In order to explore the dependence of plasticity of metallic material on a high magnetic held,the effects of the different magnetic induction intensities（H = 0 T,0.5 T,1 T,3 T,and 5 T） and pulses number（N = 0,10,20...In order to explore the dependence of plasticity of metallic material on a high magnetic held,the effects of the different magnetic induction intensities（H = 0 T,0.5 T,1 T,3 T,and 5 T） and pulses number（N = 0,10,20,30,40,and 50） on tensile strength（σ;） and elongation（δ） of 2024 aluminum alloy are investigated in the synchronous presences of a high magnetic held and external stress.The results show that the magnetic held exerts apparent and positive effects on the tensile properties of the alloy.Especially under the optimized condition of H;=1 T and N;=30,the σ;and 8 are 410 MPa and 17% that are enhanced by 9.3% and 30.8% respectively in comparison to those of the untreated sample.The synchronous increases of tensile properties are attributed to the magneto-plasticity effect on a quantum scale.That is,the magnetic held will accelerate the state conversion of radical pair generated between the dislocation and obstacles from singlet to the triplet state.The bonding energy between them is meanwhile lowered and the moving flexibility of dislocations will be enhanced.At H;= 1 T and N;= 30,the dislocation density is enhanced by 1.28 times.The relevant minimum grain size is 266.1 nm,which is reduced by 35.2%.The grain rehning is attributed to the dislocation accumulation and subsequent dynamic recrystallization.The（211） and（220） peak intensities are weakened.It is deduced that together with the recrystallization,the hne grains will transfer towards the slip plane and contribute to the slipping deformation.展开更多
Hot forming with synchronous cooling(HFSC)is a novel technique for heat-treatable,high-strength aluminum alloys,which allows the alloys to acquire good formability,negligible springback,rapid processing and better mec...Hot forming with synchronous cooling(HFSC)is a novel technique for heat-treatable,high-strength aluminum alloys,which allows the alloys to acquire good formability,negligible springback,rapid processing and better mechanical properties.However,the deformation behavior and microstructure evolution of the alloys during HFSC are complex and need to be studied due to the temperature and strain rate effects.Uniaxial tensile tests in a temperature range of 250—450℃and a strain rate range of 0.01—1 s-1 for AA2024-H18 aluminum alloy sheet are conducted with a Gleeble-3500 Thermal-Mechanical Simulation Tester.And based on metallography observation and analysis,AA2024-H18 aluminum alloy sheet in HSFC process exhibits hardening and dynamic recovery behaviors within the temperature range of 250—450 ℃.Strain rate shows different effects on ductility at different temperatures.Compared with traditional warm/hot forming methods,AA2024-H18 aluminum alloy achieves a better work-hardening result through HFSC operations,which promises an improved formability at elevated temperature and thus good mechanical properties of final part.After HSFC operations,the microstructure of the specimens is composed of elongated static recrystallization grain.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.51371091,51174099,and 51001054)the Industrial Center of Jiangsu University,China(Grant No.ZXJG201586)
文摘In order to explore the dependence of plasticity of metallic material on a high magnetic held,the effects of the different magnetic induction intensities（H = 0 T,0.5 T,1 T,3 T,and 5 T） and pulses number（N = 0,10,20,30,40,and 50） on tensile strength（σ;） and elongation（δ） of 2024 aluminum alloy are investigated in the synchronous presences of a high magnetic held and external stress.The results show that the magnetic held exerts apparent and positive effects on the tensile properties of the alloy.Especially under the optimized condition of H;=1 T and N;=30,the σ;and 8 are 410 MPa and 17% that are enhanced by 9.3% and 30.8% respectively in comparison to those of the untreated sample.The synchronous increases of tensile properties are attributed to the magneto-plasticity effect on a quantum scale.That is,the magnetic held will accelerate the state conversion of radical pair generated between the dislocation and obstacles from singlet to the triplet state.The bonding energy between them is meanwhile lowered and the moving flexibility of dislocations will be enhanced.At H;= 1 T and N;= 30,the dislocation density is enhanced by 1.28 times.The relevant minimum grain size is 266.1 nm,which is reduced by 35.2%.The grain rehning is attributed to the dislocation accumulation and subsequent dynamic recrystallization.The（211） and（220） peak intensities are weakened.It is deduced that together with the recrystallization,the hne grains will transfer towards the slip plane and contribute to the slipping deformation.
基金supported by the National Natural Science Foundation of China(No.51175252)
文摘Hot forming with synchronous cooling(HFSC)is a novel technique for heat-treatable,high-strength aluminum alloys,which allows the alloys to acquire good formability,negligible springback,rapid processing and better mechanical properties.However,the deformation behavior and microstructure evolution of the alloys during HFSC are complex and need to be studied due to the temperature and strain rate effects.Uniaxial tensile tests in a temperature range of 250—450℃and a strain rate range of 0.01—1 s-1 for AA2024-H18 aluminum alloy sheet are conducted with a Gleeble-3500 Thermal-Mechanical Simulation Tester.And based on metallography observation and analysis,AA2024-H18 aluminum alloy sheet in HSFC process exhibits hardening and dynamic recovery behaviors within the temperature range of 250—450 ℃.Strain rate shows different effects on ductility at different temperatures.Compared with traditional warm/hot forming methods,AA2024-H18 aluminum alloy achieves a better work-hardening result through HFSC operations,which promises an improved formability at elevated temperature and thus good mechanical properties of final part.After HSFC operations,the microstructure of the specimens is composed of elongated static recrystallization grain.