emerged as potential replacements to synthetic fibers as reinforcing materials composites owing to t...Polymer matrix composites(PMC)are extensively been used in many engineering applications.Various natural fibers have emerged as potential replacements to synthetic fibers as reinforcing materials composites owing to their fairly better mechanical properties,low cost,environment friendliness and biodegradability.Selection of appropriate constituents of composites for a particular application is a tedious task for a designer/engineer.Impact loading has emerged as the serious threat for the composites used in structural or secondary structural application and demands the usage of appropriate fiber and matrix combination to enhance the energy absorption and mitigate the failure.The objective of the present review is to explore the composite with various fiber and matrix combination used for impact applications,identify the gap in the literature and suggest the potential naturally available fiber and matrix combination of composites for future work in the field of impact loading.The novelty of the present study lies in exploring the combination of naturally available fiber and matrix combination which can help in better energy absorption and mitigate the failure when subjected to impact loading.In addition,the application of multi attributes decision making(MADM)tools is demonstrated for selection of fiber and matrix materials which can serve as a benchmark study for the researchers in future.展开更多
In this present work siliconized e-glass fibre reinforced epoxy resin composite has been prepared and compared with acid and base treated e-glass fibre epoxy composites to know the significant advantage of silane trea...In this present work siliconized e-glass fibre reinforced epoxy resin composite has been prepared and compared with acid and base treated e-glass fibre epoxy composites to know the significant advantage of silane treatment on fibre. The composites were fabricated by laying 20, 30 and 40vol% of e-glass fibre into epoxy resin matrix. The e-glass fibre woven mat was surface treated by an amine functional coupling agent 3-Aminopropyletrimethoxysilane(APTMS). The fibres were surface treated by aqueous solution method and thermo assisted to create silinol groups. Similarly for acid treatment H_2SO_4 and base treatment Na OH with 1N concentration was used for surface treating the fibres. Effectiveness of silane treatment on glass fibre was compared by inter laminar shear strength test according to ASTM D 2344.Drilling process with varying diameter drill bit and varying cutting speed was applied to check the composites for their delamination resistance while machining. Maximum improvement of 15%, 12.5% and9%(20, 30 and 40 vol %) on ILSS was achieved for siliconized e-glass fibre reinforced epoxy composites.The scanning electron microscopy images revealed that no fibre pull out was present on fractured surfaces of composites which contains siliconized e-glass fibre. Similarly better dimensional accuracy was achieved on drilling process for composites contains siliconized e-glass fibre.展开更多
The laminated glasses(LGs)composites are gaining popularity as protectivestructural material. Delamination strength(DS) of(LGs) with different inter-layers and their different nominal thicknesses were compared. The ef...The laminated glasses(LGs)composites are gaining popularity as protectivestructural material. Delamination strength(DS) of(LGs) with different inter-layers and their different nominal thicknesses were compared. The effect of inter-layer thickness, delamination load, and inter-layer type on DS is clearly observed from this brief study. It is concluded that inter-layer thickness has the significant role in determining the DS of LGs. The statistical analysis confirmed the strong association of DS with inter-layer thickness and the interlayer type. It was found that the LG-PVB composite has the comparatively lower DS than LG-EVA composite and inter-layer thickness has the prominent role in the determination of DS in the LG-EVAcomposite. There is an increment in DS with an increment in critical inter-layer thickness in both LG-EVA and LG-PVBcomposites. The increment in the inter-layer thickness from 0.38 mm to 0.76 mm increases DS significantly; whereas, the further increment in the inter-layer thickness to the higher value has a lesser effect. The finite element model was constituted(without considering the effect of temperature) for determining DS of LG composite. The simulation results were in a good match with experimental results. The results of the present work can be utilized by the design engineers while selecting LG for structural applications.展开更多
