In order to investigate the existing form and action mechanism of minor scandium （Sc） and zirconium （Zr） in AI-Cu-Mg alloy, microstructures of Al-4Cu-1Mg-Sc-Zr alloy under different conditions, including states of...In order to investigate the existing form and action mechanism of minor scandium （Sc） and zirconium （Zr） in AI-Cu-Mg alloy, microstructures of Al-4Cu-1Mg-Sc-Zr alloy under different conditions, including states of as-cast, homogenized, hot-rolled, as-solution and natural aged, were observed by scanning electron microscopy （SEM）, X-ray diffractometry （XRD） and transmission electron microscopy （TEM）. It is revealed that Sc and Zr are completely dissolved into the supersaturated solid solution in as-cast ingot, but grain refinement is not observed. Coffee-bean-like AI3（Sc, Zr） particles deposit during homogenization of ingot induce an increase in hardness. Al3（Sc, Zr） particles are slightly coarsened in as-solution samples, but they still maintain coherent to matrix, which indicates a high thermal stability of these particles. Good coherency ofAl3（Sc, Zr） particles makes some benefits for inhibiting recrystallization and reserving work-hardening.展开更多
基金Project(2005DFA50550) supported by International Science and Technology Cooperation Program of ChinaProject(2005CB623705) supported by the National Basic Research Program of China
文摘In order to investigate the existing form and action mechanism of minor scandium （Sc） and zirconium （Zr） in AI-Cu-Mg alloy, microstructures of Al-4Cu-1Mg-Sc-Zr alloy under different conditions, including states of as-cast, homogenized, hot-rolled, as-solution and natural aged, were observed by scanning electron microscopy （SEM）, X-ray diffractometry （XRD） and transmission electron microscopy （TEM）. It is revealed that Sc and Zr are completely dissolved into the supersaturated solid solution in as-cast ingot, but grain refinement is not observed. Coffee-bean-like AI3（Sc, Zr） particles deposit during homogenization of ingot induce an increase in hardness. Al3（Sc, Zr） particles are slightly coarsened in as-solution samples, but they still maintain coherent to matrix, which indicates a high thermal stability of these particles. Good coherency ofAl3（Sc, Zr） particles makes some benefits for inhibiting recrystallization and reserving work-hardening.