The synthesis of Al2O3-coated and uncoated LiMn2O4 by solid-state method and fabrication of LiMn2O4/graphite battery were described. The structure and morphology of the powders were characterized by X-ray diffraction ...The synthesis of Al2O3-coated and uncoated LiMn2O4 by solid-state method and fabrication of LiMn2O4/graphite battery were described. The structure and morphology of the powders were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The electrochemical and overcharge performances of Al2O3-coated and uncoated LiMn2O4 batteries were investigated and compared. The uncoated LiMn2O4 battery shows capacity loss of 16.5% after 200 cycles, and the coated LiMn2O4 battery only shows 12.5% after 200 cycles. The uncoated LiMn2O4 battery explodes and creates carbon, MnO, and Li2CO3 after 3C/10 V overcharged test, while the coated LiMn2O4 battery passes the test. The steadier structure, polarization of electrode and modified layer are responsible for the safety performance.展开更多
Alumina coated LiNi1/3Mn1/3Co1/3O2 particles were obtained by a simple method of solid state reaction at room temperature. The reaction mechanism of solid state reaction at room temperature was investigated. The struc...Alumina coated LiNi1/3Mn1/3Co1/3O2 particles were obtained by a simple method of solid state reaction at room temperature. The reaction mechanism of solid state reaction at room temperature was investigated. The structure and morphology of the coating materials were investigated by XRD, SEM and TEM. The electrochemical performances of uncoated and Al2O3-coated LiNi1/3Co1/3Mn1/3O2 cathode materials were studied within a voltage window of 3.00?4.35 V at current density of 30 mA/g. SEM, TEM and EDS analytical results indicate that the surface of LiNi1/3Mn1/3Co1/3O2 particles is coated with very fine Al2O3 composite, which leads to the improved cycle ability though a slight decrease in the first discharge capacity is observed. It is proposed that surface treatment by solid state reaction at room temperature is a simple and effective method to improve the cycle performance of LiNi1/3Co1/3Mn1/3O2 particles.展开更多
Numerical simulation and experimental study of the Vickers indentation testing of the Al2O3 ceramic coated by diamond-like carbon(DLC) layer were conducted.The numerical analysis was implemented by a two-dimensional f...Numerical simulation and experimental study of the Vickers indentation testing of the Al2O3 ceramic coated by diamond-like carbon(DLC) layer were conducted.The numerical analysis was implemented by a two-dimensional finite element(FE) axis symmetry model.FE analysis results gave insight into the fracture mechanism of DLC films coated on brittle ceramic(Al2O3) substrates.The maximum principal stress field was used to locate the most expected area for crack formation and propagation during the Vickers indentation testing.The results show that the median crack initiates in the interface under indenter,before ring crack occurs as the indenter presses down.Finally,the plastic deformation appears when the indenter penetrates into the substrate.The thicker DLC coating increases the Vickers hardness and fracture toughness.展开更多
The high-temperature oxidation resistance behavior of 7% （mass fraction） Y203-ZrO2 thermal barrier coatings （TBCs） irradiated by high-intensity pulsed ion beam （HIPIB） was investigated under the cyclic oxidation...The high-temperature oxidation resistance behavior of 7% （mass fraction） Y203-ZrO2 thermal barrier coatings （TBCs） irradiated by high-intensity pulsed ion beam （HIPIB） was investigated under the cyclic oxidation condition of 1 050 ℃ and 1 h. The columnar grains in the TBCs disappear after the HIPIB irradiation at ion current densities of 100-200 A/cm^2 and the irradiated surface becomes smooth and densified after remelting and ablation due to the HIPIB irradiation. The thermally grown oxide （TGO） layer thickness of the irradiated TBCs is smaller than that of the original TBCs. After 15 cycles, the mass gains of the original TBCs and those irradiated by ion current densities of 100 and 200 A/cm^2 due to the oxidation are found to be 0.8-0.9, 0.6-0.7, and 0.3-0.4 mg/cm^2, respectively. The inward diffusion of oxygen through the irradiated TBCs is significantly impeded by the densified top layer formed due to irradiation, which is the main reason for the improved overall oxidation resistance of the irradiated TBCs.展开更多
以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO ...以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。展开更多
基金Project(10JDG041) supported by the Advanced Person Fund of Jiangsu University, ChinaProject(2007CB613607) supported by the National Basic Research Program of China
文摘The synthesis of Al2O3-coated and uncoated LiMn2O4 by solid-state method and fabrication of LiMn2O4/graphite battery were described. The structure and morphology of the powders were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The electrochemical and overcharge performances of Al2O3-coated and uncoated LiMn2O4 batteries were investigated and compared. The uncoated LiMn2O4 battery shows capacity loss of 16.5% after 200 cycles, and the coated LiMn2O4 battery only shows 12.5% after 200 cycles. The uncoated LiMn2O4 battery explodes and creates carbon, MnO, and Li2CO3 after 3C/10 V overcharged test, while the coated LiMn2O4 battery passes the test. The steadier structure, polarization of electrode and modified layer are responsible for the safety performance.
