We prepared TiO 2(anatase) and Sn doped TiO 2 nanoparticlate film by Plasma enhanced Chemical Vapor Deposition(PECVD) method. XRD and XPS experiments showed that Sn was doped into the lattice of TiO 2 with a ratio of ...We prepared TiO 2(anatase) and Sn doped TiO 2 nanoparticlate film by Plasma enhanced Chemical Vapor Deposition(PECVD) method. XRD and XPS experiments showed that Sn was doped into the lattice of TiO 2 with a ratio of n (Sn)∶ n (Ti)=1∶10 . Sn doping largely enhanced the photocatalytic activity of TiO 2 film for phenol degradation. The enhancement in photoactivity by doping was discussed, based on the characterization with AFM, FTIR and EFISPS. Sn doping produced localized level of Sn 4+ in the band gap of TiO 2, about 0.4 eV below the conduction band, which could capture photogenerated electrons and reduce O 2 adsorbed on the surface of TiO 2 film, thus accelerated the photocatalytic reaction.展开更多
The transition metal ion doped TiO 2 nanoparticles were prepared with hydrothermal method, and the effects of doping different metal ions on the ability of TiO 2 in photocatalyzing degradation of rhodamine B(RB) were ...The transition metal ion doped TiO 2 nanoparticles were prepared with hydrothermal method, and the effects of doping different metal ions on the ability of TiO 2 in photocatalyzing degradation of rhodamine B(RB) were studied. The results showed that the doping of Fe 3+ , Co 2+ , Ni 2+ and Cr 3+ in TiO 2 nanoparticles made the photocatalytic efficiency of the TiO 2 particles reduce and the higher the initial content of Fe 3+ , the lower the ability of TiO 2 in photocatalyzing the degradation of RB. But the doping of Zn 2+ and Cd 2+ , especially Zn 2+ , made the photocatalytic efficiency of the TiO 2 particles enhance, showing a great increase of the rate constant( k ) and the initial reaction rate( r ini ).展开更多
Nanocrystalline TiO 2 has been studied extensively in recent years as photocatalysts to deal with environmental pollutions, such as water purification, wastewater treatment and air purification. Here a novel sonochemi...Nanocrystalline TiO 2 has been studied extensively in recent years as photocatalysts to deal with environmental pollutions, such as water purification, wastewater treatment and air purification. Here a novel sonochemical method for directly preparing anatase nanocrystalline TiO 2 has been established. Nanocrystalline TiO 2 were synthesized by the hydrolysis of titanium tetrabutyl in the presence of water and ethanol under a high intensity ultrasonic irradiation(20 kHz, 100 W/cm 2) at 363 K for 3 h. The structure and particle sizes of the product were dependent upon the reaction temperature, the acidity of the medium and the reaction time. Characterization was accomplished by using various different techniques, such as powder X ray diffraction(XRD), transmission electron microscopy(TEM), thermogravimetry differential thermal analysis(TG DTA) and Fourier transform infrared(FTIR) spectroscopy. The TEM images showed that the particles of TiO 2 were columnar in shape and the average sizes were ca. 3 nm×7 nm . The formation mechanism of nanocrystalline TiO 2 under a high intensity ultrasonic irradiation was also investigated. The hydrolytic species of titanium tetrabutyl in water condensed to form a large number of tiny gel nuclei which aggregated to form larger clusters. Ultrasound irradiation generated a lot of local hot spots within the gel and the crystal structural unit was formed near the hot spots with the decrease of the gel nuclei, which lead to form nanocrystal particles.展开更多
纳米 Ti O2 具有独特的光催化性、优异的颜色效应以及紫外线屏蔽等功能 ,在光催化剂、化妆品、抗紫外线吸收剂、功能陶瓷、气敏传感器件等方面具有广阔的应用前景 ,国内外文献对纳米 Ti O2 的性质、应用及其制备方法进行了大量的研究报...纳米 Ti O2 具有独特的光催化性、优异的颜色效应以及紫外线屏蔽等功能 ,在光催化剂、化妆品、抗紫外线吸收剂、功能陶瓷、气敏传感器件等方面具有广阔的应用前景 ,国内外文献对纳米 Ti O2 的性质、应用及其制备方法进行了大量的研究报道。本工作对有关纳米 Ti O2的性能。展开更多
A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acid...A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.展开更多
