High-density germanate glasses doped with Tb^(3+)ions were synthesized via the melt-quenching meth-od.The physical and luminescent properties of these glasses were characterized through various techniques,in-cluding d...High-density germanate glasses doped with Tb^(3+)ions were synthesized via the melt-quenching meth-od.The physical and luminescent properties of these glasses were characterized through various techniques,in-cluding density measurement,differential scanning calorimetry(DSC),photoluminescence(PL)spectroscopy,X-ray excited luminescence(XEL)spectroscopy,and fluorescence decay analysis.The densities of the germanate glasses were greater than 6.1 g/cm^(3).Upon excitations of ultraviolet(UV)light and X-rays,the glasses emitted in-tense green emissions.The fluorescence lifetime of the strongest emission peak at 544 nm,measured under 377 nm excitation,ranged from 1.52 ms to 1.32 ms.In the glass specimens,the maximum XEL integral intensity reached roughly 26%of that of the commercially available Bi_(4)Ge_(3)O_(12)(BGO)crystal.These results indicate that Tb^(3+)-doped high-density germanate scintillating glasses hold potential as scintillation materials for X-ray imaging applications.展开更多
Y_(3)Al_(2)Ga_(3)O_(12):Ce^(3+),Cr^(3+)(YAGG:Ce^(3+),Cr^(3+)),as a persistent luminescent material,has advantages of high initial luminescence intensity and long persistent time,which is promising in persistent lumine...Y_(3)Al_(2)Ga_(3)O_(12):Ce^(3+),Cr^(3+)(YAGG:Ce^(3+),Cr^(3+)),as a persistent luminescent material,has advantages of high initial luminescence intensity and long persistent time,which is promising in persistent luminescent material applications.At present,YAGG:Ce^(3+),Cr^(3+)powders exhibit good persistent performance,but their persistent performance of ceramics still needs to be further improved to meet the new requirements.In this work,(Y_(0.998)Ce_(0.002))_(3)(Al_(1-x)Cr_(x))_(2)Ga_(3)O_(12) ceramics with different Cr^(3+)doping concentrations were prepared by solid-state reaction,including air pre-sintering,hot isostatic pressing(HIP)post-treatment and air annealing,to investigate the effects of Cr^(3+)doping concentration on the microstructure,optical properties and persistent performance of the ceramics.The results showed that as the doping concentration of Cr^(3+)increased from 0.025%to 0.2%(in atom),no significant effect of Cr^(3+)concentration on the morphology of pre-sintered ceramics or HIP post-treatment ceramics was observed,but the in-line transmittance gradually increased while the persistent performance gradually decreased.Among them,YAGG:Ce^(3+),Cr^(3+)ceramics doped with 0.025%Cr^(3+)showed the strongest initial luminescence intensity exceeding 6055 mcd/m^(2) and a persistent time of 1030 min after air pre-sintering combined with HIP post-treatment and air annealing.By optimizing the Cr^(3+)doping concentration and the fabrication process,the persistent luminescence(PersL)performance of the YAGG:Ce^(3+),Cr^(3+)ceramics was obviously improved.展开更多
文摘High-density germanate glasses doped with Tb^(3+)ions were synthesized via the melt-quenching meth-od.The physical and luminescent properties of these glasses were characterized through various techniques,in-cluding density measurement,differential scanning calorimetry(DSC),photoluminescence(PL)spectroscopy,X-ray excited luminescence(XEL)spectroscopy,and fluorescence decay analysis.The densities of the germanate glasses were greater than 6.1 g/cm^(3).Upon excitations of ultraviolet(UV)light and X-rays,the glasses emitted in-tense green emissions.The fluorescence lifetime of the strongest emission peak at 544 nm,measured under 377 nm excitation,ranged from 1.52 ms to 1.32 ms.In the glass specimens,the maximum XEL integral intensity reached roughly 26%of that of the commercially available Bi_(4)Ge_(3)O_(12)(BGO)crystal.These results indicate that Tb^(3+)-doped high-density germanate scintillating glasses hold potential as scintillation materials for X-ray imaging applications.
基金National Key R&D Program of China(2023YFB3506600)。
文摘Y_(3)Al_(2)Ga_(3)O_(12):Ce^(3+),Cr^(3+)(YAGG:Ce^(3+),Cr^(3+)),as a persistent luminescent material,has advantages of high initial luminescence intensity and long persistent time,which is promising in persistent luminescent material applications.At present,YAGG:Ce^(3+),Cr^(3+)powders exhibit good persistent performance,but their persistent performance of ceramics still needs to be further improved to meet the new requirements.In this work,(Y_(0.998)Ce_(0.002))_(3)(Al_(1-x)Cr_(x))_(2)Ga_(3)O_(12) ceramics with different Cr^(3+)doping concentrations were prepared by solid-state reaction,including air pre-sintering,hot isostatic pressing(HIP)post-treatment and air annealing,to investigate the effects of Cr^(3+)doping concentration on the microstructure,optical properties and persistent performance of the ceramics.The results showed that as the doping concentration of Cr^(3+)increased from 0.025%to 0.2%(in atom),no significant effect of Cr^(3+)concentration on the morphology of pre-sintered ceramics or HIP post-treatment ceramics was observed,but the in-line transmittance gradually increased while the persistent performance gradually decreased.Among them,YAGG:Ce^(3+),Cr^(3+)ceramics doped with 0.025%Cr^(3+)showed the strongest initial luminescence intensity exceeding 6055 mcd/m^(2) and a persistent time of 1030 min after air pre-sintering combined with HIP post-treatment and air annealing.By optimizing the Cr^(3+)doping concentration and the fabrication process,the persistent luminescence(PersL)performance of the YAGG:Ce^(3+),Cr^(3+)ceramics was obviously improved.