Carbon-based composites, including carbon reinforced composites and carbon-matrix composites, in defence technologies have raised a lot of attention due to its significant physical capabilities, superior thermal and m...Carbon-based composites, including carbon reinforced composites and carbon-matrix composites, in defence technologies have raised a lot of attention due to its significant physical capabilities, superior thermal and mechanical stability, and its eco-friendly nature. Carbon-based composite which incorporating with various carbonaceous materials such as coke, char, black carbon, activated carbon, carbon fibre and other carbon nanomaterials (carbon nanotubes, carbon nanofibres, graphene and graphite) are the greatest viable option for the development of advanced defence technologies. In this review article the characteristics of carbon-based materials and its composites are discussed for their distinct application in defence sectors;aeronautics, maritime, automotive, electronics, energy storage, electromagnetic interference (EMI) shielding and structures. The origin of carbonaceous materials and its production techniques were discussed. Carbon-based composites have a promising future in defence technology, particularly in chemical sensors, drug delivery agents, radar technologies, and nanocomposites due to their low cost, easy availability, flexibility in design and processing.展开更多
In this paper, turning experiments of machining particle reinforced metal matri x composites(PRMMCs) SiC p/Al with PCD tools have been carried out. The cutting force characteristics in ultrasonic vibration turning com...In this paper, turning experiments of machining particle reinforced metal matri x composites(PRMMCs) SiC p/Al with PCD tools have been carried out. The cutting force characteristics in ultrasonic vibration turning compared with that in com mon turning were studied. Through the single factor experiments and multiple fac tor orthogonal experiments, the influences of three kinds of cutting conditions such as cutting velocity, amount of feed and cutting depth on cutting force were analyzed in detail. Meanwhile, according to the experimental data, the empirica l formula of main cutting force in ultrasonic vibration turning was conclude d. According to the test results, the cutting force is direct proportion to cutt ing depth basically according to the relation between cutting force and other fa ctors, which is similar to that of common cutting, so is the feed rate, but the influence is not so big. The influence of cutting speed is larger than that of f eed rate on cutting force because the efficient cutting time increases in vibrat ion cycle with the increase of cutting speed, which causes cutting force to incr ease. The research results indicate: (1) Ultrasonic vibration turning possesses much lower main cutting force than that in common turning when adopting smaller cutting parameters. If using larger cutting parameters, the difference will inco nspicuous. (2) There are remarkable differences of cutting force-cutting veloci ty characteristics in ultrasonic vibration turning from that in common turning m ainly because built-up edge does not emerge in ultrasonic turning unlike common turning in corresponding velocity range. (3) In ultrasonic vibration cutting, t he influence of cutting velocity on cutting force is most obvious among thre e cutting parameters and the influence of feed is smallest. So adopting lower cu tting velocity and larger cutting depth not only can reduce cutting force effect ively but also can ensure cutting efficiency. (4) The conclusions are useful in precision and super precision manufacturing thin-wall pieces.展开更多
This paper summarizes the authors’ experimental study on the characterization system of composite behavior to withstand impact. The content includes: (1)The dent depth is the best parameter describing the impact dama...This paper summarizes the authors’ experimental study on the characterization system of composite behavior to withstand impact. The content includes: (1)The dent depth is the best parameter describing the impact damage state. (2) There exists the knee point phenomenon for damage resistance behavior (i.e. the relationship between impact energy or contact force and dent depth) and damage tolerance behavior (i.e. the relationship between dent depth and compressive failure strain or stress) of composite laminates. (3) The physical meaning of the knee point phenomenon is that the failure mechanisms change of damaged composites to fiber breakage in the first front plies from matrix crack and delamination. Some suggestions on the characterization system of composite behavior to withstand impact were proposed.展开更多
The densification rate of C/C composites fabricated by directional flow thermal gradient chemical vapor infiltration process from C 3H 6, C 3H 6 N 2 and C 3H 6 H 2 was investigated respectively. The mechanism on the r...The densification rate of C/C composites fabricated by directional flow thermal gradient chemical vapor infiltration process from C 3H 6, C 3H 6 N 2 and C 3H 6 H 2 was investigated respectively. The mechanism on the role of carrier gas in chemical vapor infiltration was also discussed. The results shows that whether or not adding N 2 as carrier gas has little influences on the densification behavior of C/C composites with the controlled temperature, the partial pressure of hydrocarbon and the effective residence time of the gas phase remain constant. When the controlled temperature is not less than 1 173 K,using N 2 or H 2 as carrier gas makes pronounced differences in densifying of C/C composites. The average bulk density of C/C composites from C 3H 6 H 2 is eight to ten percent higher than that from C 3H 6 N 2. However, when the controlled temperature is not higher than 1 123 K,the densification rate of C/C composites from C 3H 6 H 2 is much lower than that from C 3H 6 N 2, which implies that effects of carrier gas on densification of C/C composites are closely related to the type of carrier gas and infiltration temperature. At higher temperature, using H 2 as carrier gas is favorable to the densification of C/C composites, while at lower temperature, hydrogen, acting as reactive gas, can inhibit the formation of pyrolytic carbon.展开更多
