Continuous basalt fiber(CBF)is an outstanding inorganic fiber produced from nature,which has a wide range of applications in the field of armor protection of national defense military.However,the mechanical response a...Continuous basalt fiber(CBF)is an outstanding inorganic fiber produced from nature,which has a wide range of applications in the field of armor protection of national defense military.However,the mechanical response and failure mechanism of 3D printed CBF reinforced components are still not well understood.Here,the 3D printing thermoplastic composites with high volume fraction CBF have been successfully prepared by fused deposition modelling(FDM)method.The effects of fiber printing direction and polymer matrix type on the tensile and flexural properties of the 3D printed composites have been explored,and the detailed failure morphology has been characterized using scanning electron microscopy and optical microscopy.It was found that under high fiber volume fraction,3D printed CBF reinforced polyamides(PA)composites have the best ability to maintain material integrity of the composites,followed by acrylonitrile butadiene styrene(ABS)and high impact polystyrene(HIPS).Besides,the results from rule of mixtures can accurately predict the longitudinal Young’s modulus of the 3D printed specimens,but there exists a large discrepancy for the prediction of the tensile strength.The microstructure analysis shows that the failure modes of 3D printed composites mainly include fiber debonding,fiber pull-out,stress whitening and matrix cracking.展开更多
It was found that air dielectric barrier discharge(DBD) plasma contributed to the grafting of epoxy resin onto continuous PBO fiber surface. This air-plasma-grafting-epoxy method yielded a noticeable enhancement in th...It was found that air dielectric barrier discharge(DBD) plasma contributed to the grafting of epoxy resin onto continuous PBO fiber surface. This air-plasma-grafting-epoxy method yielded a noticeable enhancement in the interfacial adhesion between PBO fiber and thermoplastic matrix resin, with the interlaminar shear strength of the resulting composites increased by 66.7%. DSC and FTIR analyses were then used to study the curing behavior of epoxy coating on PBO fiber surface, deduce the possible grafting reactions and investigate the grafting mechanism. More importantly, TGA measurement showed that the grafting of epoxy onto PBO fiber had almost no effect on the composite heat resistance, and there was more thermoplastic matrix resin adhering to the fiber surface; the latter could also be clearly found in the SEM photos. Thereby, the air-plasma-grafting-epoxy treatment was proved to be an effective method for the improvement of continuous PBO fiber surface adhesive properties.展开更多
基金the financial support from the National Key Research and Development Program of China(grant no.2020YFA0711800)National Natural Science Foundation of China(grant no.11802027)+2 种基金State Key Laboratory of Explosion Science and Technology(grant no.YPJH20-6,QNKT20-01,JCRC18-01)BITBRFFR Joint Research Program(BITBLR2020018)Beijing Institute of Technology Research Fund。
文摘Continuous basalt fiber(CBF)is an outstanding inorganic fiber produced from nature,which has a wide range of applications in the field of armor protection of national defense military.However,the mechanical response and failure mechanism of 3D printed CBF reinforced components are still not well understood.Here,the 3D printing thermoplastic composites with high volume fraction CBF have been successfully prepared by fused deposition modelling(FDM)method.The effects of fiber printing direction and polymer matrix type on the tensile and flexural properties of the 3D printed composites have been explored,and the detailed failure morphology has been characterized using scanning electron microscopy and optical microscopy.It was found that under high fiber volume fraction,3D printed CBF reinforced polyamides(PA)composites have the best ability to maintain material integrity of the composites,followed by acrylonitrile butadiene styrene(ABS)and high impact polystyrene(HIPS).Besides,the results from rule of mixtures can accurately predict the longitudinal Young’s modulus of the 3D printed specimens,but there exists a large discrepancy for the prediction of the tensile strength.The microstructure analysis shows that the failure modes of 3D printed composites mainly include fiber debonding,fiber pull-out,stress whitening and matrix cracking.
基金Project(L2014056)supported by the Liaoning Education Department,ChinaProject(201501089)supported by the Dr.Start-up Fund of Liaoning Province,China
文摘It was found that air dielectric barrier discharge(DBD) plasma contributed to the grafting of epoxy resin onto continuous PBO fiber surface. This air-plasma-grafting-epoxy method yielded a noticeable enhancement in the interfacial adhesion between PBO fiber and thermoplastic matrix resin, with the interlaminar shear strength of the resulting composites increased by 66.7%. DSC and FTIR analyses were then used to study the curing behavior of epoxy coating on PBO fiber surface, deduce the possible grafting reactions and investigate the grafting mechanism. More importantly, TGA measurement showed that the grafting of epoxy onto PBO fiber had almost no effect on the composite heat resistance, and there was more thermoplastic matrix resin adhering to the fiber surface; the latter could also be clearly found in the SEM photos. Thereby, the air-plasma-grafting-epoxy treatment was proved to be an effective method for the improvement of continuous PBO fiber surface adhesive properties.