With the aim to effectively depolymerize polyethylene terephthalate(PET)under mild reaction conditions,PET methanolysis and dimethyl terephthalate(DMT)hydrolysis are integrated in a catalyst system.Firstly,methanolysi...With the aim to effectively depolymerize polyethylene terephthalate(PET)under mild reaction conditions,PET methanolysis and dimethyl terephthalate(DMT)hydrolysis are integrated in a catalyst system.Firstly,methanolysis of PET to DMT is achieved over Cu-Mg-Al oxide catalyst.Next,terephthalic acid(TPA)is prepared by DMT hydrolysis.It is found that hydrolysis of DMT to TPA can be promoted by introducing trace amount of water in this catalyst system.CuO-MgO-4.5Al_2O_(3)catalyst demonstrates the excellent catalytic performance for the depolymerization of PET with high conversion rate and TPA yield(100%and 99.5%,respectively)after reaction at 160℃for 6 h,which provides a new idea for the depolymerization of PET.展开更多
Fe-ZSM-5 catalysts modified by Cu and Ce by aqueous solution ion-exchange and incipient wetness impregnation methods were tested in the selective catalytic reduction of NO_(x) with NH_(3).A variety of characterization...Fe-ZSM-5 catalysts modified by Cu and Ce by aqueous solution ion-exchange and incipient wetness impregnation methods were tested in the selective catalytic reduction of NO_(x) with NH_(3).A variety of characterization techniques(NH_(3)-SCO,BET,XRD,XPS,UV-Vis,NH_(3)-TPD,H_(2)-TPR)were used to explore the changes of the active sites,acid sites and pore structure of the catalyst.It was found that the dispersion of active Cu species and Fe species had great influences on the catalytic activity in the whole catalytic process.The Cu doping into the Fe-ZSM-5 catalyst produced new active species,isolated Cu ions and CuO particles,resulting in the improved low-temperature catalytic activity.However,the NH_(3) oxidation was enhanced,and part of the Fe^(3+)active sites and more Brønsted acidic sites in the catalyst were occupied by Cu species,which causes the decrease of the high-temperature activity.The recovery of hightemperature activity could be attributed to the recovery of active Cu species and Fe species promoted by Ce and the promotion of active species dispersion.The results provide theoretical support for adjusting the active window of Febased SCR catalyst by multi-metal doping.展开更多
文摘With the aim to effectively depolymerize polyethylene terephthalate(PET)under mild reaction conditions,PET methanolysis and dimethyl terephthalate(DMT)hydrolysis are integrated in a catalyst system.Firstly,methanolysis of PET to DMT is achieved over Cu-Mg-Al oxide catalyst.Next,terephthalic acid(TPA)is prepared by DMT hydrolysis.It is found that hydrolysis of DMT to TPA can be promoted by introducing trace amount of water in this catalyst system.CuO-MgO-4.5Al_2O_(3)catalyst demonstrates the excellent catalytic performance for the depolymerization of PET with high conversion rate and TPA yield(100%and 99.5%,respectively)after reaction at 160℃for 6 h,which provides a new idea for the depolymerization of PET.
基金Project(51906089)supported by the National Natural Science Foundation of ChinaProject(NELMS2018A18)supported by the National Engineering Laboratory for Mobile Source Emission Control Technology,China+1 种基金Project(XNYQ2021-002)supported by the Provincial Engineering Research Center for New Energy Vehicle Intelligent Control and Simulation Test Technology of Sichuan,ChinaProject(GY2020016)supported by the Zhenjiang City Key R&D Program,China。
文摘Fe-ZSM-5 catalysts modified by Cu and Ce by aqueous solution ion-exchange and incipient wetness impregnation methods were tested in the selective catalytic reduction of NO_(x) with NH_(3).A variety of characterization techniques(NH_(3)-SCO,BET,XRD,XPS,UV-Vis,NH_(3)-TPD,H_(2)-TPR)were used to explore the changes of the active sites,acid sites and pore structure of the catalyst.It was found that the dispersion of active Cu species and Fe species had great influences on the catalytic activity in the whole catalytic process.The Cu doping into the Fe-ZSM-5 catalyst produced new active species,isolated Cu ions and CuO particles,resulting in the improved low-temperature catalytic activity.However,the NH_(3) oxidation was enhanced,and part of the Fe^(3+)active sites and more Brønsted acidic sites in the catalyst were occupied by Cu species,which causes the decrease of the high-temperature activity.The recovery of hightemperature activity could be attributed to the recovery of active Cu species and Fe species promoted by Ce and the promotion of active species dispersion.The results provide theoretical support for adjusting the active window of Febased SCR catalyst by multi-metal doping.