基金National Natural Science Foundation of China(No.22405249)Open Project of Key Laboratory of Rubber Research Institute,Chinese Academy of Tropical Agricultural Science in 2025(No.RRI-KLOF202402)。
文摘To enhance the overall performance of cyclotrimethylenetrinitramine(RDX),a modification strategy for RDX via in situ coordination with monometallic polydopamine(PDA)coatings(PDA-Fe,PDA-Cu,and PDA-Pb)was developed.The thermal properties of pristine RDX and its modified variants(RDX@PDA-Fe,RDX@PDA-Cu,RDX@PDA-Pb)were characterized using differential scanning calorimetry(DSC)and accelerating rate calorimetry(ARC).The impact sensitivity of these materials was evaluated via the characteristic drop-height method.The results demonstrate that PDA-metal metal coatings—formed through coordination between PDA and single metal ions(Fe^(3+),Cu^(2+),or Pb^(2+))—significantly enhance RDX′s thermal stability while attenuating its mechanical sensitivity.These coatings act as energy-absorbing barriers against external stimuli,effectively mitigating RDX′s sensitivity.Furthermore,they elevate RDX′s thermal stability by increasing its decomposition onset temperature and accelerating its decomposition kinetics.The monometallic coatings also catalyze RDX′s thermal decomposition and combustion,with Cu and Pb exhibiting particularly distinct catalytic effects.
基金Aeronautical Science Foundation of China(2021Z057053001)。
文摘Continuous carbon fiber reinforced silicon carbide(C/SiC)composites are often subjected to low-velocity impacts when utilized as structural materials for thermal protection.However,research on in-plane impact damage and multiple impact damage of C/SiC composites is limited.To investigate the in-plane impact damage behavior of C/SiC composites,a drop-weight impact test method was developed for strip samples,and these results were subsequently compared with those of C/SiC composite plates.Results show that the in-plane impact behavior of C/SiC strip samples is similar to that of C/SiC composite plates.Variation of the impact load with displacement is characterized by three stages:a nearly linear stage,a severe load drop stage,and a rebound stage where displacement occurs after the impact energy exceeds its peak value.Impact damage behavior under single and multiple impacts on 2D plain and 3D needled C/SiC composites was investigated at different impact energies and durations.Crack propagation in C/SiC composites was studied by computerized tomography(CT)technique.In the 2D plain C/SiC composite,load propagation between layers is hindered during impact,leading to delamination and 90°fiber brittle fracture.The crack length perpendicular to the impact direction increases with impact energy increases,resulting in more serious 0°fiber fracture and a larger area of fiber loss.In the 3D needled C/SiC composite,load propagates between the layers during impact through the connection of needled fibers.The fibers continue to provide substantial structural support,with notable instances of fiber pull-off and debonding.Consequently,the impact resistance is superior to that of 2D plain C/SiC composite.When the 3D needled C/SiC composite undergoes two successive impacts of 1.5 J,the energy absorption efficiency of the second impact is significantly lower,accompanied by a smaller impact displacement.Moreover,the total energy absorption efficiency of these two impacts of 1.5 J is lower than that of a single 3.0 J impact.
基金Anusandhan National Research Foundation (ANRF), Department of Science & Technology (DST), New Delhi, India under Ramanujan award (SB/S2/RJN-159/2017)。
文摘The rising concern over electromagnetic (EM) pollution is re-sponsible for the rapid progress in EM interference (EMI) shielding and EM wave absorption in the last few years, and carbon materials with a large sur-face area and high porosity have been investigated. Compared to other car-bon materials, biomass-derived carbon (BC) are considered efficient and eco-friendly materials for this purpose. We summarize the recent advances in BC materials for both EMI shielding and EM wave absorption. After a brief overview of the synthesis strategies of BC materials and a precise out-line of EM wave interference, strategies for improving their EMI shielding and EM wave absorption are discussed. Finally, the existing challenges and the future prospects for such materials are briefly summarized.
