为提高聚合物光波导放大器的增益性能,利用高温法合成了Ba Lu F5∶Yb3+,Er3+纳米晶,并分别对纳米晶的形貌、晶体结构和近红外发射特性进行了表征。测试结果表明,纳米晶平均粒径为13 nm,并在1 530 nm处具有较强的发射,荧光半高宽为50 nm...为提高聚合物光波导放大器的增益性能,利用高温法合成了Ba Lu F5∶Yb3+,Er3+纳米晶,并分别对纳米晶的形貌、晶体结构和近红外发射特性进行了表征。测试结果表明,纳米晶平均粒径为13 nm,并在1 530 nm处具有较强的发射,荧光半高宽为50 nm。将合成的纳米晶掺杂入SU-8聚合物作为光波导放大器的芯层材料,使用光刻显影等工艺,在表面长有二氧化硅的硅衬底上制备出了聚合物光波导放大器。当980 nm波长泵浦光功率为280 m W、信号光波长为1 530 nm且功率为0.1 m W时,在长度为1.1 cm的光波导放大器中,获得了3.95 d B的相对增益。展开更多
A homoleptic lanthanide guanidinate complex [（CH2）5NC（NiPr）2]3Yb was synthesized by the metathesis reaction of lithium guanidinate with anhydrous YbCl3 in 3∶1 molar ratio in THF.Its crystal structure was determin...A homoleptic lanthanide guanidinate complex [（CH2）5NC（NiPr）2]3Yb was synthesized by the metathesis reaction of lithium guanidinate with anhydrous YbCl3 in 3∶1 molar ratio in THF.Its crystal structure was determined by X-ray diffraction.The crystallographic data:C36H72N9Yb,Mr=804.07,orthorhombic,space group P212121（#19）,a=10.3168（7）,b=11.443（7）,c=35.5649（2）?,V=4199.1（5）?3,Z=4,Dc=1.272 g/cm3,F（000）=1684.00,T=193.1K,λ（MoKα）=0.7107?,μ=22.61 cm-1,R=0.040,wR=0.126 for 8653 observed reflections with（I>3.00 σ（I））.The ytterbium is six-coordinate by six nitrogen atoms of three chelation bidentate guanidinate ligands.展开更多
The influence of Er3+ ions on the spectra of Yb^(3+),Er^(3+): Sc_2 SiO_5(SSO) single crystal, which was obtained by Czochralski(Cz) method, is discussed. The absorption coefficient at 980 nm was 13.36 cm^(-1) with a p...The influence of Er3+ ions on the spectra of Yb^(3+),Er^(3+): Sc_2 SiO_5(SSO) single crystal, which was obtained by Czochralski(Cz) method, is discussed. The absorption coefficient at 980 nm was 13.36 cm^(-1) with a peak absorption cross-section of 1.46 × 10^(-20) cm2. The emission cross-sections at 1034 nm and 1062 nm were 5.5 × 10^(-21) cm^2 and4.9 × 10^(-21) cm^2, respectively. The fluorescence lifetime was estimated as 1.24 ms at 1061 nm. The mechanical properties of SSO single crystal were also presented.展开更多
文摘为提高聚合物光波导放大器的增益性能,利用高温法合成了Ba Lu F5∶Yb3+,Er3+纳米晶,并分别对纳米晶的形貌、晶体结构和近红外发射特性进行了表征。测试结果表明,纳米晶平均粒径为13 nm,并在1 530 nm处具有较强的发射,荧光半高宽为50 nm。将合成的纳米晶掺杂入SU-8聚合物作为光波导放大器的芯层材料,使用光刻显影等工艺,在表面长有二氧化硅的硅衬底上制备出了聚合物光波导放大器。当980 nm波长泵浦光功率为280 m W、信号光波长为1 530 nm且功率为0.1 m W时,在长度为1.1 cm的光波导放大器中,获得了3.95 d B的相对增益。
文摘A homoleptic lanthanide guanidinate complex [（CH2）5NC（NiPr）2]3Yb was synthesized by the metathesis reaction of lithium guanidinate with anhydrous YbCl3 in 3∶1 molar ratio in THF.Its crystal structure was determined by X-ray diffraction.The crystallographic data:C36H72N9Yb,Mr=804.07,orthorhombic,space group P212121（#19）,a=10.3168（7）,b=11.443（7）,c=35.5649（2）?,V=4199.1（5）?3,Z=4,Dc=1.272 g/cm3,F（000）=1684.00,T=193.1K,λ（MoKα）=0.7107?,μ=22.61 cm-1,R=0.040,wR=0.126 for 8653 observed reflections with（I>3.00 σ（I））.The ytterbium is six-coordinate by six nitrogen atoms of three chelation bidentate guanidinate ligands.
基金supported by the National Key Research and Development Program of China(Grant No.2016YFB0701002)the Joint Fund of the National Natural Science Foundation of China and China Academy of Engineering Physics(NSAF)(Grant No.U1530152)+1 种基金the National Natural Science Foundation of China(Grant Nos.91222112 and 61475177)Shanghai Rising-Star Program(B type),China(Grant No.14QB1401600)
文摘The influence of Er3+ ions on the spectra of Yb^(3+),Er^(3+): Sc_2 SiO_5(SSO) single crystal, which was obtained by Czochralski(Cz) method, is discussed. The absorption coefficient at 980 nm was 13.36 cm^(-1) with a peak absorption cross-section of 1.46 × 10^(-20) cm2. The emission cross-sections at 1034 nm and 1062 nm were 5.5 × 10^(-21) cm^2 and4.9 × 10^(-21) cm^2, respectively. The fluorescence lifetime was estimated as 1.24 ms at 1061 nm. The mechanical properties of SSO single crystal were also presented.