The effect of sinter basicity on softening-melting behaviors of mixed burden made from chromium-bearing vanadium-titanium magnetite(Cr-V-Ti magnetite) was investigated and the function mechanism was simultaneously ana...The effect of sinter basicity on softening-melting behaviors of mixed burden made from chromium-bearing vanadium-titanium magnetite(Cr-V-Ti magnetite) was investigated and the function mechanism was simultaneously analyzed.The results show that with increasing sinter basicity from 1.71 to 2.36,the softening interval tends to increase from 149.3 ℃ to 181.7 ℃while the melting interval tends to decrease from 178.0 ℃ to 136.7 ℃.The location of cohesive zone moves downwards firstly and then ascends slightly,but the cohesive zone becomes thinner.The softening-melting characteristic value becomes small,which indicates that the permeability of burden column is improved.The dripping ratio of mixed burden tends to increase firstly and then decrease,which comes to the highest value of 74.50%when the sinter basicity is 2.13.The content and the recovery of V and Cr in dripping iron are all increased.The generation amount of components with high melting point in slag becomes little with the increase of sinter basicity,which could improve the permeability of mixed burden.Taking softening-melting behaviors of mixed burden and recovery of valuable elements into account,the proper sinter basicity is no less than 2.13 for smelting mixed burden made from Cr-V-Ti magnetite in blast furnace.展开更多
The effects of basicity and temperature on the reduction process of Hongge high-chromium vanadium-titanium magnetite(HCVTM)sinter were investigated in this work.The main characterization methods of X-ray fluorescence(...The effects of basicity and temperature on the reduction process of Hongge high-chromium vanadium-titanium magnetite(HCVTM)sinter were investigated in this work.The main characterization methods of X-ray fluorescence(XRF),X-ray diffraction(XRD),scanning electron microscope(SEM),and metallographic microscope were employed in this study.In this work,the reduction of HCVTM sinter with different temperature and basicity were experimented.The Fe,FeO,and TiO in reductive samples increase with increasing basicity and temperatures.The increase of basicity and temperature is favorable to the reduction of HCVTM sinter.The Fe phase has out-migration tendency to the surface of sinter while the perovskite and silicate phases have in-migration tendency to the inside of sinter.The reduction degradation index(RDI)decreases while the reduction index(RI)increases with increasing basicity.The RI increases from 67.14%to 82.09%with increasing temperature from 1073 K to 1373 K.展开更多
基金Project(51574067)supported by the National Natural Science Fundation of ChinaProjects(2012AA062302,2012AA062304)supported by the National High Technology Research and Development Program of ChinaProject(N110202001)supported by the Fundamental Research Funds for the Central Universities of China
文摘The effect of sinter basicity on softening-melting behaviors of mixed burden made from chromium-bearing vanadium-titanium magnetite(Cr-V-Ti magnetite) was investigated and the function mechanism was simultaneously analyzed.The results show that with increasing sinter basicity from 1.71 to 2.36,the softening interval tends to increase from 149.3 ℃ to 181.7 ℃while the melting interval tends to decrease from 178.0 ℃ to 136.7 ℃.The location of cohesive zone moves downwards firstly and then ascends slightly,but the cohesive zone becomes thinner.The softening-melting characteristic value becomes small,which indicates that the permeability of burden column is improved.The dripping ratio of mixed burden tends to increase firstly and then decrease,which comes to the highest value of 74.50%when the sinter basicity is 2.13.The content and the recovery of V and Cr in dripping iron are all increased.The generation amount of components with high melting point in slag becomes little with the increase of sinter basicity,which could improve the permeability of mixed burden.Taking softening-melting behaviors of mixed burden and recovery of valuable elements into account,the proper sinter basicity is no less than 2.13 for smelting mixed burden made from Cr-V-Ti magnetite in blast furnace.
基金Project(2013CB632603)supported by the National Basic Research Program of ChinaProject(2015BAB19B02)supported by the National Key Technology R&D Program of ChinaProjects(51674084,51174051,51574082)supported by National Natural Science Foundation of China
文摘The effects of basicity and temperature on the reduction process of Hongge high-chromium vanadium-titanium magnetite(HCVTM)sinter were investigated in this work.The main characterization methods of X-ray fluorescence(XRF),X-ray diffraction(XRD),scanning electron microscope(SEM),and metallographic microscope were employed in this study.In this work,the reduction of HCVTM sinter with different temperature and basicity were experimented.The Fe,FeO,and TiO in reductive samples increase with increasing basicity and temperatures.The increase of basicity and temperature is favorable to the reduction of HCVTM sinter.The Fe phase has out-migration tendency to the surface of sinter while the perovskite and silicate phases have in-migration tendency to the inside of sinter.The reduction degradation index(RDI)decreases while the reduction index(RI)increases with increasing basicity.The RI increases from 67.14%to 82.09%with increasing temperature from 1073 K to 1373 K.