文摘Plant roots are widely known to provide mechanical reinforcement to soils against shearing and further increase slope stability.However,whether roots provide reinforcement to loess cyclic re-sistance and how various factors affect roots reinforcement during seismic loading have rarely been studied.The objective is to conduct a series of cyclic direct simple shear tests and DEM numerical simulation to investigate the cyclic behaviour of rooted loess.The effects of initial static shear stress and loading frequency on the cyclic resistance of root-soil composites were first investigated.After that,cyclic direct simple shear simulations at constant volume were carried out based on the discrete element method(PFC^(3D))to investigate the effects of root geome-try,mechanical traits and root-soil bond strength on the cyclic strength of rooted loess.It was discovered that the roots could effectively improve the cyclic resistance of loess.The cyclic resistance of the root-soil composite decreases with the increase of the initial shear stress,then increases,and improves with the increase of the frequency.The simulation result show that increases in root elastic modulus and root-soil interfacial bond strength can all enhance the cyclic resistance of root-soil composites,and the maximum cyclic resistance of the root-soil composite was obtained when the initial inclination angle of the root system was 90°.
基金National Natural Science Foundation of China(U23A6014,52103357)。
文摘In a high heat flux ablative environment,the surface temperature of aircraft rises rapidly,leading to traditional high thermal conductivity materials being ineffective at protecting internal metal components.In this study,continuous carbon fiber reinforced Li_(2)O-Al_(2)O_(3)-SiO_(2)(C_(f)/LAS)glass ceramic composites doped with SiC particles(SiC_(p))were prepared by slurry immersion winding and hot pressing sintering.Effect of matrix crystallinity on ablative properties of the composites under ultra-high heat flux was investigated.By utilizing heat absorption and low thermal conductivity characteristics associated with SiO_(2)gasification within composite materials,both surface and internal temperatures of these materials are effectively reduced,thereby ensuring the safe operation of aircraft and electronic devices.Results indicate that the average linear ablation rate of composites doped with 10%(in mass)of SiC_(p)significantly decreases at a heat flux of 20 MW/m^(2).Transmission electron microscope observation reveals that the doped glass matrix exhibits increased crystallinity,reduced internal stress,and minimized lattice distortion,thereby enhancing the composites’high-temperature performance.However,excessive SiC_(p)doping leads to reduced crystallinity and deteriorated ablation performance.Ultimately,the average linear ablation rate of C_(f)/LAS composites with 10%(in mass)SiC_(p)at 20 MW/m^(2)heat flux is comparable to that of commercial carbon/carbon composites,accompanied by providing lower thermal conductivity and higher bending strength.This novel high-performance C_(f)/LAS composite is cost-effective,short-cycled,and suitable for mass production,offering promising potential for widespread application in ablation-resistant components of hypersonic vehicles.
基金Project(2021YFC2900200)supported by the National Key Research and Development Project of ChinaProject(20230203114SF)supported by the Key Research and Development Project of Jilin Province,China。
文摘Basalt fibers/7075 aluminum matrix composites were studied to meet the demand of aluminum alloy drill pipes for material wear resistance.The composites with different basalt fiber additions were prepared by hot pressed sintering and hot extrusion.The mechanical properties as well as friction and wear properties of the composites were studied by microstructure analysis,tensile experiments,friction and wear experiments.The results showed that basalt fibers were oriented and uniformly distributed and led to local grain refinement in the alloy matrix.The hardness and elongation of the composites were improved.The friction coefficient of the composites increased and then decreased,and the maximum wear depth and wear amount decreased,then increased,then decreased again with the growth of basalt fiber addition.Meanwhile,the inclusion of basalt fibers mitigated the uneven wear of the extruded 7075 aluminum alloy.The value of wear depth difference of 7075-0.2BF was the smallest,and that of 7075-2.0BF was close to it.The maximum wear depth and wear volume the 7075-0.2BF and 7075-2.0BF were also the smallest.The inhibition of uneven wear by basalt fibers enhanced of wear resistance for 7075 aluminum alloy,which has reference significance for improving the performance of aluminum alloy drill pipes.
