Electroshocking treatment(EST),an efficient and rapid material treatment method,promotes microstructure evolution and improves mechanical properties.This study incorporates EST into the conventional cold rolling-quenc...Electroshocking treatment(EST),an efficient and rapid material treatment method,promotes microstructure evolution and improves mechanical properties.This study incorporates EST into the conventional cold rolling-quenching tempering process of M50 steel and investigates the influence and mechanism of applying EST at different stages of the process on the microstructure and mechanical properties.Scanning electron microscope(SEM),transmission electron microscope(TEM),and X-ray diffraction(XRD)were used to characterize the effect of EST on microstructure.The results show that EST can refine the grains of M50(average reduction of 10.1%in grain size),homogenize the grain size distribution,reduce the dislocation density(20.9%in average),promote the dissolution of carbides in the matrix and distribute them more uniformly along the grain boundaries,resulting in the improvement of mechanical properties.The mechanical properties of the specimen with the process flow of rolling-quenching-tempering-electroshocking showed excellent performance,with an increase in hardness of 1.4%,tensile strength of 17.7%,and elongation at break of 24.3%as compared to the specimen without EST.The tensile properties of the specimen with the process flow of rolling electroshocking-quenching-tempering showed the best performance,with an increase in tensile strength of 30.0%and elongation at break of 30.7%as compared to the specimen without EST.展开更多
Effect of tempering temperature on the microstructure and mechanical properties of AISI 6150 steel was investigated. All samples were austenitized at 870 ℃ for 45 min followed by oil quenching, and then tempered at t...Effect of tempering temperature on the microstructure and mechanical properties of AISI 6150 steel was investigated. All samples were austenitized at 870 ℃ for 45 min followed by oil quenching, and then tempered at temperatures between 200 and 600 ℃ for 60 min. The results show that the microstructure of tempered sample at 200 ℃ mainly consists of tempered martensite. With increasing the tempered temperature, the martensite transforms to the ferrite and carbides. The ultimate tensile strength, the hardness and the retained austenite decrease with increasing tempered temperature, and 0.2% yield strength increases when the temperature increases from 200 to 300 ℃ and then decreases with increasing the temperature, but the elongation and impact energy increase with increasing the tempering temperature.展开更多
基金Project(G202403)supported by the Open Foundation of The State Key Laboratory of Refractories and Metallurgy,ChinaProject(2022CFB378)supported by the Natural Science Foundation of Hubei Province,China+2 种基金Project(B 17034)supported by 111 Project,ChinaProject(IRT_17R83)supported by the Innovative Research Team Development Program of Ministry of Education of ChinaProject(P2024-026)supported by the Open Foundation of The State Key Laboratory of Materials Processing and Die&Mould Technology,China。
文摘Electroshocking treatment(EST),an efficient and rapid material treatment method,promotes microstructure evolution and improves mechanical properties.This study incorporates EST into the conventional cold rolling-quenching tempering process of M50 steel and investigates the influence and mechanism of applying EST at different stages of the process on the microstructure and mechanical properties.Scanning electron microscope(SEM),transmission electron microscope(TEM),and X-ray diffraction(XRD)were used to characterize the effect of EST on microstructure.The results show that EST can refine the grains of M50(average reduction of 10.1%in grain size),homogenize the grain size distribution,reduce the dislocation density(20.9%in average),promote the dissolution of carbides in the matrix and distribute them more uniformly along the grain boundaries,resulting in the improvement of mechanical properties.The mechanical properties of the specimen with the process flow of rolling-quenching-tempering-electroshocking showed excellent performance,with an increase in hardness of 1.4%,tensile strength of 17.7%,and elongation at break of 24.3%as compared to the specimen without EST.The tensile properties of the specimen with the process flow of rolling electroshocking-quenching-tempering showed the best performance,with an increase in tensile strength of 30.0%and elongation at break of 30.7%as compared to the specimen without EST.
基金Project(2011BAE13B03) supported by the National Key Technology R&D Program of China
文摘Effect of tempering temperature on the microstructure and mechanical properties of AISI 6150 steel was investigated. All samples were austenitized at 870 ℃ for 45 min followed by oil quenching, and then tempered at temperatures between 200 and 600 ℃ for 60 min. The results show that the microstructure of tempered sample at 200 ℃ mainly consists of tempered martensite. With increasing the tempered temperature, the martensite transforms to the ferrite and carbides. The ultimate tensile strength, the hardness and the retained austenite decrease with increasing tempered temperature, and 0.2% yield strength increases when the temperature increases from 200 to 300 ℃ and then decreases with increasing the temperature, but the elongation and impact energy increase with increasing the tempering temperature.