The (Y,Gd)BO 3∶Eu phosphor was synthesized by solid state reaction. The UV spectra showed that in a certain range of Gd 3+ concentration, more Gd 3+ absorbed energy and transferred it to Eu 3+ with its increasing con...The (Y,Gd)BO 3∶Eu phosphor was synthesized by solid state reaction. The UV spectra showed that in a certain range of Gd 3+ concentration, more Gd 3+ absorbed energy and transferred it to Eu 3+ with its increasing concentration. From the spectra in VUV region, it was observed that both the doping and the concentrations of Gd 3+ , Eu 3+ greatly affected the absorption of the host lattice. The absorbances at 147 nm and 170 nm increased when the Gd 3+ was doped which can be explained as that Gd 3+ transferred energy to BO 4. The optical properties of (Y,Gd)BO 3∶Eu were the best when the concentration of Eu 3+ was about 0.04.展开更多
Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re...Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.展开更多
文摘The (Y,Gd)BO 3∶Eu phosphor was synthesized by solid state reaction. The UV spectra showed that in a certain range of Gd 3+ concentration, more Gd 3+ absorbed energy and transferred it to Eu 3+ with its increasing concentration. From the spectra in VUV region, it was observed that both the doping and the concentrations of Gd 3+ , Eu 3+ greatly affected the absorption of the host lattice. The absorbances at 147 nm and 170 nm increased when the Gd 3+ was doped which can be explained as that Gd 3+ transferred energy to BO 4. The optical properties of (Y,Gd)BO 3∶Eu were the best when the concentration of Eu 3+ was about 0.04.
文摘Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.