基金supported by a grant from the Ministry of Research, Innovation and Digitization, UEFISCDI, Grant Nos. PN-IIIP2-2.1-PED-2021-1890, PN-IV-P6-6.3-SOL-2024-2-0254 and PNIV-P7-7.1-PTE-2024-0517, within PNCDI Ⅳ.
文摘This study represents an important step forward in the domain of additive manufacturing of energetic materials.It presents the successful formulation and fabrication by 3D printing of gun propellants using Fused Deposition Modeling(FDM)technology,highlighting the immense potential of this innovative approach.The use of FDM additive manufacturing technology to print gun propellants is a significant advancement due to its novel application in this field,which has not been previously reported.Through this study,the potential of FDM 3D-printing in the production of high-performance energetic composites is demonstrated,and also a new standard for manufacturability in this field can be established.The thermoplastic composites developed in this study are characterized by a notably high energetic solids content,comprising 70%hexogen(RDX)and 10%nitrocellulose(NC),which surpasses the conventional limit of 60%energetic solids typically achieved in stereolithography and light-curing 3D printing methods.The primary objective of the study was to optimize the formulation,enhance performance,and establish an equilibrium between printability and propellant efficacy.Among the three energetic for-mulations developed for 3D printing feedstock,only two were suitable for printing via the FDM tech-nique.Notably,the formulation consisting of 70%RDX,10%NC,and 20%polycaprolactone(PCL)emerged as the most advantageous option for gun propellants,owing to its exceptional processability,ease of printability,and high energetic performance.
基金Project(2022J318)supported by the Natural Science Foundation of Ningbo,ChinaProject(2021A1515110525)supported by the Guangdong Basic and Applied Basic Research Foundation,ChinaProject(2022QN05023)supported by the Inner Mongolia Natural Science Foundation Youth Project,China。
文摘In order to obtain high-density dual-scale ceramic particles(8.5 wt.%SiC+1.5 wt.%TiC)reinforced Al-Mg Sc-Zr composites with uniform microstructure,50 nm TiC and 7μm SiC particles were pre-dispersed into 15−53μm aluminum alloy powders by low-speed ball milling and mechanical mixing technology,respectively.Then,the effects of laser energy density,power and scanning rate on the density of the composites were investigated based on selective laser melting(SLM)technology.The effect of micron-sized SiC and nano-sized TiC particles on solidification structure,mechanical properties and fracture behaviors of the composites was revealed and analyzed in detail.Interfacial reaction and phase variations in the composites with varying reinforced particles were emphatically considered.Results showed that SiC-TiC particles could significantly improve forming quality and density of the SLMed composites,and the optimal relative density was up to 100%.In the process of laser melting,a strong chemical reaction occurs between SiC and aluminum matrix,and micron-scale acicular Al_(4)SiC_(4) bands were formed in situ.There was no interfacial reaction between TiC particles and aluminum matrix.TiC/Al semi-coherent interface had good bonding strength.Pinning effect of TiC particles in grain boundaries could prevent the equiaxial crystals from growing and transforming into columnar crystals,resulting in grain refinement.The optimal ultimate tensile strength(UTS),yield strength(YS),elongation(EL)and elastic modulus of the SiC-TiC/Al-Mg-Sc-Zr composite were~394 MPa,~262 MPa,~8.2%and~86 GPa,respectively.The fracture behavior of the composites included ductile fracture of Al matrix and brittle cleavage fracture of Al_(4)SiC_(4) phases.A large number of cross-distributed acicular Al_(4)SiC_(4) bands were the main factors leading to premature failure and fracture of SiC-TiC/Al-Mg-Sc-Zr composites.
