A new anodic material of ternary Pb-0.8%Ag-(0-5.0%)Bi alloy for zinc electrowinning was obtained by doping Bi.The anodic oxygen evolution potential,corrosion rate,surface products after polarization,and microstructure...A new anodic material of ternary Pb-0.8%Ag-(0-5.0%)Bi alloy for zinc electrowinning was obtained by doping Bi.The anodic oxygen evolution potential,corrosion rate,surface products after polarization,and microstructures before and after polarization were studied and compared with those of Pb-0.8%Ag anode used in industry.The results show the anodic overpotential decreases with the increase of Bi content in the alloys.When the content of Bi is 1.0%(mass fraction),the anodic overpotential is 40-50 mV lower than that of Pb-0.8%Ag anode.While the corrosion rate decreases and then increases with the increase of Bi content.The Pb-0.8%Ag-0.1%Bi anode has the lowest corrosion rate(0.090 6 mg/(h·cm2).Doping Bi influences the structure of the anodic layer,but does not change the phase.The Pb-0.8%Ag-1.0%Bi anode layer is of a more fine-grained structure compared with Pb-0.8%Ag anode.展开更多
基金Project(2007SK2009)supported by the Science and Technology Research Project of Hunan Province,China
文摘A new anodic material of ternary Pb-0.8%Ag-(0-5.0%)Bi alloy for zinc electrowinning was obtained by doping Bi.The anodic oxygen evolution potential,corrosion rate,surface products after polarization,and microstructures before and after polarization were studied and compared with those of Pb-0.8%Ag anode used in industry.The results show the anodic overpotential decreases with the increase of Bi content in the alloys.When the content of Bi is 1.0%(mass fraction),the anodic overpotential is 40-50 mV lower than that of Pb-0.8%Ag anode.While the corrosion rate decreases and then increases with the increase of Bi content.The Pb-0.8%Ag-0.1%Bi anode has the lowest corrosion rate(0.090 6 mg/(h·cm2).Doping Bi influences the structure of the anodic layer,but does not change the phase.The Pb-0.8%Ag-1.0%Bi anode layer is of a more fine-grained structure compared with Pb-0.8%Ag anode.