A new technology was developed to recover multiple valuable elements from the spent Al2O3-based catalyst by X-ray phase analysis and exploratory experiments. The experimental results show that in the condition of roas...A new technology was developed to recover multiple valuable elements from the spent Al2O3-based catalyst by X-ray phase analysis and exploratory experiments. The experimental results show that in the condition of roasting temperature of 750℃ and roasting time of 30 min, molar ratio of Na2O to Al2O3 of 1.2, the leaching rates of alumina, vanadium and molybdenum in the spent catalyst are 97.2%, 95.8% and 98.9%, respectively. Vanadium and molybdenum in sodium aluminate solution can be recovered by precipitators A and B, and the precipitation rates of vanadium and molybdenum are 94.8% and 92.6%. Al（OH）3 was prepared from sodium aluminate solution in the carbonation decomposition process, and the purity of Al2O3 is 99.9% after calcination, the recovery of alumina reaches 90.6% in the whole process; the Ni-Co concentrate was leached by sulfuric acid, a nickel recovery of 98.2% and cobalt recovery over 98.5% can be obtained under the experimental condition of 30% H2SO4, 80℃, reaction time 4 h, mass ratio of liquid to solid 8, stirring rate 800r/min.展开更多
Bayan Obo deposit in Inner Mongolia,China is not only the largest Iron-LREE-niobium deposit known in the world but also a giant fluorite deposit.Banded and streaky fluorite-rich REE-iron ores,bastnasiteapatite-pyroxen...Bayan Obo deposit in Inner Mongolia,China is not only the largest Iron-LREE-niobium deposit known in the world but also a giant fluorite deposit.Banded and streaky fluorite-rich REE-iron ores,bastnasiteapatite-pyroxene-fluorite ores,high-Fe,REEs,and fluorite ores,monazite(bastnaesite)-fluorite(low-Fe,high REE)ores etc.are widely disseminated in the Main and the East ore bodies.展开更多
基金Project(2003 UDBEA00C020) supported by the Collaborative Project of School and Province of Yunnan Province
文摘A new technology was developed to recover multiple valuable elements from the spent Al2O3-based catalyst by X-ray phase analysis and exploratory experiments. The experimental results show that in the condition of roasting temperature of 750℃ and roasting time of 30 min, molar ratio of Na2O to Al2O3 of 1.2, the leaching rates of alumina, vanadium and molybdenum in the spent catalyst are 97.2%, 95.8% and 98.9%, respectively. Vanadium and molybdenum in sodium aluminate solution can be recovered by precipitators A and B, and the precipitation rates of vanadium and molybdenum are 94.8% and 92.6%. Al（OH）3 was prepared from sodium aluminate solution in the carbonation decomposition process, and the purity of Al2O3 is 99.9% after calcination, the recovery of alumina reaches 90.6% in the whole process; the Ni-Co concentrate was leached by sulfuric acid, a nickel recovery of 98.2% and cobalt recovery over 98.5% can be obtained under the experimental condition of 30% H2SO4, 80℃, reaction time 4 h, mass ratio of liquid to solid 8, stirring rate 800r/min.
文摘Bayan Obo deposit in Inner Mongolia,China is not only the largest Iron-LREE-niobium deposit known in the world but also a giant fluorite deposit.Banded and streaky fluorite-rich REE-iron ores,bastnasiteapatite-pyroxene-fluorite ores,high-Fe,REEs,and fluorite ores,monazite(bastnaesite)-fluorite(low-Fe,high REE)ores etc.are widely disseminated in the Main and the East ore bodies.