基金Projects(51975398,52105392)supported by the National Natural Science Foundation of ChinaProject(YDZJSX2021A006)supported by the Central Government Guided Local Science and Technology Development Fund Project,China+1 种基金Project(20210035)supported by the Scientific Activities of Selected Returned Overseas Professionals in Shanxi Province,ChinaProject(2020-037)supported by the Fund Program for the Research Project Supported by Shanxi Scholarship Council,China。
文摘In the present study,two-layered stainless steel-copper composites with a thickness of 50μm were initially subjected to annealing at 800,900 and 1000℃for 5 min,respectively,to achieve diverse microstructural features.Then the influence of annealing temperature on the formability of stainless steel-copper composites and the quality of micro composite cups manufactured by micro deep drawing(MDD)were investigated,and the underlying mechanism was analyzed.Three finite element(FE)models,including basic FE model,Voronoi FE model and surface morphological FE model,were developed to analyze the forming performance of stainless steel-copper composites during MDD.The results show that the stainless steel-copper composites annealed at 900℃possess the best plasticity owing to the homogeneous and refined microstructure in both stainless steel and copper matrixes,and the micro composite cup with specimen annealed at 900℃exhibits a uniform wall thickness as well as high surface quality with the fewest wrinkles.The results obtained from the surface morphological FE model considering material inhomogeneity and surface morphology of the composites are the closest to the experimental results compared to the basic and Voronoi FE model.During MDD process,the drawing forces decrease with increasing annealing temperature as a consequence of the strength reduction.
文摘A composite explosive based on 1,3,5-trinitro-1,3,5-triazinane(RDX)was prepared by electrostaticspray method with dioctyl sebacate(DOS)as desensitizer.After preparation,the particle size and crystal structure were characterized and chemical features,such as chemical bonds,functional groups,thermal decomposition parameters and mechanical sensitivity were investigated as well.In terms of the morphologies of the composites,the particle sizes were in the range of 1e3 mm.Compared with RDX,the crystal types,chemical bonds and functional groups of the RDX/DOS composites were unchanged.The activation energy of the composites was lower than that of raw RDX,and the 3wt%DOS composites had the lowest activation energy.The impact sensitivity and friction sensitivity of the RDX/DOS composites were lower than those of raw RDX,and the 10wt%DOS composites had the highest H50(125.9 cm)and the lowest friction sensitivity(8%).
基金Project(2007BAQ0104901) supported by the 11th Five-Year-Plan National Scientific & Technological ProgramProject(200704020) supported by the National Special Program on the Public Welfare Forests supported by Ministry of Science and Technology of China
文摘Green composites made from bamboo fibers and biodegradable resins were fabricated with press molding.On the basis of the Weibull distribution and the weakest-link theory,the statistical strength and distribution of bamboo fiber were analyzed,and the tensile strength of green composites was also investigated.The result confirms that the tensile statistical strength of fiber fits well with two-parameter Weibull distribution.In addition,the tensile strength of bamboo fiber reinforced composites is about 330 MPa with the fiber volume fraction of 70%.This value is close to or higher than that of other natural fiber reinforced green composites.
文摘In the present work, the surface characteristics of Electrical Discharge Machined (EDM) Al (6351)eSiC and Al (6351)eSiCeB4C composites are investigated. The composites are prepared by employing the conventional stir casting technique, as it can produce better particle dispersion in the matrix. The detailed experimental study is performed on the composites by varying current (I), duty factor (t), pulse on time (Ton), and the gap voltage (V) in order to analyze the Heat Affected Zone (HAZ) formed in the sub surface and the average crater diameter formed on the machined surface of the composites as an output function. The formation of recast layers, presence of bubbles and the surface texture of the composites at various machining conditions are observed. The results show that the increased Metal Removal Rate (MRR) increases the depth of HAZ and the average crater diameter on the machined area. Further, the addition of B4C particles to the composite produces more surface defect than the AleSiC composite.
文摘Effects of sintering temperature in hot pressing, t yp es, states and amounts of rare earth as well as TiH 2 on the transverse rupture strength (TRS) of Fe-based composites are studied by means of orthogonal test and variance analysis in this paper. It is found that sintering temperature has a significant effect on the TRS of Fe-based diamond composites. The optimal sin tering temperature is 780～860 ℃. On the contrary, the effects of RE additi v es on values of TRS of the diamond composites have on distinct difference no mat ter the RE is in the state of mixture or compound or oxidization. Experimental r esults demonstrate that Fe-based diamond composites with RE additives exhibit h igher TRS, which results in an increase in diamond retention capacity. The degre e of increment of TRS is different at different sintering temperatures. The opti mal amount of rare earth was found to be about 1% in weight. The effect of RE is more significant at lower sintering temperature. The experimental results also reveal that TiH 2 additive has a negative effect on the TRS of Fe-based compos ites. Microscope observations demonstrate that specimen without TiH 2 additives , shows fewer pores and denser structures in the base metal. It can also be seen from the SEM observation of the resulting fracturing surface of bending test sp ecimens that the bonding of the diamond-matrix interface is better in the speci men without TiH 2 than in the specimen with TiH 2. Also the fracture surface o f the specimen without TiH 2 reveals ductile cup and cone behavior.
