MoS2/γ－Al2O3 ceramic composite membrane is successfully synthesized by the sol-gel method based on the inorganic salt route. The aluminum hydrate sol derived from the inorganic salt Al(NO3)3, whose transparence and ...MoS2/γ－Al2O3 ceramic composite membrane is successfully synthesized by the sol-gel method based on the inorganic salt route. The aluminum hydrate sol derived from the inorganic salt Al(NO3)3, whose transparence and viscosity are 97% and 1.2 × 10-3 Pa. s, respectively, can be formed through adjusting the ratio of the peptizing agent H+ to Al3+ to 0.3. The aluminum hydrate gel at 110℃ is amorphous in structure and is heat-treated in air at 800℃ to form γ－Al2O3. The precursor derived from the mixture solution of ammonium molybdate, thioacetamide and a reducing agent, can be transformed into crystal MoS2 under reducing condition at 800℃. MoS2/γ－Al2O3 composite membrane is an organic whole and bps no gradation from MoS2 layer to γ－Al2O3 Iayer. The separation factor a H2/H2S through the MoS2/γ－Al2O3 composite membrane increase with rising temperature and a H2/H2S at 600℃ is 4.45 higher than the theoretical separation factor produced by the ideal Knudsen diffusion.展开更多
文摘通过水解法制备TiO_2纳米颗粒,与经过超声处理后的MoS_2片层纳米材料复合制备MoS_2/TiO_2纳米催化剂,考察不同MoS_2负载量对其光催化降解苯酚效率及路径的影响。XRD、SEM、EDS、FT-IR和UV-vis DRS等表征结果表明,复合催化剂主要由锐钛矿型TiO_2和MoS_2组成;剥离后的MoS_2呈现薄片层状结构,均匀地分散在TiO_2纳米颗粒当中。光催化降解苯酚性能测试结果显示,对于MoS_2/TiO_2催化剂,MoS_2负载量的提高有利于光催化降解苯酚效率的提高;当MoS_2负载量为27%时,复合M o S2/TiO_2纳米颗粒的光催化性能最佳,反应80 min后可将苯酚完全降解。通过对苯酚降解过程中生成中间产物跟踪发现,MoS_2负载量的提高有利于促进中间产物苯醌、对苯二酚以及邻苯二酚的生成,进而提升了MoS_2/TiO_2复合材料的光催化性能。
文摘MoS2/γ－Al2O3 ceramic composite membrane is successfully synthesized by the sol-gel method based on the inorganic salt route. The aluminum hydrate sol derived from the inorganic salt Al(NO3)3, whose transparence and viscosity are 97% and 1.2 × 10-3 Pa. s, respectively, can be formed through adjusting the ratio of the peptizing agent H+ to Al3+ to 0.3. The aluminum hydrate gel at 110℃ is amorphous in structure and is heat-treated in air at 800℃ to form γ－Al2O3. The precursor derived from the mixture solution of ammonium molybdate, thioacetamide and a reducing agent, can be transformed into crystal MoS2 under reducing condition at 800℃. MoS2/γ－Al2O3 composite membrane is an organic whole and bps no gradation from MoS2 layer to γ－Al2O3 Iayer. The separation factor a H2/H2S through the MoS2/γ－Al2O3 composite membrane increase with rising temperature and a H2/H2S at 600℃ is 4.45 higher than the theoretical separation factor produced by the ideal Knudsen diffusion.