基金Project(50604018) supported by the National Natural Science Foundation of China
文摘Alumina coated LiNi1/3Mn1/3Co1/3O2 particles were obtained by a simple method of solid state reaction at room temperature. The reaction mechanism of solid state reaction at room temperature was investigated. The structure and morphology of the coating materials were investigated by XRD, SEM and TEM. The electrochemical performances of uncoated and Al2O3-coated LiNi1/3Co1/3Mn1/3O2 cathode materials were studied within a voltage window of 3.00?4.35 V at current density of 30 mA/g. SEM, TEM and EDS analytical results indicate that the surface of LiNi1/3Mn1/3Co1/3O2 particles is coated with very fine Al2O3 composite, which leads to the improved cycle ability though a slight decrease in the first discharge capacity is observed. It is proposed that surface treatment by solid state reaction at room temperature is a simple and effective method to improve the cycle performance of LiNi1/3Co1/3Mn1/3O2 particles.
文摘Numerical simulation and experimental study of the Vickers indentation testing of the Al2O3 ceramic coated by diamond-like carbon(DLC) layer were conducted.The numerical analysis was implemented by a two-dimensional finite element(FE) axis symmetry model.FE analysis results gave insight into the fracture mechanism of DLC films coated on brittle ceramic(Al2O3) substrates.The maximum principal stress field was used to locate the most expected area for crack formation and propagation during the Vickers indentation testing.The results show that the median crack initiates in the interface under indenter,before ring crack occurs as the indenter presses down.Finally,the plastic deformation appears when the indenter penetrates into the substrate.The thicker DLC coating increases the Vickers hardness and fracture toughness.
基金Projects supported by The 2nd Stage of Brain Korea and Korea Research Foundation
文摘The high-temperature oxidation resistance behavior of 7% （mass fraction） Y203-ZrO2 thermal barrier coatings （TBCs） irradiated by high-intensity pulsed ion beam （HIPIB） was investigated under the cyclic oxidation condition of 1 050 ℃ and 1 h. The columnar grains in the TBCs disappear after the HIPIB irradiation at ion current densities of 100-200 A/cm^2 and the irradiated surface becomes smooth and densified after remelting and ablation due to the HIPIB irradiation. The thermally grown oxide （TGO） layer thickness of the irradiated TBCs is smaller than that of the original TBCs. After 15 cycles, the mass gains of the original TBCs and those irradiated by ion current densities of 100 and 200 A/cm^2 due to the oxidation are found to be 0.8-0.9, 0.6-0.7, and 0.3-0.4 mg/cm^2, respectively. The inward diffusion of oxygen through the irradiated TBCs is significantly impeded by the densified top layer formed due to irradiation, which is the main reason for the improved overall oxidation resistance of the irradiated TBCs.
文摘以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。