文摘Polymer matrix composites(PMC)are extensively been used in many engineering applications.Various natural fibers have emerged as potential replacements to synthetic fibers as reinforcing materials composites owing to their fairly better mechanical properties,low cost,environment friendliness and biodegradability.Selection of appropriate constituents of composites for a particular application is a tedious task for a designer/engineer.Impact loading has emerged as the serious threat for the composites used in structural or secondary structural application and demands the usage of appropriate fiber and matrix combination to enhance the energy absorption and mitigate the failure.The objective of the present review is to explore the composite with various fiber and matrix combination used for impact applications,identify the gap in the literature and suggest the potential naturally available fiber and matrix combination of composites for future work in the field of impact loading.The novelty of the present study lies in exploring the combination of naturally available fiber and matrix combination which can help in better energy absorption and mitigate the failure when subjected to impact loading.In addition,the application of multi attributes decision making(MADM)tools is demonstrated for selection of fiber and matrix materials which can serve as a benchmark study for the researchers in future.
文摘In this present work siliconized e-glass fibre reinforced epoxy resin composite has been prepared and compared with acid and base treated e-glass fibre epoxy composites to know the significant advantage of silane treatment on fibre. The composites were fabricated by laying 20, 30 and 40vol% of e-glass fibre into epoxy resin matrix. The e-glass fibre woven mat was surface treated by an amine functional coupling agent 3-Aminopropyletrimethoxysilane(APTMS). The fibres were surface treated by aqueous solution method and thermo assisted to create silinol groups. Similarly for acid treatment H_2SO_4 and base treatment Na OH with 1N concentration was used for surface treating the fibres. Effectiveness of silane treatment on glass fibre was compared by inter laminar shear strength test according to ASTM D 2344.Drilling process with varying diameter drill bit and varying cutting speed was applied to check the composites for their delamination resistance while machining. Maximum improvement of 15%, 12.5% and9%(20, 30 and 40 vol %) on ILSS was achieved for siliconized e-glass fibre reinforced epoxy composites.The scanning electron microscopy images revealed that no fibre pull out was present on fractured surfaces of composites which contains siliconized e-glass fibre. Similarly better dimensional accuracy was achieved on drilling process for composites contains siliconized e-glass fibre.
基金supported by Technical Education Quality Improvement Programme (TEQIP-II) of Motilal Nehru National Institute of Technology Allahabad,Allahabad (U.P.),India financiallyby Invertis University,Bareilly,(U.P.),India
文摘The laminated glasses(LGs)composites are gaining popularity as protectivestructural material. Delamination strength(DS) of(LGs) with different inter-layers and their different nominal thicknesses were compared. The effect of inter-layer thickness, delamination load, and inter-layer type on DS is clearly observed from this brief study. It is concluded that inter-layer thickness has the significant role in determining the DS of LGs. The statistical analysis confirmed the strong association of DS with inter-layer thickness and the interlayer type. It was found that the LG-PVB composite has the comparatively lower DS than LG-EVA composite and inter-layer thickness has the prominent role in the determination of DS in the LG-EVAcomposite. There is an increment in DS with an increment in critical inter-layer thickness in both LG-EVA and LG-PVBcomposites. The increment in the inter-layer thickness from 0.38 mm to 0.76 mm increases DS significantly; whereas, the further increment in the inter-layer thickness to the higher value has a lesser effect. The finite element model was constituted(without considering the effect of temperature) for determining DS of LG composite. The simulation results were in a good match with experimental results. The results of the present work can be utilized by the design engineers while selecting LG for structural applications.