The dynamic wetting of water spreading on TiO 2 and TiO 2 SiO 2 films prepared by sol gel method and subsequently treated by air plasma and UV irradiation was investigated. Water completely spread on TiO 2 surface wit...The dynamic wetting of water spreading on TiO 2 and TiO 2 SiO 2 films prepared by sol gel method and subsequently treated by air plasma and UV irradiation was investigated. Water completely spread on TiO 2 surface within 3 s and its dynamic contact angles can be expressed by a power law θ d= k(t+a) -n with the n value 0.98. Less than 50%(molar fraction) SiO 2 addition can accelerate the dynamic water spreading rate on the TiO 2 SiO 2 films and the optimum molar fraction of SiO 2 amount corresponding to as annealed, air plasma, and UV irradiation treatment process is 15%, 10% and 20%, respectively.展开更多
文摘We prepared TiO 2(anatase) and Sn doped TiO 2 nanoparticlate film by Plasma enhanced Chemical Vapor Deposition(PECVD) method. XRD and XPS experiments showed that Sn was doped into the lattice of TiO 2 with a ratio of n (Sn)∶ n (Ti)=1∶10 . Sn doping largely enhanced the photocatalytic activity of TiO 2 film for phenol degradation. The enhancement in photoactivity by doping was discussed, based on the characterization with AFM, FTIR and EFISPS. Sn doping produced localized level of Sn 4+ in the band gap of TiO 2, about 0.4 eV below the conduction band, which could capture photogenerated electrons and reduce O 2 adsorbed on the surface of TiO 2 film, thus accelerated the photocatalytic reaction.
文摘The transition metal ion doped TiO 2 nanoparticles were prepared with hydrothermal method, and the effects of doping different metal ions on the ability of TiO 2 in photocatalyzing degradation of rhodamine B(RB) were studied. The results showed that the doping of Fe 3+ , Co 2+ , Ni 2+ and Cr 3+ in TiO 2 nanoparticles made the photocatalytic efficiency of the TiO 2 particles reduce and the higher the initial content of Fe 3+ , the lower the ability of TiO 2 in photocatalyzing the degradation of RB. But the doping of Zn 2+ and Cd 2+ , especially Zn 2+ , made the photocatalytic efficiency of the TiO 2 particles enhance, showing a great increase of the rate constant( k ) and the initial reaction rate( r ini ).
文摘Nanocrystalline TiO 2 has been studied extensively in recent years as photocatalysts to deal with environmental pollutions, such as water purification, wastewater treatment and air purification. Here a novel sonochemical method for directly preparing anatase nanocrystalline TiO 2 has been established. Nanocrystalline TiO 2 were synthesized by the hydrolysis of titanium tetrabutyl in the presence of water and ethanol under a high intensity ultrasonic irradiation(20 kHz, 100 W/cm 2) at 363 K for 3 h. The structure and particle sizes of the product were dependent upon the reaction temperature, the acidity of the medium and the reaction time. Characterization was accomplished by using various different techniques, such as powder X ray diffraction(XRD), transmission electron microscopy(TEM), thermogravimetry differential thermal analysis(TG DTA) and Fourier transform infrared(FTIR) spectroscopy. The TEM images showed that the particles of TiO 2 were columnar in shape and the average sizes were ca. 3 nm×7 nm . The formation mechanism of nanocrystalline TiO 2 under a high intensity ultrasonic irradiation was also investigated. The hydrolytic species of titanium tetrabutyl in water condensed to form a large number of tiny gel nuclei which aggregated to form larger clusters. Ultrasound irradiation generated a lot of local hot spots within the gel and the crystal structural unit was formed near the hot spots with the decrease of the gel nuclei, which lead to form nanocrystal particles.
文摘A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.
文摘The dynamic wetting of water spreading on TiO 2 and TiO 2 SiO 2 films prepared by sol gel method and subsequently treated by air plasma and UV irradiation was investigated. Water completely spread on TiO 2 surface within 3 s and its dynamic contact angles can be expressed by a power law θ d= k(t+a) -n with the n value 0.98. Less than 50%(molar fraction) SiO 2 addition can accelerate the dynamic water spreading rate on the TiO 2 SiO 2 films and the optimum molar fraction of SiO 2 amount corresponding to as annealed, air plasma, and UV irradiation treatment process is 15%, 10% and 20%, respectively.