ZnO(4mol%),In 2O 3(1mol%)and Fe 2O 3(0.05mol%)were doped in LiNbO 3 and Czochralski method was used to grow Zn∶In∶Fe∶LiNbO 3 crystal.The diameter of the crystal we grew is 30mm.The technology parameter we took is t...ZnO(4mol%),In 2O 3(1mol%)and Fe 2O 3(0.05mol%)were doped in LiNbO 3 and Czochralski method was used to grow Zn∶In∶Fe∶LiNbO 3 crystal.The diameter of the crystal we grew is 30mm.The technology parameter we took is that the axial temperature gradient is 40℃/cm,the growth rate is 1mm/h, the rotation rate is 15-25r/min,the temperature of polarization is 1220℃ and the current density of polarization is 5mA/cm 2.The wafer dimension is 10mm×10mm×3mm and was covered in Li 2CO 3 powder to reduce.The reduction temperature is 500℃ and reduction time is 30 hours. OH - stretch vibration transmission spectra were measured by Fourier infrared spectrophotometer. There are two absorption peaks in OH - spectra of Zn∶In∶Fe∶LiNbO 3,in which one is at 3534cm -1 (2.83μm) and the other is at 3505cm -1 (2.85μm).The peak at 2.85μm is far lower than that at 2.83μm. Because of the threshold effect of Zn 2+ and In 3+ ,the peak at 2.83μm is generated and the peak at 2.85μm is related with Fe 3+ .In LiNbO 3 only doped with Fe,Li + site is taken place by Fe 3+ .When doping Zn 2+ and In 3+ in high concentration,these two ions take place Nb that is at Li site and Fe 3+ substitutes for Nb 5+ at the same time.The interaction between Fe 3+ and OH - make the OH - peak shift to 2.85μm.展开更多
对铈铁掺杂铌酸锂(Ce:Fe:Li Nb O_3)晶体进行氧化、还原处理。通过红外光谱、紫外可见吸收光谱测试了晶体样品的组成和缺陷结构。采用透射光斑畸变法测试了晶体样品的抗光损伤能力,结果表明:生长态晶体比还原态晶体的抗光致散射能力基...对铈铁掺杂铌酸锂(Ce:Fe:Li Nb O_3)晶体进行氧化、还原处理。通过红外光谱、紫外可见吸收光谱测试了晶体样品的组成和缺陷结构。采用透射光斑畸变法测试了晶体样品的抗光损伤能力,结果表明:生长态晶体比还原态晶体的抗光致散射能力基本上高一个数量级,氧化态的晶体要比还原态的晶体高两个数量级。采用二波耦合实验测试了晶体样品的光折变性能,结果表明:从氧化到生长再到还原态,衍射效率逐渐降低,响应时间缩短,光折变灵敏度增加,动态范围逐渐降低。展开更多
文摘ZnO(4mol%),In 2O 3(1mol%)and Fe 2O 3(0.05mol%)were doped in LiNbO 3 and Czochralski method was used to grow Zn∶In∶Fe∶LiNbO 3 crystal.The diameter of the crystal we grew is 30mm.The technology parameter we took is that the axial temperature gradient is 40℃/cm,the growth rate is 1mm/h, the rotation rate is 15-25r/min,the temperature of polarization is 1220℃ and the current density of polarization is 5mA/cm 2.The wafer dimension is 10mm×10mm×3mm and was covered in Li 2CO 3 powder to reduce.The reduction temperature is 500℃ and reduction time is 30 hours. OH - stretch vibration transmission spectra were measured by Fourier infrared spectrophotometer. There are two absorption peaks in OH - spectra of Zn∶In∶Fe∶LiNbO 3,in which one is at 3534cm -1 (2.83μm) and the other is at 3505cm -1 (2.85μm).The peak at 2.85μm is far lower than that at 2.83μm. Because of the threshold effect of Zn 2+ and In 3+ ,the peak at 2.83μm is generated and the peak at 2.85μm is related with Fe 3+ .In LiNbO 3 only doped with Fe,Li + site is taken place by Fe 3+ .When doping Zn 2+ and In 3+ in high concentration,these two ions take place Nb that is at Li site and Fe 3+ substitutes for Nb 5+ at the same time.The interaction between Fe 3+ and OH - make the OH - peak shift to 2.85μm.
文摘对铈铁掺杂铌酸锂(Ce:Fe:Li Nb O_3)晶体进行氧化、还原处理。通过红外光谱、紫外可见吸收光谱测试了晶体样品的组成和缺陷结构。采用透射光斑畸变法测试了晶体样品的抗光损伤能力,结果表明:生长态晶体比还原态晶体的抗光致散射能力基本上高一个数量级,氧化态的晶体要比还原态的晶体高两个数量级。采用二波耦合实验测试了晶体样品的光折变性能,结果表明:从氧化到生长再到还原态,衍射效率逐渐降低,响应时间缩短,光折变灵敏度增加,动态范围逐渐降低。