文摘Carbon-based composites, including carbon reinforced composites and carbon-matrix composites, in defence technologies have raised a lot of attention due to its significant physical capabilities, superior thermal and mechanical stability, and its eco-friendly nature. Carbon-based composite which incorporating with various carbonaceous materials such as coke, char, black carbon, activated carbon, carbon fibre and other carbon nanomaterials (carbon nanotubes, carbon nanofibres, graphene and graphite) are the greatest viable option for the development of advanced defence technologies. In this review article the characteristics of carbon-based materials and its composites are discussed for their distinct application in defence sectors;aeronautics, maritime, automotive, electronics, energy storage, electromagnetic interference (EMI) shielding and structures. The origin of carbonaceous materials and its production techniques were discussed. Carbon-based composites have a promising future in defence technology, particularly in chemical sensors, drug delivery agents, radar technologies, and nanocomposites due to their low cost, easy availability, flexibility in design and processing.
文摘In this paper, turning experiments of machining particle reinforced metal matri x composites(PRMMCs) SiC p/Al with PCD tools have been carried out. The cutting force characteristics in ultrasonic vibration turning compared with that in com mon turning were studied. Through the single factor experiments and multiple fac tor orthogonal experiments, the influences of three kinds of cutting conditions such as cutting velocity, amount of feed and cutting depth on cutting force were analyzed in detail. Meanwhile, according to the experimental data, the empirica l formula of main cutting force in ultrasonic vibration turning was conclude d. According to the test results, the cutting force is direct proportion to cutt ing depth basically according to the relation between cutting force and other fa ctors, which is similar to that of common cutting, so is the feed rate, but the influence is not so big. The influence of cutting speed is larger than that of f eed rate on cutting force because the efficient cutting time increases in vibrat ion cycle with the increase of cutting speed, which causes cutting force to incr ease. The research results indicate: (1) Ultrasonic vibration turning possesses much lower main cutting force than that in common turning when adopting smaller cutting parameters. If using larger cutting parameters, the difference will inco nspicuous. (2) There are remarkable differences of cutting force-cutting veloci ty characteristics in ultrasonic vibration turning from that in common turning m ainly because built-up edge does not emerge in ultrasonic turning unlike common turning in corresponding velocity range. (3) In ultrasonic vibration cutting, t he influence of cutting velocity on cutting force is most obvious among thre e cutting parameters and the influence of feed is smallest. So adopting lower cu tting velocity and larger cutting depth not only can reduce cutting force effect ively but also can ensure cutting efficiency. (4) The conclusions are useful in precision and super precision manufacturing thin-wall pieces.
基金The financial support from the National Natural Science Foundation of China under project No.10472107 is gratefully acknowledgedThe authors also wish to acknowledge the supports from the Aeronautical Science Foundation of China under project Nos. 04B23002 and 04B52009.
文摘This paper summarizes the authors’ experimental study on the characterization system of composite behavior to withstand impact. The content includes: (1)The dent depth is the best parameter describing the impact damage state. (2) There exists the knee point phenomenon for damage resistance behavior (i.e. the relationship between impact energy or contact force and dent depth) and damage tolerance behavior (i.e. the relationship between dent depth and compressive failure strain or stress) of composite laminates. (3) The physical meaning of the knee point phenomenon is that the failure mechanisms change of damaged composites to fiber breakage in the first front plies from matrix crack and delamination. Some suggestions on the characterization system of composite behavior to withstand impact were proposed.
文摘The densification rate of C/C composites fabricated by directional flow thermal gradient chemical vapor infiltration process from C 3H 6, C 3H 6 N 2 and C 3H 6 H 2 was investigated respectively. The mechanism on the role of carrier gas in chemical vapor infiltration was also discussed. The results shows that whether or not adding N 2 as carrier gas has little influences on the densification behavior of C/C composites with the controlled temperature, the partial pressure of hydrocarbon and the effective residence time of the gas phase remain constant. When the controlled temperature is not less than 1 173 K,using N 2 or H 2 as carrier gas makes pronounced differences in densifying of C/C composites. The average bulk density of C/C composites from C 3H 6 H 2 is eight to ten percent higher than that from C 3H 6 N 2. However, when the controlled temperature is not higher than 1 123 K,the densification rate of C/C composites from C 3H 6 H 2 is much lower than that from C 3H 6 N 2, which implies that effects of carrier gas on densification of C/C composites are closely related to the type of carrier gas and infiltration temperature. At higher temperature, using H 2 as carrier gas is favorable to the densification of C/C composites, while at lower temperature, hydrogen, acting as reactive gas, can inhibit the formation of pyrolytic carbon.